Non-polar modified TPU for shoe material and preparation method thereof

A non-polar and modified technology, applied in the field of thermoplastic polyurethane, can solve problems such as increased odor, influence of soft segment content, and poor yellowing resistance, so as to reduce product processing temperature, improve hydrolysis stability, and improve The effect of mobility

Active Publication Date: 2022-04-19
SHANDONG INOV POLYURETHANE
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the disadvantages are that these methods will make the mechanical strength of the TPU material worse, the odor will become larger, and the yellowing resistance will be worse.
"Preparation and Performance Research of Thermoplastic Polyurethane with Dimer Alcohol as Soft Segment" mentioned starting from the structure of the soft segment, introducing bio-based diol-dimer alcohol with non-polar side chains as the soft segment, and using MDI and BDO synthesized a new type of thermoplastic polyurethane PDU for the hard segment. The soft segment of the PDU is all composed of dimer alcohol. The content of the soft segment is 40%, which means that the performance of the PDU has reached a better state. Improve or reduce the content of the soft segment. will be affected, which greatly limits the adjustable range of product hardness, which in turn affects the application range of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-polar modified TPU for shoe material and preparation method thereof
  • Non-polar modified TPU for shoe material and preparation method thereof
  • Non-polar modified TPU for shoe material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The non-polar modified TPU used for shoe materials is made of the following raw materials in parts by mass:

[0030]

[0031] The preparation method comprises the following steps:

[0032] (1) Mix dimer alcohol, polyethylene adipate polyol and 1,4-butanediol, then add antioxidant 1010, and fully stir at 90°C to obtain a premix;

[0033] (2) Add 4,4'-diphenylmethane diisocyanate and stannous octoate catalyst to storage tank A, add the premix to storage tank B, stir at 500r / min, and vacuum at 110°C Dehydration, injection into the twin-screw extruder;

[0034] (3) React in a twin-screw extruder at 120°C and granulate to obtain TPU particles; the temperature of the feeding section of the twin-screw extruder is 110°C, the temperature of the mixing section is 130°C, and the temperature of the extrusion section is 170°C , the head temperature is 150°C.

Embodiment 2

[0036] The non-polar modified TPU used for shoe materials is made of the following raw materials in parts by mass:

[0037]

[0038]

[0039] The preparation method comprises the following steps:

[0040] (1) Mix dimer alcohol, polybutylene adipate polyol and 1,4-butanediol, then add antioxidant 1024, stir well at 100°C to obtain a premix;

[0041] (2) Add hexamethylene diisocyanate and stannous octoate catalyst into storage tank A, add the pre-mixture into storage tank B, stir at 400r / min, dehydrate in vacuum at 110°C, and pump into double In the screw extruder;

[0042] (3) At 130°C, react in a twin-screw extruder and granulate to obtain TPU particles; the temperature of the feeding section of the twin-screw extruder is 120°C, the temperature of the mixing section is 150°C, and the temperature of the extrusion section is 180°C °C, the head temperature is 160 °C.

Embodiment 3

[0044] The non-polar modified TPU used for shoe materials is made of the following raw materials in parts by mass:

[0045]

[0046] The preparation method comprises the following steps:

[0047] (1) Mix dimer alcohol, polybutylene adipate polyol and 1,6-hexanediol mixed chain extender, then add antioxidant 264, and fully stir at 100°C to obtain a premix;

[0048] (2) Add 4,4'-diphenylmethane diisocyanate and stannous octoate catalyst into storage tank A, add the premix into storage tank B, stir at 600r / min, and vacuum dehydrate at 110°C , injected into the twin-screw extruder;

[0049] (3) React in a twin-screw extruder at 160°C, and granulate to obtain TPU particles; the temperature of the feeding section of the twin-screw extruder is 120°C, the temperature of the mixing section is 150°C, and the temperature of the extrusion section is 180°C. The head temperature is 160°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of thermoplastic polyurethane, and in particular relates to a non-polar modified TPU used for shoe materials and a preparation method thereof. The TPU includes the following raw materials in parts by weight: 20-40 parts of diisocyanate, 20-30 parts of diols with non-polar side chains, 30-50 parts of polyester polyols, 5-10 parts of chain extenders, 0.1-0.5 part of antioxidant, 0.5-1 part of catalyst; the present invention introduces dimer alcohol with non-polar side chain, and uses dimer alcohol and polyester polyol as soft segment to extend chain with diisocyanate and small molecule The TPU prepared by using dimer alcohol, polyester polyol and chain extender to pre-mix rapid prototyping process, has excellent wear resistance, good mechanical strength, oil resistance and anti-corrosion of polyurethane elastomer. It has the advantages of excellent oxygen resistance, excellent hydrolytic stability, low temperature performance, processing fluidity and elasticity, and can avoid problems such as precipitation and odor caused by adding plasticizers.

Description

technical field [0001] The invention belongs to the technical field of thermoplastic polyurethane, and in particular relates to a non-polar modified TPU used for shoe materials and a preparation method thereof. Background technique [0002] Running and outdoor sports have become more and more popular fitness methods nowadays, and hydrolysis resistance, low temperature performance and elasticity are important indicators to measure shoe materials. Thermoplastic polyurethane elastomer (TPU) is a kind of polymer synthetic material with excellent performance. It not only has the elasticity of rubber but also the hardness of plastic, and also has good mechanical properties and resilience properties. It is widely used in shoe materials. However, TPU molecules contain more strong polar groups (such as ester groups, ether groups, carbamate groups, urea groups, biuret groups and allophanate groups, etc.), which endow TPU with polarity. Excellent performance and at the same time, non-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/66C08G18/32C08G18/42C08G18/44
CPCC08G18/6674C08G18/3212C08G18/3206C08G18/4238C08G18/44
Inventor 徐艳艳陈淑海宋小娜高振胜管永王真
Owner SHANDONG INOV POLYURETHANE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com