Titanium alloy compound material for dental department and preparation method thereof

A technology of dental materials and titanium alloys, applied in dental preparations, dentistry, dental prostheses, etc., can solve problems such as limited application, and achieve the effects of simple processing industry, enhanced mechanical properties, and improved plasticity

Inactive Publication Date: 2019-01-01
佛山市佛冠义齿有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The price and color of gold alloys limit its applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A titanium alloy composite dental material, the titanium alloy composite dental material includes the following chemical composition and weight percentage: Cu: 2%, Zr: 3%, Ce: 0.05%, Ag: 0.02% Graphene oxide fiber: 10 %, and the balance is Ti.

[0018] The preparation method of the above-mentioned titanium alloy composite dental material comprises the following steps:

[0019] (1) Grinding the alloy raw materials except graphene oxide to a nearly spherical powder with a particle size of 50-100 μm, and mixing them uniformly to obtain an alloy matrix powder;

[0020] (2) adding graphene oxide nanosheets to absolute ethanol for stirring and mixing, and then using an ultrasonic cell pulverizer to disperse for more than 30 minutes to prepare a graphene oxide solution;

[0021] (3) stirring and mixing the alloy matrix powder and the graphene oxide solution in an inert gas environment to obtain a mixed slurry;

[0022] (4) Drying the mixed slurry prepared in step (3) under a...

Embodiment 2

[0025] A titanium alloy composite dental material, the titanium alloy composite dental material includes the following chemical composition and weight percentage: Cu: 2.1%, Zr: 4.2%, Ce: 0.06%, Ag: 0.05%, graphene oxide: 12 %, and the balance is Ti.

[0026] The preparation method of the titanium alloy composite dental material described in this example is the same as that in Example 1.

Embodiment 3

[0028] A titanium alloy composite dental material, the titanium alloy composite dental material includes the following chemical composition and weight percentage: Cu: 3%, Zr: 5%, Ce: 0.1%, Ag: 0.1% Graphene oxide fiber: 15 %, and the balance is Ti.

[0029] The preparation method of the titanium alloy composite dental material described in this example is the same as that in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a titanium alloy compound material for dental department and a preparation method thereof. The titanium alloy compound material for the dental department is prepared from the following chemical components in percentage by weight: 2 to 3 percent of Cu, 3 to 5 percent of Zr, 0.05 to 0.1 percent of Ce, 0.02 to 0.1 percent of Ag, 10 to 15 percent of graphene oxide fibers and the balance of Ti. According to the titanium alloy compound material for the dental department, graphene oxide is added so that the mechanical property is greatly enhanced; compared with an alloy matrix, the composite material provided by the invention has the advantages that the plasticity is greatly improved when the room-temperature strength of the composite material is improved, and the corrosion resisting performance of the titanium alloy compound material for the dental department is ensured; an inert gas protected stirring method is used for preparing mixed slurry of the graphene oxide and alloy powder, the interface bonding property of the graphene oxide and the alloy powder is improved, and oxidization of the alloy powder is avoided, so that the molding property of subsequent powdersintering is improved; a processing technology of the preparation method is simple, and the preparation method is easy to popularize in a large scale.

Description

technical field [0001] The invention belongs to the technical field of medical materials, in particular to a titanium alloy composite dental material and a preparation method thereof. Background technique [0002] According to statistics, periodontal disease, dental caries, and irregular dentition are the three most common dental diseases in my country at present. The various sequelae of these three dental diseases, such as tooth loss, gingival swelling and pain, and tooth extraction, also plague people, accounting for 90% of them. of people suffer from varying degrees of gingivitis and periodontitis. In the past, due to the restriction of the level of economic development and the concept and awareness of oral hygiene, the understanding and cooperation of early treatment and preventive treatment among the Chinese lagged behind that of developed countries. In recent years, with the improvement of people's living standards and the enhancement of patients' awareness of treatmen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C47/14C22C47/02C22C49/11A61K6/04C22C101/00
CPCA61K6/84C22C47/02C22C47/14C22C49/11
Inventor 刘秀兰冼志行尹春
Owner 佛山市佛冠义齿有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com