Electromagnetic valve surface environment-friendly treatment process

An environmental protection treatment, solenoid valve technology, applied in the direction of surface reaction electrolytic coating, electrolytic coating, anodizing, etc., can solve the problems of complex treatment process operation, unable to effectively protect the surface, easy to oxidize on the surface, etc. High efficiency, super anti-oxidation performance, easy to spray effect

Inactive Publication Date: 2021-02-09
南通东昌锻压机床有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The surface of aluminum products is prone to oxidation after long-term use. Therefore, the surface needs to be treated. The existing treatment process is complicated to operate and cannot effectively protect it. Therefore, it is necessary to improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The present invention provides the following technical solutions: an environmentally friendly treatment process for the surface of a solenoid valve, comprising the following steps:

[0019] A. First, sandblast the surface of aluminum products to remove surface oxides;

[0020] B. Wash the sandblasted aluminum products once, and dry them naturally at room temperature;

[0021] C. Put the dried aluminum products into the electrolyte for anode electrolysis to form a protective film;

[0022] D. Wash the aluminum products after anodic electrolysis for a second time, and put them into a low-temperature drying oven to dry;

[0023] E. Finally, spray a layer of antioxidant on the surface of the aluminum product after drying, which completes the treatment of the surface of the aluminum product.

[0024] In this embodiment, brown corundum abrasives are used for sandblasting in step A.

[0025] In this embodiment, the anode electrolysis in step C is specifically as follows: in...

Embodiment 2

[0029] An environmentally friendly treatment process for the surface of a solenoid valve, comprising the following steps:

[0030] A. First, sandblast the surface of aluminum products to remove surface oxides;

[0031] B. Wash the sandblasted aluminum products once, and dry them naturally at room temperature;

[0032] C. Put the dried aluminum products into the electrolyte for anode electrolysis to form a protective film;

[0033] D. Wash the aluminum products after anodic electrolysis for a second time, and put them into a low-temperature drying oven to dry;

[0034] E. Finally, spray a layer of antioxidant on the surface of the aluminum product after drying, which completes the treatment of the surface of the aluminum product.

[0035] In this embodiment, brown corundum abrasives are used for sandblasting in step A.

[0036] In this embodiment, the anode electrolysis in step C is specifically as follows: in a sulfuric acid electrolytic solution with a concentration of 18%...

Embodiment 3

[0040] An environmentally friendly treatment process for the surface of a solenoid valve, comprising the following steps:

[0041] A. First, sandblast the surface of aluminum products to remove surface oxides;

[0042] B. Wash the sandblasted aluminum products once, and dry them naturally at room temperature;

[0043] C. Put the dried aluminum products into the electrolyte for anode electrolysis to form a protective film;

[0044] D. Wash the aluminum products after anodic electrolysis for a second time, and put them into a low-temperature drying oven to dry;

[0045] E. Finally, spray a layer of antioxidant on the surface of the aluminum product after drying, which completes the treatment of the surface of the aluminum product.

[0046] In this embodiment, brown corundum abrasives are used for sandblasting in step A.

[0047] In this embodiment, the anode electrolysis in step C is specifically as follows: in a sulfuric acid electrolytic solution with a concentration of 15%...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an electromagnetic valve surface environment-friendly treatment process. The process comprises the following steps: A, firstly, carrying out sand blasting treatment on the surface of an aluminum product to remove surface oxides; B, carrying out primary washing on the aluminum product subjected to sand blasting, and naturally drying at normal temperature; C, putting the dried aluminum product into an electrolyte for anodic electrolysis, and generating a protective film; D, carrying out secondary water washing on the aluminum product subjected to anode electrolysis, and putting the aluminum product into a low-temperature drying oven for drying; and E, finally, spraying a layer of antioxidant on the surface of the dried aluminum product to finish the treatment of the surface of the aluminum product. The electromagnetic valve surface environment-friendly treatment process adopted by the invention is environment-friendly, non-toxic and high in treatment efficiency, the aluminum product can be effectively treated, and the oxidation phenomenon of the aluminum product after long-time use is prevented.

Description

technical field [0001] The invention relates to the technical field of surface treatment of aluminum products, in particular to an environmentally friendly treatment process for the surface of an electromagnetic valve. Background technique [0002] Aluminum products are a general term for daily necessities and industrial products processed from aluminum alloy as the main raw material. Aluminum alloy is a general term for alloys based on aluminum. The main alloying elements are copper, silicon, magnesium, zinc, manganese, and the secondary alloying elements are nickel, iron, titanium, chromium, lithium, etc.; the aluminum alloy has low density, but relatively high strength, which is close to or exceeds high-quality steel, and has good plasticity and can be processed Formed into various profiles, it has excellent electrical conductivity, thermal conductivity and corrosion resistance. It is widely used in industry, and its usage is second only to steel. [0003] The surface o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D11/08C25D11/16C25D11/18C09D191/00C09D7/61C09D7/63
CPCC25D11/08C25D11/16C25D11/18C09D191/00C09D7/61C09D7/63C09D5/18C08K2201/011C08K13/02C08K3/18C08K5/13C08K5/1345
Inventor 章宜友章志超
Owner 南通东昌锻压机床有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com