Composite passivating agent for galvanized plate and aluminum alloy and copper alloy metal plate

A passivation agent, aluminum alloy technology, applied in the direction of metal material coating process, etc., to achieve good salt resistance and improve corrosion resistance.

Inactive Publication Date: 2019-01-01
ANHUI UNIVERSITY OF TECHNOLOGY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing passivators are difficult to meet the above requirements at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite passivating agent for galvanized plate and aluminum alloy and copper alloy metal plate
  • Composite passivating agent for galvanized plate and aluminum alloy and copper alloy metal plate
  • Composite passivating agent for galvanized plate and aluminum alloy and copper alloy metal plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] It is determined that the mass percent composition of the composite passivating agent for galvanized sheet, aluminum alloy and copper alloy metal plate is as follows:

[0022]

Embodiment 2

[0024] It is determined that the mass percent composition of the composite passivating agent for galvanized sheet, aluminum alloy and copper alloy metal plate is as follows:

[0025]

Embodiment 3

[0027] It is determined that the mass percent composition of the composite passivating agent for galvanized sheet, aluminum alloy and copper alloy metal plate is as follows:

[0028]

[0029]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a composite passivating agent for a galvanized plate, an aluminum alloy metal plate and a copper alloy metal plate, and belongs to the technical field of surface treatment of metal materials. The composite passivating agent is prepared from the following components in percentage by mass: 4 to 20% of fatty alcohol polyoxyethylene ether phosphate, 0.5 to 5% of 5-chloro-2-methyl-4-isothiazoline-3-one and 2-methyl-4-isothiazoline-3-one mixture, 0.5 to 5% of sodium dehydroacetate, 0.1 to 2% of sodium N-lauroyl sarcosinate, 0.01 to 0.5% of high-carbon alcohol fatty acid estercomplex, 0.1 to 2% of strontium bismuthate nanospheres, and the balance of water. The composite passivating agent has the advantages that the pretreatment is not required before use, and the composite passivating agent can be directly applied to a metal surface; after the galvanized plate, the aluminum alloy metal plate or the copper alloy metal plate is passivated by the composite passivating agent, the good salt resistance, weather resistance, water resistance, acid resistance, alkaline resistance, solvent resistance, fingerprint resistance and lubricating property are realized.

Description

technical field [0001] The invention belongs to the technical field of metal material surface treatment, and in particular relates to a composite passivator for galvanized sheets, aluminum alloys and copper alloy metal sheets. Background technique [0002] Zinc, aluminum and copper, as more active metals, are prone to corrosion in humid atmospheres and environments containing chloride ions, which will affect the surface quality of metals. In order to improve the surface quality and corrosion resistance of galvanized sheets, aluminum and copper alloy metal sheets, and prolong the service life of the metal sheets, passivation treatment is required to form a layer of passivation with high density and high stability on the metal surface film to increase the corrosion resistance of the metal plate surface. The hexavalent chromium in the traditionally used chromate passivation agent has carcinogenic effect and is harmful to human body and environment, so it is required to replace...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C22/68
CPCC23C22/68
Inventor 裴立宅吴胜华林飞飞
Owner ANHUI UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com