A light diffusion and glass technology, which is applied in the field of glass production and processing, can solve the problems of plant light burns and low light transmittance, and achieve the effects of reducing burns, moderate light intensity, and no roof truss shadows

Inactive Publication Date: 2019-12-13
中国建材桐城新能源材料有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0025] The purpose of the present invention is to provide a low-sodium and low-iron barium-containing silicic acid to solve the defects of low light transmittance, light shadow and direct light that easily cause light burns to plants in the second-generation ordinary flat glass for greenhouses in the prior art. Salt light-diffusing glass to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Embodiment 1, the composition of the low-sodium and low-iron barium-containing silicate glass contains the following ultra-clear rolled glass composed of the following components by weight percentage:

[0050] Element SiO 2

al 2 o 3

Fe 2 o 3

CaO MgO Na 2 o

BaO Sb 2 o 3

SO 3

Content (wt.%) 71.0～73.0 0.9～1.5 0.0090～0.012 8～10 2.5～3.9 12.5～13.0 0.5～1.5 0.18～0.22 0.20

[0051] The above-mentioned ultra-clear rolled glass is made of the following two raw materials in weight percentage:

[0052] materials silica sand soda ash Calcite dolomite Aluminum powder barium carbonate Compound clarifying agent Proportion (wt.%) 59～62 16.5～17.0 4～7 8～15 0.85～1.5 1.0～2.0 1.2～1.5

[0053] or

[0054] materials silica sand soda ash Calcite dolomite Aluminum powder barium carbonate Compound clarifying agent Proportion (wt.%) 59～62 16.5～17.0 4～7 ...

Embodiment 2

[0055] Embodiment two, the percentage by weight of the ultra-clear rolling glass component described in embodiment one is:

[0056] Element SiO 2

Al 2 o 3

Fe 2 o 3

CaO MgO Na 2 o

BaO Sb 2 o 3

SO 3

Content (wt.%) 72.6 1.5 0.01 8.21 2.5 12.9 1.0 0.18 0.2

[0057] The above-mentioned ultra-clear rolled glass is made of the following two raw materials in weight percentage:

[0058] materials silica sand soda ash Calcite dolomite Aluminum powder barium carbonate Compound clarifying agent Proportion (wt.%) 60.8 17.2 7 10 1.5 2.0 1.5

[0059] or

[0060] materials silica sand soda ash Calcite dolomite Aluminum powder barium carbonate Compound clarifying agent Proportion (wt.%) 60.8 17.2 6.5 9.5 1.5 3.0 1.5

Embodiment 3

[0061] Embodiment three, the percentage by weight of the ultra-clear rolling glass component described in embodiment one is:

[0062] Element SiO 2

Al 2 o 3

Fe 2 o 3

CaO MgO Na 2 o

BaO Sb 2 o 3

SO 3

Content (wt.%) 73.0 1.44 0.01 8.21 3 13.1 0.5 0.18 0.2

[0063] The above-mentioned ultra-clear rolled glass is made of the following two raw materials in weight percentage:

[0064] materials silica sand soda ash Calcite dolomite Aluminum powder barium carbonate Compound clarifying agent Proportion (wt.%) 61.8 17.2 7 10 1.5 1.0 1.5

[0065] or

[0066] materials silica sand soda ash Calcite dolomite Aluminum powder barium carbonate Compound clarifying agent Proportion (wt.%) 61.8 17.2 6.5 9.5 1.5 2.0 1.5

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
transmittivityaaaaaaaaaa
refractive indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a light diffusion glass. The light diffusion glass comprises the basic components of common soda-lime silicate glass, the content of sodium oxide in the basic components of common soda-lime silicate glass is reduced by 1.5wt.%-2.8wt.%, and at the same time, 0.5wt.%-1wt.% of a new component barium oxide is added. Compared with the prior art, the light diffusion glass provided by the invention is machined without changing the existing rolled glass production line equipment, the content of sodium oxide in the components of common soda-lime silicate rolled glass is reduced,the component barium oxide is added, the light diffusion glass has higher light transmittance, better chemical stability, higher thermal shock resistance, better hardness and wear resistance, and higher strength than ultra-white rolled glass, and more importantly, the light diffusion glass increases light scattering and transmission, and while shading a light source and a dazzling light source, also can make the light transmitting the glass become softer and more uniform, thus reaching light-transmitting and non-transparent comfortable effects.

Description

technical field [0001] The invention relates to the technical field of glass production and processing, in particular to a light-diffusing glass. Background technique [0002] As of September 2017, there are about 2.1 million hectares of greenhouses in China (among them: 1.37 million hectares of the first-generation plastic greenhouses and 730,000 hectares of the second-generation ordinary glass greenhouses). These greenhouses are small in scale and occupy a large area (low land utilization rate), poor lighting performance, low level of mechanized cultivation technology, low risk of resisting natural disasters and pests and diseases, harsh planting environment, and serious food environmental protection problems. In order to further meet people's needs for pollution-free and health-care food consumption, the country is now starting to develop the third-generation greenhouse—a solar organic plant factory greenhouse workshop that adopts "Dutch greenhouse agriculture + Israeli p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/087C03C6/04C03C1/00
CPCC03C1/00C03C1/004C03C3/087
Inventor 彭寿杨京安杨镇远
Owner 中国建材桐城新能源材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap