Insulating waterproof coating and using method thereof

A waterproof coating, mass fraction technology, applied in wax coatings, coatings, devices for coating liquid on surfaces, etc., can solve the problems of water resistance and insulation to be improved, and achieve good elasticity and flexibility, excellent environmental performance. Effect

Inactive Publication Date: 2017-10-24
太仓红潮新材料科技有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the waterproof and insulating properties of the current composite coatings need to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] An insulating waterproof coating, based on its total weight, including the following components in mass fractions:

[0033] Acrylate elastic emulsion 15%, partial chloride emulsion 1%, chlorinated paraffin wax 10%, mica powder 5%, talc powder 1%, boron nitride 1%, zirconium nitride 1%, aluminum oxide 2%, alkaline silica sol 5%, defoamer 2%, adhesion promoter 3%, and the balance is water.

Embodiment 2

[0035] An insulating waterproof coating, based on its total weight, including the following components in mass fractions:

[0036] Acrylate elastic emulsion 15%, partial chloride emulsion 1%, chlorinated paraffin wax 10%, mica powder 5%, talc powder 1%, boron nitride 1%, zirconium nitride 1%, aluminum oxide 2%, alkaline silica sol 5%, defoamer 2%, dispersant 3%, and the balance is water.

Embodiment 3

[0038] An insulating waterproof coating, based on its total weight, including the following components in mass fractions:

[0039] Acrylate elastic emulsion 15%, partial chloride emulsion 1%, chlorinated paraffin wax 10%, mica powder 5%, talc powder 1%, boron nitride 1%, zirconium nitride 1%, aluminum oxide 2%, alkaline silica sol 5%, the balance is water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an insulating waterproof coating, which comprises the following components in mass fractions based on the total weight: 15-20% of acrylate elastic emulsion, 1-2% of partial chlorine emulsion, 5-10% of chlorinated paraffin, Mica powder 1‑5%, talc powder 1‑5%, boron nitride 1‑2%, zirconium nitride 1‑2%, alumina 1‑2%, binder 5‑10%, additive 5‑10 %, the balance is water. The present invention also provides a method for using the insulating waterproof coating, comprising the following steps: coating the insulating waterproof coating on the surface of the base material to form an insulating waterproof layer; coating a layer of phosphoric acid solution of aluminum dihydrogen phosphate on the insulating waterproof layer . The paint of the invention is suitable for various base materials, and can be applied on wet base surfaces without affecting the combination of the insulating waterproof layer and the base surface.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an insulating waterproof coating and a using method thereof. Background technique [0002] Present composite coating mainly contains two kinds of composite forms, and one is the composite of two types of coatings in varieties, and the other is the composite decoration of the coating of two types of coatings. The compounding of the two types of coatings is to prepare water-based organic resin and water-soluble silicate to form a mixed solution or dispersion, or to graft an organic polymer on the surface of an inorganic substance to form a suspension. [0003] Organic polymers or resins in composite coatings can improve the disadvantages of inorganic materials that become hard and brittle after film formation, and at the same time avoid or alleviate the problems of organic materials such as easy aging, pollution resistance, and poor heat resistance. However, the water resistance and insula...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D127/08C09D191/06C09D5/25C09D7/12B05D3/10B05D5/00B05D7/06B05D7/14
CPCC09D133/04B05D3/108B05D5/00B05D7/06B05D7/14B05D2203/30C08K2003/2227C08K2003/385C08K2201/014C08L2205/03
Inventor 孙陆逸张冬桥俞冬辉
Owner 太仓红潮新材料科技有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com