A kind of wheat straw fiber non-woven mask base cloth and wheat straw fiber mask

A non-woven, wheat straw technology, applied in the field of wheat straw fiber mask, can solve the problems of waste, slow degradation, unfriendly environment, etc.

Active Publication Date: 2021-07-06
巩义市欧洁源环保技术服务有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the non-woven mask base fabric made of organic synthetic fibers consumes a lot of petroleum resources in the production process, and the degradation rate in the environment is slow in the later stage; the raw materials of real silk and pure cotton fiber mask base fabrics are silk and cotton, The cost itself is high, and waste of resources is caused by disposables; craft silk, viscose fiber and tencel mask base fabrics are produced from natural fibers, and the raw materials are cotton, wood fiber, etc., and a large amount of organic solvents are used in the production process and chemicals, which are not environmentally friendly; the raw material of the biocellulose facial mask base cloth is bacterial cellulose fermented by Gluconacetobacter, the production process is complicated, difficult, and costly, and the popularization and use are limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of wheat straw fiber non-woven mask base cloth and wheat straw fiber mask

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The wheat straw fiber nonwoven mask base cloth of the present embodiment is prepared by the following method:

[0035] 1) Take dried wheat straw and cut it into small sections with a length of 40-60 mm, immerse it in water at room temperature, take it out after soaking for 12 hours, squeeze and dehydrate it with rolls, and dry naturally until the water content is 40%, to obtain wheat straw scraps;

[0036] 2) Place the wheat straw scraps obtained in step 1) in a steam explosion device, inject saturated water steam to carry out steam explosion, the steam temperature is 210°C, the explosion pressure is 3.5MPa, heat preservation and pressure holding for 5.0min, the pressure is released and the material is exploded fiber material;

[0037] 3) According to the solid-to-liquid mass ratio of 1:4, immerse the blasting fiber material obtained in step 2) in water at a temperature of 65°C for washing. The soaking time for heat preservation is 6 hours. After taking it out, squeeze ...

Embodiment 2

[0044] The wheat straw fiber nonwoven mask base cloth of the present embodiment is prepared by the following method:

[0045] 1) Take dried wheat straw and cut it into small sections with a length of 40-60 mm, immerse it in water at room temperature, take it out after soaking for 14 hours, squeeze and dehydrate it with rolls, and dry it naturally until the water content is 43%, to obtain wheat straw scrap;

[0046] 2) Place the wheat straw scraps obtained in step 1) in a steam explosion device, and inject saturated steam to carry out steam explosion. The steam temperature is 215°C, the explosion pressure is 3.3MPa, and the heat preservation and pressure are kept for 4.0min. fiber material;

[0047] 3) According to the solid-to-liquid mass ratio of 1:4.5, immerse the blasting fiber material obtained in step 2) in water with a temperature of 65° C. for washing. The soaking time for heat preservation is 5 hours. After taking it out, squeeze and dehydrate to obtain the washed fibe...

Embodiment 3

[0054] The wheat straw fiber nonwoven mask base cloth of the present embodiment is prepared by the following method:

[0055] 1) Take the dry wheat straw and cut it into small sections with a length of 40-60 mm, immerse it in water at room temperature, take it out after soaking for 16 hours, squeeze and dehydrate it with rolls, and dry it naturally until the water content is 45%, to obtain wheat straw scraps;

[0056] 2) Place the wheat straw scraps obtained in step 1) in a steam explosion device, inject saturated water steam to carry out steam explosion, the steam temperature is 220°C, the explosion pressure is 3.0MPa, heat preservation and pressure holding for 5.0min, and the pressure is released to discharge the material. fiber material;

[0057] 3) According to the solid-to-liquid mass ratio of 1:5, immerse the blasting fiber material obtained in step 2) in water at a temperature of 65° C. for washing, and keep the soaking time for 4 hours. After taking it out, squeeze and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to a wheat straw fiber non-woven facial mask base fabric and a wheat straw fiber facial mask. The facial mask base fabric is prepared by the following methods: 1) taking wheat straw and cutting it, soaking it in water, then taking out and extruding and dehydrating to obtain wheat straw scraps; 2) cutting the wheat straw into pieces The material is steam-exploded to obtain an explosive fiber material; 3) the obtained explosive fiber material is washed with water to obtain a water-washed fiber material; 4) the washed fiber material is combed into a net, spunlace reinforced and dried to obtain a non-woven base material; 5) in the non-woven The ethanol solution of α-bisabolol is evenly sprayed on the surface of the substrate, and the ethanol is dried to remove the ethanol to obtain the Shumin base material; 6) The Shumin base material is immersed in the aqueous solution of chitosan acetic acid, degassed under negative pressure, and the excess liquid is squeezed out after being taken out and dried. have to. The obtained mask base fabric has appropriate mechanical properties, good liquid holding capacity and air permeability, good biocompatibility and antibacterial properties, no adverse reaction to human skin during use, and good use effect; The degradation rate in the environment is fast, and it is environmentally friendly.

Description

technical field [0001] The invention belongs to the technical field of skin care products sticking mask, and in particular relates to a wheat straw fiber nonwoven mask base cloth, and also relates to a wheat straw fiber mask prepared by using the wheat straw fiber nonwoven mask base cloth. Background technique [0002] Among the daily skin care products, facial masks are favored by consumers because of their obvious effects and easy portability, and have become one of the fastest-growing market segments in my country's daily chemical industry. The rapid development of facial mask is closely related to its efficacy. Its mechanism of action mainly includes: 1. Mask blocks the contact between skin and air, inhibits water evaporation, increases skin temperature and expands pores, and promotes sweat gland secretion and metabolism; Moisture and nutrients can fully moisturize the stratum corneum of the skin, making it soft, increasing elasticity and vitality; the penetration of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04H1/425D04H1/492A61K8/02A61Q19/00
CPCA61K8/0212A61Q19/00D04H1/425D04H1/492
Inventor 李朝辉
Owner 巩义市欧洁源环保技术服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com