Manufacturing method of aluminium butt welding type composite pipe

A manufacturing method and technology for composite pipes, which are applied to manufacturing tools, welding equipment, tubular articles, etc., can solve problems such as complex production processes, and achieve the effects of high pipe quality, fast welding speed, and uniform pipe wall thickness.

Inactive Publication Date: 2020-03-06
樊伟
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a method for manufacturing an aluminum butt-welded composite pipe, which solves the problem of complex production processes in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] First, the aluminum strip is perforated according to a certain arrangement rule; the aluminum strip is turned into an aluminum half pipe through a preforming mechanism; the aluminum half pipe is heated by a heater to about 220°C, and then enters the inner pipe head to sizing and seams to form an aluminum pipe. After the tube is molded, it is welded into a tube; the polymer plastic material, acrylic acid and filler are fully mixed, heated to 165°C, and extruded through an extruder; the extruded plastic polymer is extruded into the inner tube head At the same time, blow out compressed air to expand the inner plastic tube; extrude the extruded plastic high molecular polymer out of the outer plastic tube with the outer tube head, coat the outer plastic and outer plastic on the outer wall of the aluminum tube, and Propylene hot melt adhesive is evenly coated on the inner and outer walls of the perforated aluminum tube; the temperature in the mold cavity is heated to about 220...

Embodiment 2

[0035] First, the aluminum strip is perforated according to a certain arrangement rule; the aluminum strip is turned into an aluminum half pipe through a preforming mechanism; the aluminum half pipe is heated by a heater to about 220°C, and then enters the inner pipe head to sizing and seams to form an aluminum pipe. After the tube is molded, it is welded into a tube; the polymer plastic material, acrylic acid and filler are fully mixed, heated to 165°C, and extruded through an extruder; the extruded plastic polymer is extruded into the inner tube head At the same time, blow out compressed air to expand the inner plastic tube; extrude the extruded plastic high molecular polymer out of the outer plastic tube with the outer tube head, coat the outer plastic and outer plastic on the outer wall of the aluminum tube, and Propylene hot-melt adhesive is evenly coated on the inner and outer walls of the perforated aluminum tube; the temperature in the mold cavity is heated to about 220...

Embodiment 3

[0038]First, the aluminum strip is perforated according to a certain arrangement rule; the aluminum strip is turned into an aluminum half pipe through a preforming mechanism; the aluminum half pipe is heated by a heater to about 220°C, and then enters the inner pipe head to sizing and seams to form an aluminum pipe. After the tube is molded, it is welded into a tube; the polymer plastic material, acrylic acid and filler are fully mixed, heated to 165°C, and extruded through an extruder; the extruded plastic polymer is extruded into the inner tube head At the same time, blow out compressed air to expand the inner plastic tube; extrude the extruded plastic high molecular polymer out of the outer plastic tube with the outer tube head, coat the outer plastic and outer plastic on the outer wall of the aluminum tube, and Propylene hot melt adhesive is evenly coated on the inner and outer walls of the perforated aluminum tube; the temperature in the mold cavity is heated to about 220°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing method of an aluminium butt welding type composite pipe. The manufacturing method is carried out according to the following specific steps: punching an aluminium strip to manufacture an aluminium half pipe; welding the aluminium half pipe into a pipe; preparing a plastic high-molecular polymer; extruding the plastic high-molecular polymer out of an internalplastic pipe and an external plastic pipe, and uniformly coating polypropylene hot melt adhesive on the inner and outer walls of a porose aluminium pipe; simultaneously feeding the internal plastic pipe, the external plastic pipe and the porose aluminium pipe in the die cavity of a coextrusion die head; after the pipe finishing copolymerization for formation, adopting the circulating water coolingmanner to cool to the room temperature, and storing the pipe for 3-7 hours to finish cross-linking reaction; and adding a thermite and the additive silicon dioxide in the inner cavity of the composite pipe to have thermit reaction so as to form a ceramic layer, so that the composite pipe base material and a composite coating are integrally solidified to form the composite pipe. The manufacturingmethod solves the problem in the prior art that the production technology is complicated.

Description

technical field [0001] The invention belongs to the technical field of composite pipe manufacture, and relates to a method for manufacturing an aluminum butt-welded composite pipe. Background technique [0002] At present, aluminum-plastic composite pipes are made of aluminum plates and strips, overlapped and overlapped with each other, and then the ultrasonic welding head is used to heat up the overlapping pipe walls to melt and weld them together to form a pipe. This method can only weld 0.3mm The following thin materials, but the welding speed is slow, and at the same time, due to the stitch welding, the geometric dimensions of the pipe are inaccurate, the thickness of the pipe wall is uneven, and the combination of the aluminum pipe and the plastic pipe is not firm, thus affecting the treatment of the overall composite pipe. The production process is as follows: It consists of a device for forming a continuous metal strip into a U-shaped strip, a jig sleeve that bends th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29D23/00B29C48/09B29C48/21B23K31/02C23C26/02
CPCB23K31/027B29D23/001B29C48/09B29C48/21C23C26/02
Inventor 樊伟
Owner 樊伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap