Porcelain composition and manufacture process thereof

A formula and porcelain technology, applied in clay products, other household utensils, applications, etc., can solve the problems of insufficient heat resistance and antibacterial properties of porcelain, achieve excellent biodegradability, excellent antibacterial performance, and ensure safety.

Inactive Publication Date: 2018-06-12
长沙善道新材料科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a formula of porcelain and its manufacturing process to solve the problem of insufficient heat resistance and antibacterial properties of porcelain disclosed in the Chinese patent application document "Formulation and Preparation of Porcelain (Application Publication No.: CN105060856A)"

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porcelain composition and manufacture process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024]A kind of formula of porcelain, take weight part as unit, comprise following raw material: 16.8 parts of polyurethane acrylates, 8.4 parts of vinyl acetate resins, 42.6 parts of Longyan soil, 13.8 parts of bovine bone charcoal, 5.7 parts of Mingling mud, 4.2 parts of talc, sea 6.3 parts of foam stone, 8.4 parts of Enzhou strange stone powder, 7.4 parts of calcined kaolin, 5.6 parts of nano-titanium dioxide, 3.6 parts of aluminum borate, 4.7 parts of aluminum metaphosphate, 4.3 parts of tungsten oxide, 2.8 parts of zirconia, 4.9 parts of lead carbonate, hydroxyethyl 6.7 parts of base cellulose, 5.4 parts of mica, 7.8 parts of quartz sand, 4.2 parts of clay, 5.1 parts of feldspar, 4.6 parts of calcite, 3.1 parts of coke gem, 2.7 parts of rock wool, 6.8 parts of back green, 19.4 parts of polycarbonate, polycarbonate 11.2 parts of lactic acid, 5.8 parts of silane coupling agent KH-560, 4.3 parts of attapulgite, 6.4 parts of polyvinylpyrrolidone, and 7.1 parts of chitosan.

...

Embodiment 2

[0030] A kind of formula of porcelain, in weight part, comprises following raw material: 10 parts of polyurethane acrylates, 15 parts of vinyl chloride resins, 30 parts of Longyan soil, 20 parts of bovine bone charcoal, 4 parts of Mingling mud, 6 parts of talc, sea 4 parts of foam stone, 15 parts of Enzhou strange stone powder, 4 parts of calcined kaolin, 6 parts of nano-titanium dioxide, 1 part of aluminum borate, 6 parts of aluminum metaphosphate, 2 parts of tungsten oxide, 3 parts of zirconia, 3 parts of lead carbonate, hydroxyethyl 8 parts of base cellulose, 3 parts of mica, 8 parts of quartz sand, 2 parts of clay, 6 parts of feldspar, 3 parts of calcite, 5 parts of coke gem, 1 part of rock wool, 8 parts of back green, 12 parts of polycarbonate, polycarbonate 12 parts of lactic acid, 4 parts of silane coupling agent KH-5604, 5 parts of attapulgite, 5 parts of polyvinylpyrrolidone, and 8 parts of chitosan.

[0031] The manufacture craft of the formula of described porcelain...

Embodiment 3

[0036] A kind of formula of porcelain, with weight part as unit, comprises following raw material: 20 parts of polyurethane acrylates, 5 parts of vinyl acetate resins, 50 parts of Longyan soil, 10 parts of bovine bone charcoal, 8 parts of Mingling mud, 3 parts of talc, seawater 9 parts of foam stone, 5 parts of Enzhou strange stone powder, 8 parts of calcined kaolin, 2 parts of nano-titanium dioxide, 5 parts of aluminum borate, 4 parts of aluminum metaphosphate, 5 parts of tungsten oxide, 1 part of zirconia, 6 parts of lead carbonate, hydroxyethyl 2 parts of base cellulose, 9 parts of mica, 4 parts of quartz sand, 6 parts of clay, 4 parts of feldspar, 5 parts of calcite, 2 parts of burnt gemstone, 4 parts of rock wool, 5 parts of back blue, 24 parts of polycarbonate, polycarbonate 6 parts of lactic acid, 9 parts of silane coupling agent KH-5609, 3 parts of attapulgite, 9 parts of polyvinylpyrrolidone, and 4 parts of chitosan.

[0037] The manufacture craft of the formula of de...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a porcelain composition and a manufacture process thereof. The porcelain composition comprises urethane acrylate, chlorine-vinegar resin, Longyan clay, bovine bone carbon, Mingling clay, talc, sepiolite, powder of Enzhou rare stone, calcined kaolin, nano titanium dioxide, aluminum borate, aluminum metaphosphate, tungsten oxide, zirconium oxide, lead carbonate, hydroxyethylcellulose, mica, quartz sand, clay, feldspar, calcite, Jiaobao stone, rock wool, Hui Qing (pigment), polycarbonate, polylactic acid, silane coupling agent KH-560, attapulgite, polyvinylpyrrolidone andchitosan. The porcelain composition is produced by preparing a base material, preparing a modified material, mixing the main material with the modified material, fettling, drying, biscuiting at low temperature, grinding, glazing, adding Hui Qing, heating and sintering. The porcelain composition has excellent heat resistance and antibacterial property.

Description

【Technical field】 [0001] The invention belongs to the technical field of ceramic preparation, and in particular relates to a formula of porcelain and a manufacturing process thereof. 【Background technique】 [0002] my country has a long history of ceramics. For more than 10,000 years, human beings have created primitive pottery with water, earth, and fire in their settled lives. During the Tang and Song Dynasties, the ceramic industry developed unprecedentedly. Famous porcelain; Jun porcelain glaze is unique in the porcelain forest due to the magical kiln transformation produced by the reduction of copper oxide coloring; 30 years after the reform and opening up, the development of Jun porcelain art is unprecedentedly prosperous; Guoli Jun porcelain has become a business card in China and is famous worldwide. Its profound historical and cultural heritage and magnificent and rich kiln transformation charm are respected as diluted treasures that "even if you have a lot of wealth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/36C04B33/13C04B33/34C04B33/32
CPCC04B33/1305C04B33/131C04B33/1315C04B33/32C04B33/34C04B33/36C04B2235/3208C04B2235/3232C04B2235/3244C04B2235/3258C04B2235/3296C04B2235/3409C04B2235/3418C04B2235/3445C04B2235/3463C04B2235/447C04B2235/6586C04B2235/661C04B2235/96C04B2235/9607
Inventor 不公告发明人
Owner 长沙善道新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com