Preparation method for novel environment-friendly decorative material
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A decorative material and environmental protection technology, applied in the field of building decorative materials, can solve problems such as physical and mental health effects, harmful radiation, hazards, etc., and achieve the effects of good bonding durability, good adsorption, and improved comfort.
Inactive Publication Date: 2017-11-10
HEFEI XINYADA INTELLIGENT TECH CO LTD
View PDF2 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, when these decoration materials are used, they will produce harmful gases (such as benzene, formaldehyde, ether, etc.), harmful ions (such as hydrogen, oxygen, lead, molybdenum, etc.), harmful radiation (such as light, electricity, magnetism, sound, etc.), People live in this situation for a long time, which has a great impact and harm on their physical and mental health.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0024] A preparation method of a novel environment-friendly decorative material, comprising the following preparation steps:
[0025] a. Mixing nano-scale bentonite powder and nano-titanium dioxide into the furnace, and baking at a high temperature of 1200 ° C for 50 minutes to obtain mixture 1;
[0026] b. Put the mixture into deionized water, quench it into solid particles, then use a ball mill to grind it into a 3mm powder, dry it at 120°C, add chitosan acid solution, polypropylene fiber, and nano-scale bamboo powder to the powder , n-octanoic acid, patchouli leaf extract and adhesive, stirred at 300r / min for 30min to obtain material 1;
[0027] c. Spread material 1 flatly on the non-woven fabric with a laying thickness of 5 mm, arrange the non-woven fabric in a resistance furnace, raise the temperature to 1450 °C at a rate of 5 °C / min, and keep it warm for 2 hours to obtain material 2;
[0028] d. Press and form material 2 while it is hot, the pressure is 30Mpa, and the p...
Embodiment 2
[0037] A preparation method of a novel environment-friendly decorative material, comprising the following preparation steps:
[0038] a. Mixing nano-scale bentonite powder and nano-titanium dioxide into the furnace, and baking at a high temperature of 800 ° C for 40 minutes to obtain a mixture 1;
[0039] b. Put the mixture into deionized water, quench it into solid particles, then use a ball mill to grind it into a 3mm powder, dry it at 120°C, add chitosan acid solution, polypropylene fiber, and nano-scale bamboo powder to the powder , n-octanoic acid, patchouli leaf extract and adhesive, stirred at 300r / min for 20min to obtain material 1;
[0040] c. Spread material 1 flatly on the non-woven fabric with a laying thickness of 8 mm, place the non-woven fabric in a resistance furnace, raise the temperature to 1380 °C at a rate of 5 °C / min, and keep it warm for 2 hours to obtain material 2;
[0041] d. Press and form material 2 while it is hot, the pressure is 40Mpa, and the pr...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a preparation method for a novel environment-friendly decorative material. The preparation method comprises the following steps: a, adding nanometer bentonite powder and nanometer titanium dioxide into a melting furnace, and carrying out baking so as to obtain a mixture I; b, adding the mixture I into deionized water, carrying out cold quenching to obtain solid particles, then carrying out grinding with a ball mill and drying, adding an acid solution of chitosan, polypropylene fibers, nanometer bamboo powder, n-octanoic acid, the extract of leaves of Pogostemon cablin and an adhesive into the obtained powder, and the carrying out stirring so as to obtain a material I; c , flatly spreading the material I on a non-woven fabric, and treating the non-woven fabric in a resistance furnace so as to obtain a material II; and d, subjecting the material II to compression molding while the material II is still hot, then carrying out cutting and shaping as needed, and successively carrying out grinding, polishing and trimming. The environment-friendly decorative material prepared in the invention has the advantages of high mechanical strength, high hardness and good heat resistance, bending resistance, corrosion resistance and abrasion resistance.
Description
technical field [0001] The invention belongs to the technical field of building decoration materials, and in particular relates to a preparation method of a novel environment-friendly decoration material. Background technique [0002] With the improvement of people's living standards, while paying more and more attention to the quality of life, they pay more attention to environmental protection and health, which is reflected in the increasing demand for decoration of the living environment. Therefore, the decoration concept of modern people should not only be satisfied with the beautiful and comfortable decoration, but also require the decoration materials to be pollution-free, healthy and environmentally friendly. And the place such as present conventional family residence, office place, public place, entertainment place, interior decoration generally is to use plastering cement troweling, gypsum putty batch scraping, paint surface treatment, gypsum board, line, the method...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more