Polyacrylic ester polymer cement-based waterproof paint and preparation method thereof

A polyacrylate, waterproof coating technology, applied in the field of cement-based waterproof coatings, can solve the problems of long condensation and curing time of the coating film, reduced structural strength and peel strength, shortened curing time, etc. Compatibility, the effect of improving compatibility and structural stability

Active Publication Date: 2018-09-18
安徽朗凯奇科技股份有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polyacrylate polymer cement-based waterproof coating is a two-component waterproof coating composed of liquid material and powder material. The liquid material is composed of polyacrylate emulsion and various additives. The powder material is composed of cement and fine sand. It has excellent water resistance, durability and stability. However, in actual construction, due to the poor compatibility between the polymer liquid material and the cement-based powder, the structural strength and peel strength of the composite cement-based waterproof coating Reduced, easy to separate from the base layer, and the coating film condenses and cures for a long time
[0003] The patent application number is CN201510028456.3, which discloses a polymer cement-based waterproof coating. The waterproof coating is obtained by mixing a liquid material composed of acrylic emulsion and other additives and a powder composed of inorganic ores such as cement and quartz powder, which shortens the The curing time improves the bonding strength of the coating to a certain extent, but it does not essentially solve the compatibility problem between materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyacrylic ester polymer cement-based waterproof paint and preparation method thereof
  • Polyacrylic ester polymer cement-based waterproof paint and preparation method thereof
  • Polyacrylic ester polymer cement-based waterproof paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] Below in conjunction with embodiment, the present invention is described in further detail, so that those skilled in the art can implement according to referring to description text.

[0014] The present invention proposes the polyacrylate polymer cement-based waterproof coating of an embodiment, comprising following components by weight:

[0015]

[0016] The present invention uses tricalcium silicate cement as the gelling base material, which can absorb the moisture in the polyacrylate emulsion, and rapidly hydrates into calcium silicate gel at room temperature. Compared with dicalcium silicate cement, the hydration reaction is faster Strong, saves the drying and solidification time of waterproof coatings, and although the curing strength is high, its hydration reaction equation is as follows: 3CaO·SiO 2 +nH O =xCaO·SiO 2 ·yH 2 O+(3-x)Ca(OH) 2 , x represents the ratio of calcium to silicon, n represents the amount of bound water, and y represents the number of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses polyacrylic ester polymer cement-based waterproof paint and a preparation method thereof. The paint is prepared from the following ingredients in parts by weight: 100 parts oftricalcium silicate cement, 40 to 60 parts of tetra-calcium aluminoferrite cement, 70 to 110 parts of polyacrylic ester emulsion, 60 to 80 parts of quartz sand, 5 to 15 parts of polysiloxane, 1 to 5 parts of silane coupling agents, 10 to 20 parts of silicon nitride and 10 to 16 parts of magnesium oxalate. The preparation method comprises the following steps of mixing the tricalcium silicate cement, the tetra-calcium aluminoferrite cement, the quartz sand, the silicon nitride and the silicon carbide; dispersing the mixture into the polyacrylic ester emulsion; heating the materials to 85 DEG C;then, adding the polysiloxane and silane coupling agents; performing stirring reaction; when the quantity of Si-C, Si-O-C, Si-C-N and Si-O-Si in the reaction system is unchanged, and after the cooling, adding the magnesium oxalate; performing homogeneous treatment. The produced polyacrylic ester polymer cement-based waterproof paint can be fast cured and coagulated; the space structure is compact;excellent mechanical property and waterproof and acid-alkali resistant performance are realized.

Description

technical field [0001] The invention relates to a cement-based waterproof coating, in particular to a polyacrylate polymer cement-based waterproof coating and a preparation method thereof. Background technique [0002] Polyacrylate polymer cement-based waterproof coating is a two-component waterproof coating composed of liquid material and powder material. The liquid material is composed of polyacrylate emulsion and various additives. The powder material is composed of cement and fine sand. It has excellent water resistance, durability and stability. However, in actual construction, due to the poor compatibility between the polymer liquid material and the cement-based powder, the structural strength and peel strength of the composite cement-based waterproof coating Reduced, easy to separate from the base layer, and the coating film condenses and cures for a long time. [0003] The patent application number is CN201510028456.3, which discloses a polymer cement-based waterpro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B111/27C04B111/20
CPCC04B28/06C04B2111/20C04B2111/27C04B7/02C04B24/2641C04B14/06C04B24/42C04B24/06C04B14/328
Inventor 乔启信
Owner 安徽朗凯奇科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com