Glass fiber grid adhesive tape and preparation method thereof

A technology of glass fiber and grid, which is applied in the field of glass fiber grid tape and its preparation, which can solve the problems of insufficient adhesive performance and easy falling off, and achieve the effect of strong viscosity, high bidirectional tensile strength and firm bonding

Inactive Publication Date: 2020-10-16
福建友谊胶粘带集团有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Fiberglass mesh tape is suitable for bonding with EPDM rubber, foam, sponge, non-woven fabric, leather, profiles, decorative strips, etc., and is widely used in foamed rubber door and window anti-collision strips, and automobile sealing strips , On the anti-collision strip of the window, it plays the role of leak-proof sealing, shock absorption and buffering, but in the prior art, the glass fiber mesh tape has the problem of insufficient adhesive performance and easy to fall off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass fiber grid adhesive tape and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] Further, the preparation method of above-mentioned fiberglass mesh adhesive tape, comprises the following steps:

[0023] Step 1: Put 0.5-1.0 parts of acrylic acid, 0.3-0.5 parts of hydroxyethyl acrylate, 29-32 parts of isooctyl acrylate, 9-11 parts of butyl acrylate and 7-10 parts of vinyl acetate into the emulsification tank, turn on the stirring and mixing for 10 Minutes to obtain mixed products;

[0024] Step 2: Put half of the total amount of the mixed product into the reaction furnace, put 40-44 parts of ethyl acetate in the reaction furnace, turn on the stirring, feed nitrogen, the speed of the reaction furnace is 25 revolutions per minute, and the temperature is raised to 74-76°C;

[0025] Step 3: Mix 0.2-0.3 parts of lauroyl peroxide and 7-9 parts of ethyl acetate, and titrate in the reaction furnace. Boiling phenomenon will appear after titration for about 20 minutes, and the temperature will rise to 85-86 ° C. Stop titration, and the temperature Drop to 63-...

Embodiment 1

[0041] Step 1: Put 0.7 parts of acrylic acid, 0.4 parts of hydroxyethyl acrylate, 30 parts of isooctyl acrylate, 10 parts of butyl acrylate and 8 parts of vinyl acetate into the emulsification tank, turn on the stirring and mixing for 10 minutes to obtain a mixed product;

[0042] Step 2: Put half of the total amount of the mixed product into the reaction furnace, put 42 parts of ethyl acetate in the reaction furnace, turn on the stirring, feed nitrogen, the speed of the reaction furnace is 25 revolutions per minute, and the temperature is raised to 75°C ;

[0043] Step 3: Mix 0.25 parts of lauroyl peroxide and 8 parts of ethyl acetate, and titrate in the reaction furnace, the temperature rises to 85°C, stop the titration, the temperature drops to 65°C, continue the titration, open the emulsification tank at the same time, in the reaction Put the other half of the mixed product in the furnace, continue to titrate to 150 minutes, cool down and unload the glue after 4 hours of h...

Embodiment 2

[0051] Step 1: Put 0.5 parts of acrylic acid, 0.3 parts of hydroxyethyl acrylate, 29 parts of isooctyl acrylate, 9 parts of butyl acrylate and 7 parts of vinyl acetate into the emulsification tank, turn on the stirring and mixing for 10 minutes to obtain a mixed product;

[0052] Step 2: Put half of the total amount of the mixed product into the reaction furnace, put 40-44 parts of ethyl acetate in the reaction furnace, turn on the stirring, feed nitrogen, the speed of the reaction furnace is 25 revolutions per minute, and the temperature is raised to 74°C;

[0053] Step 3: Mix 0.2 parts of lauroyl peroxide and 7 parts of ethyl acetate, and titrate in the reaction furnace. Boiling will appear after about 20 minutes of titration, and the temperature will rise to 85°C. Stop titration, and the temperature will drop to 63°C. Continue Titrate, open the emulsification tank at the same time, put the other half of the mixed product in the reaction furnace, continue to titrate to 150 m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of adhesive tapes, and especially relates to a glass fiber grid adhesive tape and a preparation method thereof. The glass fiber grid adhesive tape comprises a glass fiber grid cloth layer and a glue layer coated on the surface of the glass fiber grid cloth layer, wherein the glue layer is prepared by mixing the following components in parts by weight; 0.5 to 1.0 part of acrylic acid, 0.3 to 0.5 part of hydroxyethyl acrylate, 29 to 32 parts of iso-octyl acrylate, 9 to 11 parts of butyl acrylate, 7 to 10 parts of vinyl acetate, 47 to 53 parts of ethylacetate, 0.2 to 0.3 part of lauroyl peroxide and 7 to 9 parts of ethyl acetate. The glass fiber grid cloth keeps dimensional stability in a very wide temperature range, and can provide longitudinal and transverse stable dimensions without deformation. The adhesive tape has the advantages of high viscosity, high biaxial tensile strength, softness, fitness, wear resistance, water resistance and moisture resistance, and can also be used for firmly adhering rough or irregular surfaces.

Description

technical field [0001] The invention relates to the technical field of adhesive tapes, in particular to a glass fiber mesh adhesive tape and a preparation method thereof. Background technique [0002] Fiberglass mesh tape is suitable for bonding with EPDM rubber, foam, sponge, non-woven fabric, leather, profiles, decorative strips, etc., and is widely used in foamed rubber door and window anti-collision strips, and automobile sealing strips , On the anti-collision strip of the window, it plays the role of leak-proof sealing, shock absorption and buffering, but in the prior art, the glass fiber mesh tape has the problem of insufficient adhesion and easy falling off. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a glass fiber grid tape with good adhesive performance and a preparation method thereof. [0004] In order to solve the problems of the technologies described above, the technical solution adopted in the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/30C09J7/21C09J133/08C09J11/08
CPCC08L2205/035C09J11/08C09J133/066C09J2400/143C09J7/21C09J7/30C08L45/00C08L57/02C08L75/04
Inventor 张梓恒林克波林克兴林子茂
Owner 福建友谊胶粘带集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap