A curtain fabric with a good waterproof performance
A technology for curtains and fabrics, used in curtains, curtains, window decorations, etc., can solve problems such as accumulation and wetting of rainwater, and achieve the effect of improving waterproof performance and ensuring waterproof performance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] A curtain fabric with good waterproof performance is prepared from the following fibers: 30 g of bamboo fiber, 10 g of corn fiber, 10 g of mulberry silk, 20 g of flax fiber, and 80 g of waterproof modified polyester fiber. The sides are coated with a waterproof layer, in which waterproof modified polyester fibers are prepared from the following components: polyethylene terephthalate 100 g, alpha cellulose 20 g, cocamidopropylamine oxide 3 g , vermiculite 10 g, sepiolite 3 g, vinyl silane coupling agent 0.7 g, viscose fiber 0.2 g. Vermiculite and sepiolite are mixed uniformly before use and then calcined at 300°C for 6 hours.
[0024] A method for preparing a curtain fabric with good waterproof performance, comprising the following steps:
[0025] (1) Preparation of waterproof modified polyester fiber: After fully mixing the various raw material components, they are sent to a screw extruder to extrude to obtain a mixed masterbatch, and then wet-spun to make waterproof m...
Embodiment 2
[0030] A curtain fabric with good waterproof performance is prepared from the following fibers: 40 g of bamboo fiber, 12.5 g of corn fiber, 12.5 g of mulberry silk, 25 g of flax fiber, and 90 g of waterproof modified polyester fiber. The side is coated with a waterproof layer, in which the waterproof modified polyester fiber is prepared from the following components: polyethylene terephthalate 110 g, cellulose A 25 g, cocamidopropylamine oxide 4 g, Vermiculite 12.5 g, sepiolite 4 g, vinyl silane coupling agent 0.9 g, viscose fiber 0.35 g. Vermiculite and sepiolite were mixed uniformly before use and then calcined at 325°C for 5 hours.
[0031] A method for preparing a curtain fabric with good waterproof performance, comprising the following steps:
[0032] (1) Preparation of waterproof modified polyester fiber: After fully mixing the various raw material components, they are sent to a screw extruder to extrude to obtain a mixed masterbatch, and then wet-spun to make waterproo...
Embodiment 3
[0037]A curtain fabric with good waterproof performance is prepared from the following fibers: 50 g of bamboo fiber, 15 g of corn fiber, 15 g of mulberry silk, 30 g of flax fiber, and 100 g of waterproof modified polyester fiber. The sides are coated with a waterproof layer, in which waterproof modified polyester fibers are prepared from the following components: polyethylene terephthalate 120 g, alpha cellulose 30 g, cocamidopropylamine oxide 5 g , 15 g of vermiculite, 5 g of sepiolite, 1.1 g of vinyl silane coupling agent, and 0.5 g of viscose fiber. Vermiculite and sepiolite are mixed uniformly before use and then calcined at 350°C for 6 hours.
[0038] A method for preparing a curtain fabric with good waterproof performance, comprising the following steps:
[0039] (1) Preparation of waterproof modified polyester fiber: After fully mixing all raw material components, they are sent to a screw extruder to extrude to obtain a mixed masterbatch, and then wet-spun to make wate...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com