A simple preparation method of nanoscale tungsten copper precursor powder

A precursor powder, nano-level technology, applied in the direction of nanotechnology, can solve the problems of high energy consumption and long production cycle, and achieve the effects of reduced energy consumption, shortened production cycle, and simple preparation method

Active Publication Date: 2021-05-28
HENAN UNIV OF SCI & TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problems of long production cycle and high energy consumption in the existing hydrothermal method for preparing powder, and to propose a simple preparation method for nano-scale tungsten-copper precursor powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A simple preparation method of nanoscale tungsten copper precursor powder
  • A simple preparation method of nanoscale tungsten copper precursor powder
  • A simple preparation method of nanoscale tungsten copper precursor powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A simple preparation method of nano-scale tungsten-copper precursor powder adopts the following production steps:

[0028] Step 1. According to the mass percentage of W in the target composite powder is 50-60%, and the mass percentage of Cu is 40-50%, weigh sodium tungstate dihydrate and copper nitrate trihydrate, and prepare them respectively to a concentration of 0.8 mol / L solution;

[0029] Step 2, adding excessive ammoniacal liquor to the obtained copper nitrate trihydrate solution, and making it fully mixed at 30°C, so that sufficient copper complex ions are produced in the solution, and the ammoniacal liquor can be added in excess of 3-5%;

[0030] Step 3: Drop sodium tungstate solution into the solution obtained in Step 2 at a rate of 1~3 drops / s, then add ammonia water or nitric acid to adjust the pH value of the mixed solution to 4.0~6.2, and mix it in a magnetic stirrer at 60r / min speed fully stirred for 5h;

[0031] Step 4. Put the mixed solution obtained ...

Embodiment 2

[0035] A simple preparation method of nano-scale tungsten-copper precursor powder adopts the following production steps:

[0036] Step 1. According to the mass percentage of W in the target composite powder is 60-70%, and the mass percentage of Cu is 30-40%, weigh sodium tungstate dihydrate and copper nitrate trihydrate, and prepare them respectively to a concentration of 0.6 mol / L solution;

[0037] Step 2, adding excessive ammoniacal liquor to the obtained copper nitrate trihydrate solution, and making it fully mixed at 30°C, so that sufficient copper complex ions are produced in the solution, and the ammoniacal liquor is added in excess of 5-8%;

[0038] Step 3: Drop sodium tungstate solution into the solution obtained in Step 2 at a rate of 3~5 drops / s, then add ammonia water or nitric acid to adjust the pH value of the mixed solution to 4.0~6.2, and mix it in a magnetic stirrer at 60r / min speed fully stirred for 4h;

[0039] Step 4. Put the mixed solution obtained in S...

Embodiment 3

[0043] A simple preparation method of nano-scale tungsten-copper precursor powder adopts the following production steps:

[0044] Step 1. According to the mass percentage of W in the target composite powder is 70-80%, and the mass percentage of Cu is 20-30%, weigh sodium tungstate dihydrate and copper nitrate trihydrate, and prepare them respectively to a concentration of 0.4 mol / L solution;

[0045] Step 2, adding excessive ammoniacal liquor to the obtained copper nitrate trihydrate solution, and making it fully mixed at 30°C, so that sufficient copper complex ions are produced in the solution, and the ammoniacal liquor is excessively 8 to 10% when added;

[0046] Step 3: Drop sodium tungstate solution into the solution obtained in Step 2 at a rate of 5-8 drops / s, then add ammonia water or nitric acid to adjust the pH value of the mixed solution to 4.0-6.2, and mix it in a magnetic stirrer at 60r / min speed fully stirred for 3h;

[0047] Step 4. Put the mixed solution obtai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A simple preparation method of nano-scale tungsten-copper precursor powder, the corresponding solution is prepared by using sodium tungstate dihydrate and copper nitrate trihydrate as raw materials, and then the sodium tungstate solution is dropped into the containing The pH value of the mixed solution is adjusted by using ammonia water or nitric acid in the copper nitrate solution of copper complex ions, and then the mixed solution is directly placed in a vacuum drying oven to undergo a thermochemical reaction, thereby preparing a nano-scale tungsten-copper precursor powder. The method of the present invention can prepare tungsten-copper precursor powder with uniform mixing, fine particles and high purity. Compared with the hydrothermal method, the present invention is characterized by short production cycle, no need of reaction kettle, and reduced preparation cost.

Description

technical field [0001] The invention relates to the field of powder preparation in powder metallurgy technology, in particular to a simple preparation method of nano-scale tungsten-copper precursor powder. Background technique [0002] The preparation of tungsten-copper composite materials by powder metallurgy is developing and optimized in the direction of high density and high performance, and the quality of powder metallurgy products has a great relationship with the performance of powder. Therefore, the preparation of dense tungsten-copper composite materials puts forward higher technical requirements for the synthesis preparation and molding process of its powder. Due to the poor solubility of tungsten and copper, it is not easy to obtain a completely dense tungsten-copper composite material. And the research results show that the higher the tungsten content, the more the densification process of the material depends on the particle size of the powder. Therefore, the u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F9/22B82Y40/00
CPCB22F9/22B82Y40/00
Inventor 马窦琴谢敬佩陈艳芳苌清华王爱琴王文焱宋亚虎
Owner HENAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com