Waterborne polyurethane dispersion and one-component waterborne adhesive for pvc calendered coating including it

A water-based adhesive, water-based polyurethane technology, applied in textiles and papermaking, etc., can solve the problems of reducing service life, residue, and smell.

Active Publication Date: 2021-04-20
WANHUA CHEMICAL (NINGBO) CO LTD +2
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the addition of a large amount of plasticizers and other materials in the production of PVC calendering coatings, during long-term use, due to the migration of plasticizers, the PVC layer is separated from the fabric substrate, reducing the service life, so it is necessary to coat a layer Adhesive layer, solvent-based PU adhesive is commonly used at present, because of its strong taste, it will leave toxic and harmful substances such as DMF, toluene, methyl ethyl ketone, etc., and the bubbles of PVC coating products will be caused by solvent volatilization. With the increase of people's environmental awareness, Restricted by national policies, solvent-based PU adhesives are difficult to meet the increasingly high environmental protection requirements in home decoration, raincoats, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne polyurethane dispersion and one-component waterborne adhesive for pvc calendered coating including it

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Add 240g of dehydrated poly(1,4-butylene adipate) (molecular weight: 3000), 50g of TDI-80, 20g of HMDI, 36.5g of acetone, and an appropriate amount of catalyst (bismuth isooctanoate, 100ppm) to the nitrogen inlet and outlet. In a 1 L four-neck round bottom flask, the mixture was stirred at 60-80° C. until NCO reached 6.8%. Add 8g of 1,4-butanediol, 14g of dimethylolpropionic acid and 80g of acetone and continue the reaction at 60°C until NCO reaches 1.70. Then add 200g of acetone to dilute and cool down to 40°C, add 9.51g of triethylamine to neutralize for 10 minutes, add 503g of water under high-speed stirring to stir and disperse, add 3.0g of ethylenediamine to continue stirring for 15 minutes. After separating the acetone from the obtained acetone-containing emulsion by distillation, a solvent-free aqueous polyurethane dispersion with a particle size of 45 nm was obtained.

[0045] Take 100 parts of the obtained water-based polyurethane and add it into the dispersio...

Embodiment 2

[0047] Add 240g of dehydrated poly-1,4-butylene adipate (molecular weight: 2000), 50g of TDI-80, 35g of HMDI, 36.6g of acetone, and an appropriate amount of catalyst (bismuth isooctanoate, 100ppm) into the nitrogen inlet and outlet. In a 1 L four-neck round bottom flask, the mixture was stirred at 60-80° C. until NCO reached 6.99%. Add 8g of 1,4-butanediol, 15g of dimethylolpropionic acid and 80g of acetone and continue the reaction at 60°C until the NCO reaches 1.81. Then add 210g of acetone to dilute and cool down to 40°C, add 10.2g of triethylamine to neutralize for 10min, add 503g of water under high-speed stirring to stir and disperse, add 4.2g of ethylenediamine to continue stirring for 15min. After separating the acetone from the obtained acetone-containing emulsion by distillation, a solvent-free aqueous polyurethane dispersion with a particle size of 50 nm was obtained.

[0048] Take 100 parts of the obtained water-based polyurethane and add it into the dispersion ta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
molecular weightaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a water-based polyurethane dispersion and a one-component water-based adhesive for PVC calendering coating including the water-based polyurethane dispersion. The adhesive balances soft feel and bond strength. The water-based adhesive is composed of the following components: water-based polyurethane dispersion, water-based leveling agent, water-based wetting agent, water-based defoamer, pH regulator, and thickener. The invention also relates to a roll coating process used for the one-component water-based adhesive for the calendering coating. The one-component water-based adhesive for PVC calendering coating disclosed by the present invention can be used for compounding PVC paste and textile substrates, including scraping and roller coating processes, and the prepared PVC calendering coating has very high initial bonding strength. Peel strength after stabilization, resistance to plasticizers and high jungle resistance, can be widely used in packaging bags, raincoats, tablecloths, curtains, etc.

Description

technical field [0001] The invention relates to a water-based polyurethane dispersion and a single-component water-based adhesive for PVC calendering coating including the same, in particular to a water-based adhesive for calendering coating applied to a roll coating process PVC coating, and also to PVC The coating uses a one-component water-based adhesive preparation method. Background technique [0002] Due to its high chemical stability, polyvinyl chloride resin can be used in various fields such as making anti-corrosion pipes, pipe fittings, oil pipelines, centrifugal pumps and blowers. In daily life, polyvinyl chloride is used to make PVC artificial leather and PVC coating. After mixing and plasticizing PVC and plasticizer, use a three-roller or four-roller calender to apply directly on the textile substrate after high temperature to make a transparent or colored textile coating with a specified thickness. The PVC calendered coating is light in weight , water resistan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/73C08G18/76C08G18/66C08G18/42C08G18/34C08G18/32D06N3/00D06N3/14
Inventor 邓俊英李海峰王震纪学顺
Owner WANHUA CHEMICAL (NINGBO) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com