Preparation method of plastic flexible pipe material with strong wear resistance

A technology of plastic hose and wear resistance, which is applied in the field of preparation of plastic hose materials, can solve the problems of polyethylene hose constraints, short boards of wear resistance, and inability to meet the needs of long-term use, and achieve strong practicability, The effect of excellent wear resistance and good application prospects

Inactive Publication Date: 2018-11-23
苏州环亚软管塑业有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, ordinary polyethylene hoses still have great shortcomings in wear resistance, and often cannot meet the needs of long-term use when used in some environments involving frequent wear and tear, which also gives polyethylene hoses further development. Development has brought no small constraints

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] (1) Mix 85% by weight of nitric acid solution and glacial acetic acid in a ratio of 1:25, and stir evenly. Add 55 parts of high-density polyethylene and 36 parts of polyvinyl butyral ester to 1000 parts of the above-prepared mixed solution. In a constant temperature water bath at 80°C, ultrasonically oscillate at a power of 150W for 80 minutes, add 10 times the weight of the system to dilute deionized water, keep it warm and stand still. After the solution is stratified, the supernatant is discarded and the precipitate is pumped. Filter cake is obtained after filtration;

[0024] (2) Add 6 parts of hydroxyethyl cellulose to 75wt% sulfuric acid solution, soak for 100 minutes, and mix with 15 parts of ethyl 3-ethoxypropionate and 12 parts of nanocarbon sol after washing with water. In a constant temperature water bath at ℃, ultrasonically oscillate at a power of 150W for 80 minutes, then add it to deionized water 15 times the weight of the mixture, stir evenly, and obtain an...

Embodiment 2

[0031] (1) Mix 85% by weight of nitric acid solution and glacial acetic acid in a ratio of 1:25, and stir evenly. Add 60 parts of high-density polyethylene and 38 parts of polyvinyl butyral to 1000 parts of the above-prepared mixed solution. In a constant temperature water bath at 80°C, ultrasonically oscillate at a power of 200W for 90 minutes, add 11 times the weight of the system to dilute with deionized water, keep it warm and stand still. After the solution is stratified, the supernatant is discarded and the precipitate is pumped. Filter cake is obtained after filtration;

[0032] (2) Add 7 parts of hydroxyethyl cellulose to 75wt% sulfuric acid solution, soak for 125 minutes, and mix with 20 parts of ethyl 3-ethoxypropionate and 15 parts of nanocarbon sol after washing with water. In a constant temperature water bath at ℃, ultrasonically oscillate at a power of 200W for 90 minutes, then add it to deionized water 18 times the weight of the mixture, stir it evenly, and obtain ...

Embodiment 3

[0039] (1) Mix 85% by weight of nitric acid solution and glacial acetic acid in a ratio of 1:25, and stir evenly. Add 65 parts of high-density polyethylene and 40 parts of polyvinyl butyral to 1000 parts of the above-prepared mixed solution. In a constant temperature water bath at 80°C, ultrasonically oscillate at a power of 250W for 100 minutes, add 12 times the weight of the system to dilute with deionized water, keep it warm and stand still. After the solution is stratified, the supernatant is discarded and the precipitate is pumped Filter cake is obtained after filtration;

[0040] (2) Add 8 parts of hydroxyethyl cellulose to 75wt% sulfuric acid solution, soak for 150 minutes, and mix with 25 parts of ethyl 3-ethoxypropionate and 18 parts of nanocarbon sol after washing with water. In a constant temperature water bath at ℃, ultrasonically oscillate at a power of 250W for 100 minutes, then add it to 20 times the weight of the mixture in deionized water, stir evenly, and obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a plastic flexible pipe material with strong wear resistance. The method comprises the steps: performing ultrasound and separation on high density polyethylene and polyvinyl butyral in mixed acid; treating hydroxyethyl cellulose by sulphuric acid and performing ultrasound and dilution on the treated hydroxyethyl cellulose with ethyl 3-ethoxypropionate and nano carbon sol; mixing magnesium hydroxide with calcium bisulfate and adding acrylic acid, methyl trichlorosilane and stannic maleate in batches; mixing products and dewatering and curing to obtain primary blank; modifying tris(nonyl phenyl) phosphate and polyglycerol ricinoleate to obtain a modified treatment mixture; finally, smelting the primary blank and the modified treatment mixture,stirring with perlite micropowder and dewatering, extruding and cooling to obtain a finished-product plastic flexible pipe material. The prepared plastic flexible pipe material with the strong wear resistance has excellent wear resistance and a good application prospect in the flexible pipe manufacturing industry.

Description

Technical field [0001] The invention relates to the technical field of hose manufacturing, in particular to a method for preparing a plastic hose material with strong wear resistance. Background technique [0002] Because plastic hoses have the advantages of corrosion resistance, non-leakage, anti-scaling, long service life, etc., market applications and application fields are growing rapidly. At present, the consumer market for plastic hoses at home and abroad is mainly divided into four application areas: daily consumption and health care, hydraulic transmission systems in industry, automobile manufacturing and maintenance, and water conservancy projects. As far as the varieties of plastic hoses are concerned, the polyethylene market is currently growing the fastest, and it is becoming the second largest variety of plastic hoses after polyvinyl chloride. The main reasons for the rapid growth of polyethylene plastic hoses are: polyethylene hoses have very good poly-softness, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L29/14C08L1/28C08L71/02C08K3/22C08K5/526C08K3/30C08K13/02
CPCC08K2003/2224C08L23/06C08L2203/18C08L2205/035C08L2207/062C08L29/14C08L1/284C08L71/02C08K3/22C08K5/526C08K3/30C08K13/02
Inventor 张新华
Owner 苏州环亚软管塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap