Preparation method of tough scratch-resistant PMMA/ABS suitcase material

A box material and anti-scratch technology, applied in the field of polymer materials, can solve problems such as polluting the environment and increasing production costs, and achieve the effects of simple preparation process, improved surface hardness of ABS, broad application prospects, and economic and social benefits.

Pending Publication Date: 2019-09-20
XIANGXING FUJIAN BAG ANDLUGGAGE GRP CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These means not only increase production costs but also pollute the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] A kind of preparation method of strong and tough anti-scratch PMMA / ABS casing material, it comprises:

[0030] (1) Place polymethyl methacrylate, acrylonitrile-butadiene-styrene, ethylene-methyl acrylate copolymer and elastomer grafts in drying equipment for drying treatment;

[0031] (2) Add nano-titanium dioxide and dried polymethyl methacrylate, acrylonitrile-butadiene-styrene, ethylene-methyl acrylate copolymer and elastomer grafts into the mixing equipment for uniform mixing to prepare mixed raw materials;

[0032] (3) Add the mixed raw materials into a granulator for granulation treatment to obtain a granulated tough and scratch-resistant PMMA / ABS box material.

[0033] Further, the working temperature of the drying equipment in step (1) is 80°C.

[0034] Further, the working temperature of the granulator in step (3) is 210-250°C.

[0035] A strong and tough anti-scratch PMMA / ABS box body is made by injection molding of the above-mentioned strong and tough anti...

Embodiment 1

[0037] A tough anti-scratch PMMA / ABS box material, its raw material is mixed with the following components:

[0038] Polymethyl methacrylate (PMMA) 15 parts;

[0039] Acrylonitrile-butadiene-styrene (ABS) 78 parts;

[0040] 4 parts of ethylene-methyl acrylate copolymer (EMA);

[0041] 2 parts of elastomer graft;

[0042] Nano titanium dioxide 1 part.

[0043] Wherein, the elastomer graft is SEBS-g-MAH.

[0044] Its preparation method includes:

[0045] (1) Place polymethyl methacrylate, acrylonitrile-butadiene-styrene, ethylene-methyl acrylate copolymer and elastomer grafts in drying equipment for drying treatment at a temperature of 80°C;

[0046] (2) Add nano-titanium dioxide and dried polymethyl methacrylate, acrylonitrile-butadiene-styrene, ethylene-methyl acrylate copolymer and elastomer grafts into the mixing equipment for uniform mixing to prepare mixed raw materials;

[0047] (3) Add the mixed raw materials into a granulator and perform granulation treatment at ...

Embodiment 2

[0049] A tough anti-scratch PMMA / ABS box material, its raw material is mixed with the following components:

[0050] Polymethyl methacrylate (PMMA) 25 parts;

[0051] Acrylonitrile-butadiene-styrene (ABS) 67 parts;

[0052] 5 parts of ethylene-methyl acrylate copolymer (EMA);

[0053] 2 parts of elastomer graft;

[0054] Nano titanium dioxide 1 part.

[0055] Wherein, the elastomer graft is SEBS-g-MAH.

[0056] Its preparation method includes:

[0057] (1) Place polymethyl methacrylate, acrylonitrile-butadiene-styrene, ethylene-methyl acrylate copolymer and elastomer grafts in drying equipment for drying treatment at a temperature of 80°C;

[0058] (2) Add nano-titanium dioxide and dried polymethyl methacrylate, acrylonitrile-butadiene-styrene, ethylene-methyl acrylate copolymer and elastomer grafts into the mixing equipment for uniform mixing to prepare mixed raw materials;

[0059] (3) Add the mixed raw materials into a granulator and perform granulation treatment at ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a tough scratch-resistant PMMA / ABS suitcase material. PMMA is used to modify ABS to obtain a composite material. A suitcase made of the composite material has the advantages of high surface hardness, high glossiness, scratch resistant property, and low cost, does not need any protective film, and does not need any spraying or electroplating. The material can be applied to one-time injection molding or blister forming, and the steps such as mulching, polishing, grinding, spraying, and the like are not needed. The material has metal luster. Furthermore, the preparation technology is simple, the cost is low, and the ABS surface hardness of obtained PMMA / ABS alloy is improved. The suitcase material has excellent mechanical properties, can be widely applied to electronic products and automobile parts, does not need a conventional plastic surface spraying technology, has a wide application prospect, and generates high social and economical benefits. The provided tough scratch-resistant PMMA / ABS suitcase material promotes the technological development of the suitcase industry.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a preparation method of a strong and tough anti-scratch PMMA / ABS box material. Background technique [0002] ABS is an engineering plastic with excellent comprehensive performance. It can still maintain high impact strength at low temperature. At the same time, it has good dimensional stability, good insulation, wear resistance and oil resistance. It is widely used in daily necessities, household appliances, mechanical parts, Office supplies and communication equipment and other fields. However, pure ABS has some defects, such as: low surface hardness, easy to scratch, high melt viscosity, poor fluidity, poor thermal stability and weather resistance, which limit its further application. Traditional ABS hard-shell boxes are popular among consumers because of their moderate price and light weight. In order to improve the scratch resistance of ABS box shells, luggage manufacturers ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L33/12C08L23/08C08K3/22
CPCC08L55/02C08L2205/035C08K2201/011C08K2003/2241C08L33/12C08L23/0869C08K3/22
Inventor 谢孝波薛行远彭超涂思敏
Owner XIANGXING FUJIAN BAG ANDLUGGAGE GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap