A preparation method of light-controlled color-changing colorful aluminum alloy wheel hub

An aluminum alloy wheel hub, light-controlled discoloration technology, applied in multi-color effect coatings, coatings, epoxy resin coatings, etc., can solve problems such as poor weather resistance of primers, achieve good adhesion, good mechanical properties, and simple preparation methods. Effect

Active Publication Date: 2020-09-18
ZHEJIANG WANFENG MOTORCYCLE WHEEL
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This primer can be used for wheel hub coating, which can effectively cover defects such as depressions and sand marks on the hub; however, this primer has poor weather resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of light-controlled color-changing colorful aluminum alloy wheel hub
  • A preparation method of light-controlled color-changing colorful aluminum alloy wheel hub
  • A preparation method of light-controlled color-changing colorful aluminum alloy wheel hub

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for preparing a light-controlled color-changing colorful aluminum alloy wheel hub, comprising the following steps:

[0029] (1) Mix ethyl acetate and absolute ethanol, stir and mix evenly, then add titanium tetrachloride, and finally add triethylamine dropwise, and transfer the prepared mixed solution to a reaction kettle for 10 hours at 120°C to obtain a titanium-containing Sol; Wherein, the volume ratio of ethyl acetate, dehydrated alcohol, titanium tetrachloride, triethylamine is 1:50:1:1;

[0030] (2) Dissolve ethyl orthosilicate in absolute ethanol, stir and mix for 5-15min, then slowly add deionized water dropwise, stir while adding, after the dropwise addition, heat up to 50°C and continue stirring for 1h to prepare Obtain a silica sol; wherein, the volume ratio of ethyl orthosilicate, absolute ethanol, and deionized water is 1:50:0.5;

[0031] (3) Graphite powder is placed in dehydrated alcohol, 500W power is ultrasonically treated 1h, then dropwise ad...

Embodiment 2

[0036] A method for preparing a light-controlled color-changing colorful aluminum alloy wheel hub, comprising the following steps:

[0037] (1) Mix ethyl acetate and absolute ethanol, stir and mix evenly, then add titanium tetrachloride, and finally add triethylamine dropwise, transfer the prepared mixed solution to a reaction kettle for 15 hours at 150°C, and obtain titanium-containing Sol; Wherein, the volume ratio of ethyl acetate, dehydrated alcohol, titanium tetrachloride, triethylamine is 2:50:1:1;

[0038] (2) Dissolve ethyl orthosilicate in absolute ethanol, stir and mix for 5-15min, then slowly add deionized water dropwise, stir while adding, after the dropwise addition, heat up to 80°C and continue stirring for 2h to prepare Obtain silica-containing sol; wherein, the volume ratio of ethyl orthosilicate, absolute ethanol, and deionized water is 1:50:1.5;

[0039] (3) Graphite powder is placed in absolute ethanol, 1500W power is ultrasonically treated 4h, then dropwis...

Embodiment 3

[0044] A method for preparing a light-controlled color-changing colorful aluminum alloy wheel hub, comprising the following steps:

[0045] (1) Mix and stir ethyl acetate and absolute ethanol evenly, then add titanium tetrachloride, and finally add triethylamine dropwise, and transfer the obtained mixed solution to a reaction kettle for 11 hours at 130°C to obtain titanium-containing Sol; Wherein, the volume ratio of ethyl acetate, dehydrated alcohol, titanium tetrachloride, triethylamine is 1:50:1:1;

[0046] (2) Dissolve ethyl orthosilicate in anhydrous ethanol, stir and mix for 5-15min, then slowly add deionized water dropwise, stir while adding dropwise, after the dropwise addition, raise the temperature to 60°C and continue stirring for 1.5h, A silica-containing sol is obtained; wherein, the volume ratio of ethyl orthosilicate, absolute ethanol, and deionized water is 1:50:0.7;

[0047] (3) Graphite powder is placed in dehydrated alcohol, 2h of sonication under 800W powe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method for a light-controlled color-changing colorful aluminum alloy wheel hub. The preparation method comprises the following concrete steps: preparing a modified filling material, then mixing acrylic resin, amino resin, epoxy resin and a diluent into a high-speed dispersing machine, carrying out mixing under stirring, then successively adding the above-mentioned prepared modified filling material, CAB381, an anti-settling wax 229, a leveling agent, a color-changing photosensitizer and butyl ester, continuing stirring until uniform mixing is realized, andcarrying out grinding treatment in a three-roll grinder so as to prepare a coating; and polishing a motorcycle aluminum alloy wheel hub, carrying out cleaning and drying treatment, spraying a prepared coating onto the surface of the aluminum alloy wheel hub, then carrying out flash-drying at 100 DEG C, continuing spraying treatment, and carrying out baking at 150 DEG C for 3 to 5 min so as to prepare a light-controlled color-changing colorful motorcycle aluminum alloy wheel hub. The aluminum alloy wheel hub prepared by using the preparation method provided by the invention can automatically change colors with the change of illumination, and has good coating mechanical properties.

Description

Technical field: [0001] The invention relates to the field of alloy preparation, in particular to a method for preparing an optically controlled discoloration and colorful aluminum alloy wheel hub. Background technique: [0002] At present, in the traditional processing technology of aluminum alloy wheels of motorcycles, although the appearance colors are available in various colors, they are relatively single on the wheels. In order to meet individual requirements, several mixed coating processes of different colors have been developed in recent years, but none of them are truly novel and cannot meet the changing market demands of the younger generation in pursuit of fashion. [0003] Chinese patent (201610894865.6) discloses a high temperature resistant primer and its preparation method and application; solvents and thinners. The primer can be used for wheel hub coating, and can effectively cover defects such as depressions and sand marks on the hub; however, the primer ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/04C09D161/20C09D163/00C09D7/62C09D5/29
CPCC08K2003/2237C08K2201/011C08L2205/035C09D5/29C09D7/62C09D133/04C08L61/20C08L63/00C08K13/06C08K9/06C08K3/042C08K3/22C08K3/34
Inventor 吕允刚朱贤忠安博石柏江刘浩红杨斌斌
Owner ZHEJIANG WANFENG MOTORCYCLE WHEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More