Binder composition, and method for binding fibrous material by using same

A fiber material and composition technology, applied in the directions of lignin adhesives, adhesive types, non-polymer adhesive additives, etc., can solve problems such as low stiffness, improve mechanical properties, improve utilization, improve The effect of reliability and durability

Active Publication Date: 2018-01-23
KCC CORP CO LTD
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, a problem with the techniques disclosed in the above documents is that they achieve only lower stiffness compared to conventional phenolic resins

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Binder composition, and method for binding fibrous material by using same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] 450 kg of fresh water was added to the vessel used to prepare the adhesive and the pH was adjusted to a range of 8 to 14 using ammonia. Then, 0.1 kg of γ-aminopropyltriethoxysilane (silane A-1100, obtained from DOW CHEMICAL), 1.5 kg of lignin (Borrespers AM320, MW=20,000 to 50,000, obtained from Borregaard) and as a coupling agent 2 kg of glutaraldehyde (50 wt% glutaraldehyde in water from Sigma-Aldrich) was added to the vessel, and the mixture was stirred for about 10 minutes. Next, 22 kg of D-glucose monohydrate (solid content: 91% by weight) and 20 kg of lysine (solid content: 98% by weight) were added to the container, and the resulting mixture was stirred for 30 minutes until dissolution was confirmed. Then, further 0.4kg organosilicon type hydrophobic agent (SI1460Z, obtained from KCC company) and 1kg dustproof oil ( 217 / S from Govi) was added to the vessel and the resulting mixture was stirred for about ten minutes to prepare the adhesive.

Embodiment 2

[0040] 450 kg of fresh water was added to the vessel used to prepare the adhesive and the pH was adjusted to a range of 8 to 14 using ammonia. Then, 0.1kg γ-aminopropyltriethoxysilane (silane A-1100, available from DOW CHEMICAL), 1.5kg lignin (dehydrated lignin, available from Domtar Company) and 2kg glutaraldehyde (50wt% glutaraldehyde An aqueous solution of dialdehyde, available from Sigma-Aldrich) was added to the vessel, and the mixture was stirred for about 10 minutes. Next, 21 kg of D-fructose (solid content: 99% by weight) and 19 kg of glutamine (solid content: 98% by weight) were added to the container, and the resulting mixture was stirred for 30 minutes until dissolution was confirmed. Then, further 0.4kg organosilicon type hydrophobic agent (SI1460Z, obtained from KCC company) and 1kg dustproof oil ( 217 / S from Govi) was added to the vessel and the resulting mixture was stirred for about ten minutes to prepare the adhesive.

Embodiment 3

[0042] 450 kg of fresh water was added to the vessel used to prepare the adhesive and the pH was adjusted to a range of 8 to 14 using ammonia. Then, 0.1kg of γ-aminopropyltriethoxysilane (silane A-1100, obtained from DOW CHEMICAL), 1.5kg of lignin (wheat straw lignin, obtained from WuXi lansen Chemicals Co., Ltd.) and 2kg of glutaraldehyde (50wt % glutaraldehyde solution, available from Sigma-Aldrich) was added to the vessel, and the mixture was stirred for about 10 minutes. Next, 21 kg of D-fructose (solid content: 99% by weight) and 19 kg of glutamine (solid content: 98% by weight) were added to the container, and the resulting mixture was stirred for 30 minutes until dissolution was confirmed. Then, further 0.4kg organosilicon type hydrophobic agent (SI1460Z, obtained from KCC company) and 1kg dustproof oil ( 217 / S from Govi) was added to the vessel and the resulting mixture was stirred for about ten minutes to prepare the adhesive.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
boiling pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a binder composition comprising a natural aromatic polymer, and a method for binding a fibrous material by using the same.

Description

technical field [0001] The present invention relates to an adhesive composition and a method for bonding fibrous materials using the adhesive composition. More specifically, the present invention relates to an adhesive composition comprising a) one or more reducing sugars, b) one or more amino acids, c) one or more natural aromatic polymers, A derivative thereof or a salt compound thereof, d) one or more multifunctional aldehydes; and a method for bonding fiber materials using the adhesive composition. Background technique [0002] Although a technique of bonding fiber materials using phenolic resin has been developed, this technique has problems of poisonous raw materials used, foul smell of the resin, and the like. Therefore, people have begun to study various curing techniques to replace phenolic resins with different resins. [0003] Korean Registered Patent No. 240044, U.S. Patent Publication No. 2012-0133073, Korean Published Patent Application No. 1999-0037115, Kore...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J197/00C09J11/06
CPCC08H6/00C08L97/005C09J197/005C08K7/14
Inventor 李颂依金成晙洪承民金容柱
Owner KCC CORP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com