NBR-PVC (nitrile butadiene rubber-polyvinyl chloride) blended rubber-plastic alloy material, preparation method and application

A rubber-plastic alloy and blending technology, which is applied in the field of NBR-PVC blended rubber-plastic alloy materials and its preparation and application, can solve the problems of difficult small-batch multi-variety production, large equipment investment, and high overall cost.

Inactive Publication Date: 2018-06-08
JIANGSU LUOSHI DAMPING MEMBER CO LTD
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved in the present invention is to overcome the high overall cost of preparing NBR-PVC rubber-plastic alloy materials by the emulsion co-precipitation method in the prior art, the preparation process is complicated, the equipment investment is large, it is not easy to produce in rubber products factories, and it is not easy to produce in small batches. The defect of multi-variety production provides a kind of NBR-PVC blended rubber-plastic alloy material and its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • NBR-PVC (nitrile butadiene rubber-polyvinyl chloride) blended rubber-plastic alloy material, preparation method and application
  • NBR-PVC (nitrile butadiene rubber-polyvinyl chloride) blended rubber-plastic alloy material, preparation method and application
  • NBR-PVC (nitrile butadiene rubber-polyvinyl chloride) blended rubber-plastic alloy material, preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～5、 comparative example 1～2

[0087] Table 1

[0088]

[0089]

[0090] "-" in Table 1 indicates that the dosage is "0".

Embodiment 1～5

[0092] Embodiments 1 to 5, the raw material components of each embodiment in Table 1 are obtained according to the following preparation steps to obtain the product of each embodiment (the parameters of each step are as shown in Table 2):

[0093] (1) In a banbury mixer, nitrile rubber A and nitrile rubber B rubber are mixed to obtain mixture A;

[0094] (2) Mix mixture A, activator zinc oxide, magnesium oxide, stearic acid, calcium stearate, barium stearate, polyethylene glycol, 2,2,4-trimethyl- Mixing 1,2-dihydroquinoline polymer, microcrystalline wax and paraffin wax to obtain mixture B;

[0095] (3) In an internal mixer, mix mixture B and 1 / 2 of the amount of carbon black to obtain mixture C;

[0096] (4) In the internal mixer, mix mixture C, 1 / 2 of the amount of carbon black, polyvinyl chloride paste resin, plasticizer, carry out glue removal in the internal mixer, and discharge the sheet in the open mixer ( Carry out in open mill, wheelbase 3mm), get rubber premixed gl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an NBR-PVC (nitrile butadiene rubber-polyvinyl chloride) blended rubber-plastic alloy material, a preparation method and an application. The NBR-PVC blended rubber-plastic alloy material is prepared from raw materials in parts by weight as follows: 75-80 parts of NBR, 20-25 parts of PVC paste resin, 4-10 parts of an activator A, 0.5-2.5 parts of an activator B, 1-5 parts ofa heat stabilizer, 1-3 parts of an anti-ageing agent RD, 3-6.5 parts of protective wax, 85-105 parts of carbon black, 30-40 parts of a plasticizer, 0.3-0.8 parts of a vulcanizing agent A, 0.5-1.2 parts of a vulcanizing agent B, 0.9-1.5 parts of an accelerator A and 1.5-2.5 parts of an accelerator B. The preparation method is simple, lower in cost and suitable for industrial production; the obtained product has excellent comprehensive performance and wide working temperature range, is resistant to fuel, lubricating oil and ozone and good in mixing dispersity and can be widely applied to materials of gas inlet hoses of engines.

Description

technical field [0001] The invention specifically relates to an NBR-PVC blended rubber-plastic alloy material, a preparation method and an application thereof. Background technique [0002] The car engine intake hose is connected between the air filter and the intake manifold. Its material performance indicators generally include high and low temperature resistance (-40~100°C), fuel resistance (such as gasoline, diesel, biofuel), lubricating oil resistance (such as engine oil, gear oil) and ozone resistance. At present, although the existing hydrogenated nitrile rubber mixtures and special brands of low-temperature-resistant ternary fluorine rubber can all meet the index requirements of automobile engine intake pipe materials, the price is very high. For example, the market price of hydrogenated nitrile rubber raw rubber is about 200 yuan / kg, and the market price of low-temperature ternary fluorine rubber is about 230 yuan / kg, so the two are rarely used in middle and low-en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L27/06C08L91/06C08L71/02C08K13/02C08K3/04C08K3/06C08K5/09C08K5/12C08K3/22
CPCC08L9/02C08K2201/014C08L2203/18C08L2205/025C08L2205/035C08L27/06C08L91/06C08L71/02C08K13/02C08K3/04C08K3/06C08K5/09C08K5/12C08K2003/2296C08K2003/222
Inventor 黄开军
Owner JIANGSU LUOSHI DAMPING MEMBER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com