N,S-codoped graphene/molybdenum selenide/CoFe-LDH aerogel and preparation thereof

A graphene and co-doping technology, applied in the direction of graphene, binary selenium/tellurium compounds, inorganic chemistry, etc., can solve the problems of low utilization efficiency, limited wide use, and scarce resources, and achieve easy product structure and low cost. Low, safe operation effect

Active Publication Date: 2019-05-21
SHANGHAI INST OF TECH
View PDF11 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although noble metal catalysts (such as Pt-based catalysts for hydrogen evolution reaction and Ir-based catalysts for oxygen evolution reaction) are currently the most promising catalysts for water splitting, their high price and scarcity of resources greatly limit their widespread use.
In recent years, a lot of research work has reported that non-noble metal catalysts catalyze hydrogen evolution or oxygen evolution in water, and some progress has been made, but these catalysts either catalyze the oxygen evolution reaction in alkaline electrolytes or catalyze Hydrogen evolution reaction, its water utilization efficiency is not high
Considering the practical application of water splitting, efficient electrocatalysts must catalyze both hydrogen evolution reaction and oxygen evolution reaction in the same electrolyte (mainly in alkaline electrolyte), which is a challenge for many current catalysts with high activity in acidic electrolytes. say still a challenge

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • N,S-codoped graphene/molybdenum selenide/CoFe-LDH aerogel and preparation thereof
  • N,S-codoped graphene/molybdenum selenide/CoFe-LDH aerogel and preparation thereof
  • N,S-codoped graphene/molybdenum selenide/CoFe-LDH aerogel and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0048] N, S co-doped graphene / MoSe of the preferred embodiment of the present invention 2 The preparation method of / CoFe-LDH comprises:

[0049] S1, ultrasonically disperse graphite oxide in deionized water to prepare a graphene oxide lamellar dispersion. Preferably, the concentration of the prepared graphene oxide sheet dispersion is 0.5-3mg mL -1 , more preferably 2mg mL -1 .

[0050] Specifically, the graphite oxide is prepared by the following method:

[0051] S11, under ice bath and vigorous stirring, NaNO 3 Add concentrated sulfuric acid until NaNO 3 completely dissolved.

[0052] For example: adding concentration to the three-necked reaction flask is 98% concentrated sulfuric acid (H 2 SO 4 ), and the reaction bottle was placed in an ice-water bath and stirred at 150rpm, adding NaNO 3 , and continue to stir in an ice-water bath to dissolve it. Wherein, the concentrated sulfuric acid and NaNO 3 The weight ratio is: 60:1~100:1.

[0053] S12, maintain ice bath,...

Embodiment 1

[0082] A kind of N,S co-doped graphene / MoSe 2 The preparation method of / CoFe-LDH airgel comprises:

[0083] (1) Preparation of graphene oxide (GO) lamellar dispersion: disperse 200 mg of the above-mentioned graphite oxide in 100 mL of deionized water, and ultrasonically disperse for 1 hour to obtain a tan GO lamellar dispersion with a GO concentration of 2 mg mL -1 .

[0084] (2) Preparation of ultra-thin MoSe by liquid phase exfoliation 2 Preparation of nanosheet dispersion: 20mg bulk MoSe 2 Add 4 mL of isopropanol (IPA) / water mixed solvent with a volume fraction of 60%, put it into an ultrasonic instrument and perform ultrasonic vibration treatment with a power of 200W and a frequency of 40kHz for 4 hours, and maintain the ultrasonic wave by adding circulating cooling water. The temperature was controlled at room temperature during the process. Subsequently, the sonicated solution was centrifuged at 4000 rpm for 20 min to remove the unexfoliated bulk MoSe at the bottom....

Embodiment 2

[0096] The reaction and operating conditions of this example are basically the same as those of Example 1, except that the reducing agent in Example 1 is ascorbic acid, and the crosslinking agent is polypyrrole.

[0097] After testing, the N,S co-doped graphene / MoSe prepared by the present invention 2 / CoFe-LDH composite aerogel as an electrocatalytic water splitting electrode has excellent electrocatalytic water splitting performance, by Figure 5-8 As shown, when the current density is 100mA / cm 2 , the overpotential of the hydrogen evolution reaction is -290mV, and the overpotential of the oxygen evolution reaction is 1.65V.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
volumeaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

A preparing method of N,S-codoped graphene / MoSe2 / CoFe-LDH aerogel is provided. The method is characterized by including S1) separately preparing a graphene oxide sheet dispersion, a MoSe2 nanosheet dispersion and a layered CoFe-LDH nanosheet dispersion; S2) mixing the graphene oxide sheet dispersion and the MoSe2 nanosheet dispersion, adding a reductant and a crosslinking agent, fully mixing the mixture, reacting the mixture to obtain N,S-codoped graphene / MoSe2 hydrogel, freeze-drying the hydrogel to obtain N,S-codoped graphene / MoSe2 aerogel; and S3) soaking the N,S-codoped graphene / MoSe2 aerogel in the layered CoFe-LDH nanosheet dispersion to obtain N,S-codoped graphene / MoSe2 / CoFe-LDH hydrogel, and freeze-drying the hydrogel to obtain the N,S-codoped graphene / MoSe2 / CoFe-LDH aerogel. The prepared ternary N,S-codoped graphene / MoSe2 / CoFe-LDH aerogel has more excellent hydrogen evolution and oxygen evolution properties under alkaline conditions.

Description

technical field [0001] The invention relates to an electrode hydrogen and oxygen evolution material, in particular to a N, S co-doped graphene / MoSe 2 / CoFe-LDH and its preparation method. Background technique [0002] Energy and the environment are the material basis for the survival and development of human society, and their importance is self-evident. In recent years, with the rapid growth of the world's population and the accelerated consumption of energy, problems such as energy shortage and environmental pollution have become increasingly serious, posing a huge threat to human survival and health. In view of this, there is an imminent human demand for new, sustainable and clean energy. Electrocatalytic water splitting is one of the important ways to efficiently generate renewable clean energy, and its decomposition products are only O 2 and H 2 , zero pollution to the environment, and O 2 and H 2 It can also be used as a raw material for fuel cells, so water spli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25B11/06C25B1/04C01B19/04C01B32/184C01B32/194C01G51/00B82Y30/00B82Y40/00
CPCY02E60/36
Inventor 徐小威贾润萍燕飞黄志雄赵呈
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com