Medical titanium alloy bone implant and preparation method thereof

A technology of bone implants and titanium alloys, which is applied in the field of medical titanium alloy bone implants and its preparation, can solve the problems of high elastic modulus of titanium alloys, achieve good mechanical properties, wear resistance, and good biocompatibility , the effect of low corrosion rate

Inactive Publication Date: 2018-06-01
贾红琴
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a medical titanium alloy with an elastic modulus matching that of human bone, high mechanical properties, low corrosion rate and good biocompatibility for the defect that the elastic modulus of the existing titanium alloy is too high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medical titanium alloy bone implant and preparation method thereof
  • Medical titanium alloy bone implant and preparation method thereof
  • Medical titanium alloy bone implant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] According to the alloy composition shown in Table 1, the material is selected, and the specific composition is shown in the brackets in Table 1.

[0021] Table 1 Titanium alloy test alloy design composition table (wt%)

[0022]

[0023] The specific preparation process of medical titanium alloy materials is as follows:

[0024] (1) Prepare ingredients: according to the formula amount in Table 1, after mixing each metal powder, mix it in a ball mill for 10h at a rotating speed of 400;

[0025] (2) Raw material melting and casting: The mixed raw materials are smelted in a high-vacuum arc heating furnace, which is first raised to 950°C at a heating rate of 70°C / min, kept for 1.2 hours, and then increased by 1500 at a heating rate of 20°C / min. ℃, fully stirred, then kept for 7 hours, finally poured into an ingot and cooled naturally.

[0026] (3) Homogenization treatment: The obtained ingot is subjected to solution treatment at 800°C, holding time for 10h, and then nat...

Embodiment 2

[0034] Example 1 investigated the changes in material properties under the same preparation parameters, when the component contents were different, the present invention not only changed the material components, but also the preparation process was different from the prior art. At the same time, the properties of the obtained material were changed. Specifically, the preparation parameters of No. 3 in Example 1 were unchanged, and the steps 1, 2, 3, 4, 5, and 6 in the preparation process of Example 1 were changed, as shown in Table 3. The properties of the tested materials are shown in Table 3.

[0035] Table 3 Titanium alloy material properties under different preparation steps

[0036]

[0037]

[0038] It can be seen from the performance comparison of No. 3 in Table 3 and Table 2 that to obtain a human implant material with excellent performance based on the material composition of the present invention, the preparation steps of Example 1 of the present invention are i...

Embodiment 3

[0040] Also with the formula of 3 in Example 1 Table 1 as a comparison, the preparation steps are unchanged, and the parameters in each step are changed, as shown below:

[0041] (1) Change the parameters and process in step (2) of Example 1, respectively 1. Without preheating, directly increase the temperature to 1500°C at a heating rate of 20°C / min; 2. After preheating, increase the temperature to 20°C / min The heating rate was increased to 1350 °C; 3. After preheating, the heating rate was increased to 1700 °C at a heating rate of 20 °C / min. The remaining steps are consistent with those disclosed in Example 1, and the mechanical properties of the final material are tested, and the results are as follows:

[0042] The material obtained under the condition of 1 has a tensile strength of 598MPa, an elastic modulus of 37.8GPa, a yield strength of 476MPa, an elongation of 12.5%, a hardness of 357HV, and a corrosion rate of 1.86mg / cm 2 a;

[0043] The tensile strength of the mater...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Elastic modulusaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Elastic modulusaaaaaaaaaa
Login to View More

Abstract

The invention discloses a medical titanium alloy bone implant and a preparation method thereof. A medical titanium alloy is composed of following components: 4.0 wt%-6.5 wt% of Zr, 3 wt%-10 wt% of Nb,0.5 wt%-1.5 wt% of Gd, 6 wt%-13 wt% of Fe, 0.8 wt%-2.0 wt% of Mo, 0.03 wt%-0.12 wt% of Pt and the balance Ti in a smelting manner. The elasticity modulus of the obtained medical titanium alloy bone implant is 29.8 GPa-41.3 GPa. The stress shielding defect occurring during implanting is avoided, meanwhile, relatively high mechanical strength and abrasion resisting performance are achieved, an extremely-low corrosion rate and good biocompatibility are achieved, and the medical titanium alloy bone implant can serve as a medical material to be used and popularized.

Description

technical field [0001] The invention belongs to the field of new metal materials, in particular to a biological material, in particular to a medical titanium alloy bone implant and a preparation method thereof. Background technique [0002] Biomedical materials refer to a class of materials that have special properties, special functions, and are used in artificial organs, surgical repair and other medical fields without adverse effects on human tissues, mainly including biomedical metal materials, biomedical polymer materials, and bioceramics. Materials and Biomedical Composites and Biomedical Derived Materials. [0003] Metal materials were used earlier and are still widely used to repair bones, joints, teeth, etc. Stainless steel was first used in clinical medicine, and later Co-Cr alloys appeared, but the above alloys are more prone to corrosion in the human environment and dissolve Ni , Cr, Co and other elements have toxic and side effects on the human body. In additio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C14/00C22C1/02C22F1/18
CPCC22C14/00C22C1/02C22F1/183
Inventor 贾红琴其他发明人请求不公开姓名
Owner 贾红琴
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com