G-C3N4/ TiO2 coating with light-control and antibacterial functions and preparation method thereof

A g-c3n4 coating technology, applied in coating, medical science, tissue regeneration, etc., to achieve the effect of dense coating, high bonding strength and good biological activity

Active Publication Date: 2019-10-15
SOUTHWEST UNIVERSITY
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The object of the present invention is to propose a kind of g-C with light-controlled antibacterial function aiming at the above-mentioned deficiencies of artificial implant materials. 3 N 4 / TiO 2 A coating and a preparation method thereof, and a coating and a preparation method thereof that can significantly improve surface bioactivity, cell regulation ability, surface antibacterial properties and various beneficial functions at the initial stage of implantation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • G-C3N4/ TiO2 coating with light-control and antibacterial functions and preparation method thereof
  • G-C3N4/ TiO2 coating with light-control and antibacterial functions and preparation method thereof
  • G-C3N4/ TiO2 coating with light-control and antibacterial functions and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) First select TC4 titanium alloy.

[0031] (2) Pretreatment: The titanium-based alloy implant material is polished and polished step by step with metallographic sandpaper with the labels of 600#, 800#, and 1000# from coarse sand to fine sand, and then with acetone, 70% alcohol, and distilled water Ultrasonic cleaning, dry for use.

[0032] (3) Chemical polishing: prepare 40 ml of polishing solution containing hydrofluoric acid and concentrated nitric acid, the volume ratio is: H 2 O: HF: HNO 3 =5:1:4; put TC4 titanium alloy in chemical polishing solution and polish for 3 min.

[0033] (4) Advanced oxidation: Prepare 5 wt% hydrogen peroxide solution, put the TC4 titanium alloy in the oxidation solution, and irradiate its outer surface with a 254nm ultraviolet lamp, and the oxidation treatment time is 4 h.

[0034] (5) Hydrothermal synthesis treatment: The advanced oxidized TC4 titanium alloy was hydrothermally synthesized with a sodium hydroxide solution with a con...

Embodiment 2

[0038] (1) First select TC4 titanium alloy.

[0039] (2) Pretreatment: The titanium-based alloy implant material is polished and polished step by step with metallographic sandpaper with the labels of 600#, 800#, and 1000# from coarse sand to fine sand, and then with acetone, 70% alcohol, and distilled water Ultrasonic cleaning, dry for use.

[0040] (3) Chemical polishing: prepare 40 ml of polishing solution containing hydrofluoric acid and concentrated nitric acid, the volume ratio is: H 2 O: HF: HNO 3 =5:1:4; put TC4 titanium alloy in chemical polishing solution and polish for 3 min.

[0041] (4) Advanced oxidation: Prepare 5 wt% hydrogen peroxide solution, put the TC4 titanium alloy into the oxidation solution, and irradiate its outer surface with a 254nm ultraviolet lamp, and the oxidation treatment time is 3 h.

[0042] (5) Hydrothermal synthesis treatment: The highly oxidized titanium alloy bone nail was hydrothermally reacted with a sodium hydroxide solution with a c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a g-C3N4 / TiO2 coating with light-control and antibacterial functions and a preparation method thereof. The light-control antibacterial coating consists of TiO2 with athree-dimensional network structure and graphite-like phase carbon nitride (g-C3N4) deposited on the surface of the TiO2. The g-C3N4 / TiO2 coating with a three-dimensional network structure is combined with the surface of a titanium or titanium alloy substrate, rod-shaped nano-array sodium titanate is constructed on the surface of the substrate by a hydrothermal synthesis method, the nano-array sodium titanate is converted into titanium dioxide by a chemical vapor deposition technology, and the g-C3N4 is deposited at the same time. The preparation method comprises the following steps of: firstly, acquiring a rod-shaped nano-array sodium titanate biological coating on the surface of the substrate by adopting a hydrothermal synthesis method; and then converting the coating into titanium dioxide by using a high-temperature annealing technology, taking melamine as a raw material, and depositing g-C3N4 on the surface of the titanium dioxide through a chemical vapor deposition technology soas to finally obtain the g-C3N4 / TiO2 coating with the light-control and antibacterial functions.

Description

technical field [0001] The invention relates to a g-C with light-controlled antibacterial function 3 N 4 / TiO 2 The coating and its preparation method, especially relate to a sodium titanate bioceramic coating with titanium and its alloys as the base material, which is controlled to grow nanorod array structure on its surface by hydrothermal synthesis method. Using high-temperature annealing process and chemical vapor deposition technology to transform sodium titanate nanorod array structure into TiO with g-C3N4 nanosheets deposited on the surface 2 A coating with a three-dimensional network structure and a preparation method thereof belong to the technical field of biomedical materials. Background technique [0002] Titanium and titanium alloys have excellent biocompatibility, high strength, toughness and corrosion resistance. They are the main raw materials for mid-to-high-end surgical implants commonly used in current clinical treatment. They can be used as denture imp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61L27/06A61L27/56A61L27/30A61L27/50
CPCA61L27/06A61L27/56A61L27/306A61L27/50A61L2420/02A61L2430/02
Inventor 饶席杜陵
Owner SOUTHWEST UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com