Bismuth-manganese-based composite particle and preparation method and application thereof

A composite particle and composite nanoparticle technology, applied in the field of bismuth-manganese-based composite particles and their preparation, can solve the problems of poor treatment effect of cancer cells, less tumor site enrichment, lack of targeting ability, etc., and achieve chemodynamic therapy. , The effect of promoting photodynamic therapy and increasing specific surface area

Active Publication Date: 2021-02-09
SOUTH CHINA UNIV OF TECH
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CuS@mSiO with core-shell structure 2 / ICG has a single function and can only provide photothermal therapy, and its structure is simple, the porosity is low, and the loading rate of organic molecule ICG is only about 8%. In addition, this material also lacks targeting ability and is enriched in tumor sites Less, affect the final treatment effect
MnO with hollow mesoporous structure 2 / Ce6 can improve the hypoxic environment and provide two treatment methods of photothermal and photodynamic, and the hollow mesoporous structure is relatively novel, and the porosity is relatively higher than that of CuS@mSiO with core-shell structure. 2 / ICG has been improved, but the loading rate of organic molecule Ce6 (chlorine e6) is only about 17%, and this material can only be passively targeted by adding a magnetic field from the outside, and the targeting efficiency is low. , Malignant cancer cells are less effective in treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bismuth-manganese-based composite particle and preparation method and application thereof
  • Bismuth-manganese-based composite particle and preparation method and application thereof
  • Bismuth-manganese-based composite particle and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] A kind of bismuth-manganese base composite particle, its preparation method comprises the following steps (synthesis schematic diagram is as follows figure 1 shown):

[0060] 1) Under the protection of argon, 0.9701g of Bi(NO 3 ) 3 ·5H 2 O was added to 10 mL of dodecanethiol, stirred for 10 min, then placed in an oil bath to heat up until the reaction solution turned black, kept for 1 min, washed the reaction solution with cyclohexane and ethanol, and then centrifuged at 10000 rpm for 10 min, and the precipitate was obtained. Bismuth nanoparticles (referred to as Bi NPs);

[0061] 2) Add 50 mg of bismuth nanoparticles into 50 mL of cyclohexane solution and disperse ultrasonically to obtain a dispersion of bismuth nanoparticles, then add 10 mL of emulsifier legal-CO-520 (alkylphenol ethoxylate) into 50 mL of cyclohexane In the hexane solution, mix evenly to obtain an emulsifier solution, then add the bismuth nanoparticle dispersion into the emulsifier solution, mix e...

Embodiment 2

[0098] A kind of bismuth-manganese base composite particle, its preparation method comprises the following steps (synthesis schematic diagram is as follows figure 1 shown):

[0099] 1) Under the protection of argon, 0.9701g of Bi(NO 3 ) 3 ·5H 2 O was added to 10 mL of dodecanethiol, stirred for 10 min, then placed in an oil bath to heat up until the reaction solution turned black, kept for 1 min, washed the reaction solution with cyclohexane and ethanol, and then centrifuged at 10000 rpm for 10 min, and the precipitate was obtained. Bismuth nanoparticles (referred to as Bi NPs);

[0100] 2) Add 50 mg of bismuth nanoparticles into 50 mL of cyclohexane solution and disperse ultrasonically to obtain a dispersion of bismuth nanoparticles, then add 10 mL of emulsifier legal-CO-520 (alkylphenol ethoxylate) into 50 mL of cyclohexane In the hexane solution, mix evenly to obtain an emulsifier solution, then add the bismuth nanoparticle dispersion into the emulsifier solution, mix e...

Embodiment 3

[0106] A kind of bismuth-manganese base composite particle, its preparation method comprises the following steps (synthesis schematic diagram is as follows figure 1 shown):

[0107] 1) Under the protection of argon, 0.315g of BiCl 3 Add 10mL of dodecanethiol, stir for 10min, then place in an oil bath to heat up until the reaction solution turns black, keep it warm for 1min, wash the reaction solution with cyclohexane and ethanol, then centrifuge at 10000rpm for 10min, take the precipitate, and obtain bismuth Nanoparticles (referred to as Bi NPs);

[0108] 2) Add 50 mg of bismuth nanoparticles into 50 mL of cyclohexane solution and disperse ultrasonically to obtain a dispersion of bismuth nanoparticles, then add 10 mL of emulsifier legal-CO-520 (alkylphenol ethoxylate) into 50 mL of cyclohexane In the hexane solution, mix evenly to obtain an emulsifier solution, then add the bismuth nanoparticle dispersion into the emulsifier solution, mix evenly, and then add 5 mL of KMnO wi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a bismuth-manganese-based composite particle and a preparation method and application thereof. The bismuth-manganese-based composite particle comprises an inner core and a triple negative breast cancer (TNBC) cell membrane wrapping the inner core; the inner core is formed by aggregating a plurality of amino-modified bismuth-bismuth trioxide-manganese oxide composite nanoparticles with hollow structures; and indocyanine green is loaded inside and on the surfaces of the amino-modified bismuth-bismuth trioxide-manganese oxide composite nanoparticle with the hollow structures. The bismuth-manganese-based composite particle has an active targeting capability, can improve a tumor microenvironment and provide multiple treatment modes, is high in drug loading rate, novel instructure and simple in preparation method, and can be used for treating relatively large and malignant TNBC.

Description

technical field [0001] The invention relates to the technical field of organic-inorganic composite biomaterials, in particular to a bismuth-manganese-based composite particle and a preparation method and application thereof. Background technique [0002] Breast cancer is a malignant tumor that occurs in the epithelial tissue of the mammary gland. At least 1 out of every 10 cancer patients in the world is a breast cancer patient, and 99% of breast cancer patients are women, which seriously threatens women's health. About 15%-20% of breast cancer patients suffer from triple negative breast cancer (TNBC) with a high mortality rate. TNBC refers to a special type of breast cancer that is clinically negative for estrogen receptor (ER), progesterone receptor (PR) and human epidermal growth factor receptor-2 (HER-2). TNBC has no specific receptors and antibodies, and has high invasiveness, recurrence rate and metastasis rate, and the curative effect of conventional treatment method...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K41/00A61K33/245A61K33/32A61K9/51A61K47/46A61P35/00
CPCA61K9/5176A61K33/245A61K33/32A61K41/0052A61K41/0057A61P35/00A61K2300/00
Inventor 李丽华徐兴毅
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com