Preparation method of woven carpet without gumming process

Abstract

The invention discloses a preparation method of a woven carpet without a gumming process. A second coating layer is a hot-melt fiber filament or a staple fibre yarn, a first coating layer is a polypropylene fiber filament or a staple fibre yarn, the second coating layer accounts for 20%- 50% of the total mass of a composite yarn, the first coating layer accounts for 10%-15% of the total mass of the composite yarn, the balance is a core yarn, and a pile weft yarn is obtained by adopting the manner. When the non-adhesive carpet is produced by using a hot-melt ethylene-vinyl acetate copolymer fiber as a bonding material in combination with the pile yarn made of a polyester fiber, the melting occurs when the hot-melt ethylene-vinyl acetate copolymer fiber is heated to be higher than the melting point in a hot pressing process, the conformation of a fiber macromolecular chain is changed, the whole macromolecular chain slips through the transition of chain segments, viscous flow occurs, thepile and weft yarns as well as the weft yarns and warp yarns are effectively solidified after curing, and the pull strength of the pile and the shape retention and dimensional stability of the carpetare enhanced, so that the gumming process in the carpet preparation process is omitted, and the produced carpet is more environmentally friendly.

Description

technical field [0001] The invention relates to the field of household articles, in particular to a method for preparing a woven carpet without a back glue process. Background technique [0002] With the improvement of modern living standards, the requirements for the comfort, fashion and environmental protection of some public places and home decoration are also getting higher and higher. The utilization rate of carpets in some public places and home decoration accounts for a large part. Carpets have the function of heat preservation and regulation. Large-area carpets can reduce the heat lost through the ground in the room, block the invasion of cold air on the ground, and make people feel warm and comfortable. At the same time, it has a sound-absorbing function. The rich texture of the carpet and the surface of the plush tufts have a good sound-absorbing effect, and can properly reduce the impact of noise. Since the carpet is a fabric rich in elastic fibers, it has a plum...

AI Technical Summary

Problems solved by technology

Woven Wilton carpets are made by interweaving warp yarns, weft yarns, and pile yarns, and are finished by subsequent processes such as gluing, shearing, etc., so that the warp yarns, weft yarns, and pile yarns are mechanically bonded. It is also made by interweaving warp yarn, weft yarn and pile yarn, and then finishing through gluing, shearing and other processes. In the gluing process, organic solvents are needed to dissolve and dilute the glue. Therefore, in the gluing process, there are the following problems: ⑴ During the gluing process, volatile harmful gases pollute the environment and affect the health of workers; (2) The gluing and drying and curing process is long and takes a long time, which limits the production speed, the equipment occupies a large space, the amount of glue used is large, and the energy consumption is high. The production cost of the carpet is lowered; (3) the traditional carpet adopts the method of applying glue on the back of the embryo carpet, and the glue needs to be infiltrated into the pile yarn through the embryo carpet base cloth. This leads to problems such as insufficient pull-out strength, poor dimensional stability, and easy deformation of the pile yarn

At the same time, in order to reduce the cost and improve the stiffness of the carpet, the adhesive layer and calcium carbonate are generally mixed together during the gluing process. The problem brought by this method is that it is not easy to reuse, and when the waste is burned, the waste Contains flame retardant fillers

Images