Preparation method of adsorption filter element used for treating radioactive waste liquid and adsorption filter element

An adsorption filter element and modification technology, which is applied in the field of wastewater treatment, can solve the problems of destruction of the adsorption bed, overall performance decline, pollution treatment process, etc., and achieve the effect of large adsorption surface area, compact filter element structure and high adsorption capacity

Active Publication Date: 2019-04-12
RES INST OF PHYSICAL & CHEM ENG OF NUCLEAR IND
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the irregular shape and poor mechanical strength of most ion exchangers, it is easy to cause rupture and form a large number of small particles during the filling process, such as vibration, pressurization, edge fixing and other steps, or under the impact of water flow during application, forming a large number of small particles. When channeling is easy to form, the adsorption bed is destroyed, and the overall performance decreases
In addition, the ion exchanger contains a large number of small particles, which often occur in practical applications, pollute the subsequent treatment process, and cause adverse effects on the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of adsorption filter element used for treating radioactive waste liquid and adsorption filter element
  • Preparation method of adsorption filter element used for treating radioactive waste liquid and adsorption filter element
  • Preparation method of adsorption filter element used for treating radioactive waste liquid and adsorption filter element

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The preparation method of the adsorption filter core of the present invention comprises the steps of modifying the porous material mixture with zero-valent iron after grinding, mixing with the ground binder and high-density extrusion molding. The porous material is a microporous material with a pore size of 0.01 μm to 10 μm, such as a mixture of zeolite powder, bentonite, kaolin, graphene, and alumina. The adhesive used for extrusion molding of the porous material is Polyacrylonitrile or ultra-high molecular weight polyethylene. The density of the filter element is 5000kg / m 3 Above, such as 10000-80000kg / m 3 , preferably 30000-50000kg / m 3 .

[0036] The zeolite powder, bentonite, kaolin, graphene, and alumina used in the present invention are all microporous materials with rich and well-developed pore structures. After grinding, the particle size of the powder and the adhesive is controlled above 200 mesh, such as 300 mesh. ~500 mesh, and then modified by zero-valen...

Embodiment 1

[0041] (1) Weigh 3250g of modified zeolite powder, 750g of calcium-based bentonite, 400g of calcined kaolin, 350g of activated alumina, 25g of graphene oxide, and mix uniformly; the modified zeolite powder is a modified zeolite treated with 10% hydrochloric acid pink;

[0042] (2) The mixture is fully ground, and the average particle diameter of the controlled grinding mixed powder particles is 300 mesh;

[0043] (3) Soak the mixed powder in an aqueous solution with a starch content of 5%, a ferrous ion content of 4%, and a pH of 8 at room temperature for 20 minutes, then take it out and dry it;

[0044] (4) taking out the dried powder in the step (3) after being soaked for 5 minutes in the sodium borohydride aqueous solution of pH 8.5;

[0045] (5) Heat the air-dried powder in step (4) to about 380°C at a heating rate of 100°C / h under nitrogen protection, keep it warm for 2.5 hours, cool it down to below 120°C, and take it out to cool down naturally;

[0046] (6) Microwave dr...

Embodiment 2

[0054] (1) Take by weighing 3000g of modified zeolite powder, 650g of calcium-based bentonite, 350g of calcined kaolin, 300g of activated alumina, 15g of graphene oxide, and mix uniformly;

[0055] (2) The mixture is fully ground, and the average particle diameter of the controlled grinding mixed powder particles is 300 mesh;

[0056] (3) Soak the mixed powder in an aqueous solution with a starch content of 5%, a ferrous ion content of 4%, and a pH of 7.5 at room temperature for 25 minutes, then take it out and dry it;

[0057] (4) taking out the dried powder in the step (3) after being soaked in an aqueous solution of sodium borohydride with a pH of 9 for 4 minutes;

[0058] (5) Heat the dried powder in step (4) to about 420°C at a heating rate of 80°C / h under nitrogen protection, keep it warm for 3 hours, cool it down to below 120°C, and take it out to cool down naturally;

[0059] (6) Microwave drying the modified mixed powder obtained in step (5) at 400°C for 6.5 hours; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of an adsorption filter element used for treating a radioactive waste liquid and the adsorption filter element. According to the high-density extrusion process molding provided by the invention, the filter element has a compact structure and high mechanical strength, and conditions of damage and leakage of micro-particles do not occur during use; and the filter element is formed by high-density extrusion molding of microporous materials such as zeolite powder, bentonite, kaolin, graphene, aluminum oxide and the like, the filter element has a compactstructure and the characteristics of a large adsorption surface area, high adsorption capacity and high adsorption efficiency.

Description

technical field [0001] The invention belongs to the technical field of wastewater treatment, and in particular relates to a preparation method of an adsorption filter core for treating radioactive waste liquid and the adsorption filter core. Background technique [0002] The advantage of the ion exchange method for treating radioactive waste is that it is easy to operate and has a better decontamination and purification effect, but it is only suitable for systems with low salt content (<1g / L) and suspended pollutants (<4mg / L). In the practical application of the ion exchange method, the ion exchanger is filled into the exchange column, and the general filling volume is 4 / 5 of the column height. However, due to the irregular shape and poor mechanical strength of most ion exchangers, it is easy to cause rupture and form a large number of small particles during the filling process, such as vibration, pressurization, edge fixing and other steps, or under the impact of wate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01D39/20G21F9/12
CPCB01D39/2068B01D2239/0407G21F9/12
Inventor 刘明亚魏世超毕远伟杜鹃王焕志
Owner RES INST OF PHYSICAL & CHEM ENG OF NUCLEAR IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap