Novel jewelry silver alloy with surface barrier diffraction effect

A diffraction effect, silver alloy technology, applied in the field of alloys, can solve the problem of no large-scale promotion and industrialization of silver jewelry, achieve excellent liquid and solid solidification temperature range, reduce hot cracking tendency, low absorption The effect of Qi ability

Inactive Publication Date: 2019-07-26
杭州辰卓科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, although the gold alloy with the Spaniel effect has been successfully developed for gold alloys, that is, the grating effect generated on the surface by using the martensitic phase transformation of gold, there are still very few reports on the Spaniel alloy of the silver-based alloy in the international scope. So little, so that there is no large-scale promotion and industrialization of Sban silver jewelry at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A new type of silver alloy for jewelry with surface barrier diffraction effect. In terms of weight percentage, the alloy composition is: Re: 0.2wt.%, Hf: 0.5wt.%, Fe: 2.0wt.%, Y: 0.1wt.%, In: 20.0wt.%, Pt: 1.0wt.%. %, Mn: 1.5wt.%, Sn: 5.0wt.%, the balance is silver.

[0017] The above-mentioned new silver alloy for jewelry with surface fence diffraction effect includes the following steps: (a) Ingredients: weigh the raw materials according to the above mass percentage; (b) Smelting: non-vacuum induction melting with argon protection The furnace is smelted, and the crucible is graphite crucible; the alloy melt is fully stirred at 1080 degrees for 10 minutes and electromagnetic stirring is used, and then iron molds are cast, and water cooling is used for rapid cooling; (c) subsequent pressure processing and heat treatment : The obtained ingot is rolled at room temperature, and the rolling volume per pass is 6%; the intermediate annealing temperature after each two rolling i...

Embodiment 2

[0020] A new type of silver alloy for jewelry with surface barrier diffraction effect. In terms of weight percentage, the alloy composition is: Re: 0.5wt.%, Hf: 1.0wt.%, Fe: 4.0wt.%, Y: 0.2wt.%, In: 25.0wt.%, Pt: 2.0wt.%. %, Mn: 2.0wt.%, Sn: 10.0wt.%, the balance is silver.

[0021] The above-mentioned new silver alloy for jewelry with surface fence diffraction effect includes the following steps: (a) Ingredients: weigh the raw materials according to the above mass percentage; (b) Smelting: non-vacuum induction melting with argon protection The furnace is smelted, in which the crucible is a graphite crucible; the alloy melt is fully stirred at 1090 degrees for 10 minutes and electromagnetic stirring is used, and then the iron mold is cast, and water cooling is used for rapid cooling; (c) subsequent pressure processing and heat treatment : Roll the resulting ingots at room temperature, with a rolling reduction of 5% per pass; after each two rolling, the intermediate annealing tem...

Embodiment 3

[0024] A new type of silver alloy for jewelry with surface barrier diffraction effect. In terms of weight percentage, the alloy composition is: Re: 0.3wt.%, Hf: 0.8wt.%, Fe: 2.8wt.%, Y: 0.1wt.%, In: 23.0wt.%, Pt: 1.5wt. %, Mn: 1.8wt.%, Sn: 8.0wt.%, the balance is silver.

[0025] The above-mentioned new silver alloy for jewelry with surface fence diffraction effect includes the following steps: (a) Ingredients: weigh the raw materials according to the above mass percentage; (b) Smelting: non-vacuum induction melting with argon protection The furnace is smelted, in which the crucible is a graphite crucible; the alloy melt is fully stirred at 1100 degrees Celsius for 10 minutes and electromagnetic stirring is used, then iron molds are used for casting, and water cooling is used for rapid cooling; (c) subsequent pressure processing and heat treatment : Roll the resulting ingots at room temperature, and the amount of rolling is 8% per pass; after each two rolling, the intermediate a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel jewelry silver alloy with a surface barrier diffraction effect. The novel jewelry silver alloy with the surface barrier diffraction effect comprises, by weight, 0.2%-0.5% of Re, 0.5%-1.0% of Hf, 2.0%-4.0% of Fe, 0.1%-0.2% of Y, 20.0%-25.0% of In, 1.0%-2.0% of Pt, 1.5%-2.0% of Mn, 5.0%-10.0% of Sn, and the balance sliver. The novel silver alloy has a colorful appearance like pearls and meets the current requirements of the jewelry industry, namely the alloy has a Spangold effect. The novel jewelry silver alloy has great social value and economic value while meeting the current requirement for high-end jewelry silver alloys.

Description

Technical field [0001] The invention relates to the technical field of alloys, in particular to a silver alloy. Background technique [0002] Among jewelry alloys, gold alloys are the most important. The market demand for gold alloys for jewelry has expanded rapidly in the jewelry market in recent years, which indirectly illustrates the important position of gold jewelry in the world's jewelry industry. This is largely due to the beautiful color of gold, long-term storage without discoloration, and good processing properties. Although there are many types of gold alloys used in jewelry, and the appearance of color is changeable, the most eye-catching is the gold alloy for jewelry called Span gold. [0003] Spangold uses the martensite in the gold alloy or the surface relief and fine layered structure produced by the martensite transformation to produce the grating barrier diffraction effect under the action of light, so that the surface of the gold alloy can produce similar Beca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C5/06C22C1/02C22F1/14C22F1/02A44C27/00
CPCA44C27/003C22C1/02C22C5/06C22F1/002C22F1/02C22F1/14
Inventor 刘亚军
Owner 杭州辰卓科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com