Transparent conductive film and preparation method thereof

A technology of transparent conductive film and conductive polymer, which can be used in equipment for manufacturing conductive/semiconductive layer, cable/conductor manufacturing, conductive layer on insulating carrier, etc. It can solve problems such as inability to use and achieve low haze. , easy to operate, good electrical conductivity effect

Inactive Publication Date: 2018-06-29
常州市丰瑞电子有限公司
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem to be solved by the present invention is to provide a transparent conductive film and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0028] Take 25g of sodium polystyrene sulfonate, add 200mL of deionized water, stir at 300r / min for 20min, then add 10g of 3,4-ethylenedioxythiophene, 0.1g of sodium persulfate, 0.1g of ferric sulfate, and continue stirring for 15h After the reaction, add anion exchange resin to react for 1h, filter to obtain filtrate, add cation exchange resin to the filtrate to react for 1h, filter to obtain ion exchange liquid, add water to dilute the ion exchange liquid to a solid content of 1.0%, and obtain poly(3,4 - Ethylenedioxythiophene) - polystyrene sulfonic acid aqueous solution, take 12g copper chloride, 8.75g polyvinylpyrrolidone, add 1.5L deionized water, stir and mix at 300r / min for 10min, then add 15g oleic acid, 1.5g Oleylamine, disperse with 200W ultrasonic wave for 15min, then heat to 50°C, add 15g of glucose, stir for 8h, then transfer to a hydrothermal reaction kettle, react for 1h at 120°C, cool to room temperature, put it in a centrifuge and centrifuge Separate for 10 m...

example 2

[0030]Take 28g of sodium polystyrene sulfonate, add 250mL of deionized water, stir at 350r / min for 25min, then add 15g of 3,4-ethylenedioxythiophene, 0.1g of sodium persulfate, 0.1g of ferric sulfate, and continue stirring for 18h After the reaction, add anion exchange resin to react for 1h, filter to obtain filtrate, add cation exchange resin to the filtrate to react for 1h, filter to obtain ion exchange liquid, add water to dilute the ion exchange liquid to a solid content of 1.1%, and obtain poly(3,4 - Ethylenedioxythiophene) - polystyrene sulfonic acid aqueous solution, take 18g copper chloride, 12.75g polyvinylpyrrolidone, add 2.3L deionized water, stir and mix at 350r / min for 12min, then add 18g oleic acid, 1.8g Oleylamine, disperse with 250W ultrasonic wave for 18min, then heat to 55°C, add 20g of glucose, stir for 9h, then transfer to a hydrothermal reaction kettle, react for 2h at 130°C, cool to room temperature, put it in a centrifuge and centrifuge Separate for 12 m...

example 3

[0032] Take 50g of sodium polystyrene sulfonate, add 300mL of deionized water, stir at 400r / min for 30min, then add 20g of 3,4-ethylenedioxythiophene, 0.2g of sodium persulfate, 0.2g of ferric sulfate, and continue stirring for 20h After the reaction, add anion exchange resin to react for 2h, filter to obtain filtrate, add cation exchange resin to the filtrate to react for 2h, filter to obtain ion exchange liquid, add water to dilute the ion exchange liquid to a solid content of 1.2%, and obtain poly(3,4 -Ethylenedioxythiophene)-Polystyrene sulfonic acid aqueous solution, take 24g copper chloride, 17.50g polyvinylpyrrolidone, add 3.0L deionized water, stir and mix at 400r / min for 15min, then add 30g oleic acid, 3.0g Oleylamine was dispersed by 300W ultrasonic wave for 20min, then heated to 60°C, added 30g of glucose, stirred for 10h, then transferred to a hydrothermal reaction kettle, reacted for 3h at 150°C, cooled to room temperature and placed in a centrifuge for centrifugat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a transparent conductive film and a preparation method thereof, and belongs to the technical field of preparation of conductive films. With copper chloride as a copper source,oleic acid and oleylamine as inducers, glucose as a reducing agent and polyvinylpyrrolidone as a stabilizer, copper nanowires with high length-diameter ratio, uniform diameter, good dispersibility and regular morphology are prepared; through formation of a network with smaller linear density, a longer penetration path is provided, internal copper wire nodes are reduced, the resistivity is reduced, and a transparent metal film with low haze, high transparency, high conductivity and excellent mechanical flexibility and strength is achieved; then the copper nanowires are covered with an aqueouspoly(3,4-ethylenedioxythiophene)-polystyrene sulfonic acid solution to prepare a composite film to improve the oxidation resistance of the copper nanowires, so that the energy absorbing ability of themetal film layer during folding deformation is enhanced, the slippage degree of conductive particles is reduced, and thus the resistance change rate of a coating layer is reduced and the flexibilityand the electrical stability of a product are further improved.

Description

technical field [0001] The invention relates to a transparent conductive film and a preparation method thereof, belonging to the technical field of conductive film preparation. Background technique [0002] In nature, conductors are often opaque and poorly flexible, such as metal materials and graphite; while transparent materials are often non-conductive, such as glass and crystal. The emergence of transparent conductive film has broken people's traditional concept. It is a functional film with both light transmission and conductivity. [0003] As an important optoelectronic material, transparent conductive film has high light transmittance in the visible light region and high reflectivity in the infrared band. Due to these excellent photoelectric properties, transparent conductive films have been widely used in light-emitting diodes, light-emitting transistors, solar cells, touch screens and other fields. [0004] Transparent conductive films can be divided into oxide-ba...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B5/14H01B13/00
CPCH01B5/14H01B13/0026
Inventor 孟浩影王文新韩昏晓
Owner 常州市丰瑞电子有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products