Macromolecule polymer emulsion as well as preparation method thereof and waterproof coating prepared from emulsion

A high-molecular polymer and emulsion technology, applied in the field of coatings, can solve the problems of low tensile strength and elongation, high and low temperature flexibility, curing of waterproof materials, and poor high and low temperature characteristics, so as to achieve good water resistance and coating film elasticity Large, excellent weather resistance and the effect of low temperature resistance

Inactive Publication Date: 2017-07-07
呼伦贝尔辰研化工新科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, domestic cement-based waterproof coatings have disadvantages such as poor aging resistance, low tensile strength and elongation, and high and low temperature flexibility due to polymer emulsions; especially for housing waterproofing projects, high and low temperature properties are not good. It is easy to cause aging, cracking, deformation, breaking and rot; especially when construction is carried out under low temperature conditions in the north, the waterproof material is easy to solidify before freezing; therefore, it is urgent to develop a waterproof material that overcomes the above problems to make up for the waterproof market. demand gap

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Macromolecule polymer emulsion as well as preparation method thereof and waterproof coating prepared from emulsion
  • Macromolecule polymer emulsion as well as preparation method thereof and waterproof coating prepared from emulsion
  • Macromolecule polymer emulsion as well as preparation method thereof and waterproof coating prepared from emulsion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] Embodiment 1: a kind of polymer emulsion, it comprises each component of following mass fraction: 0.1 part of chloroprene latex, 3 parts of butyl latex, 45 parts of ethyl acrylate latex, 15 parts of siloxane emulsion, ortho 4 parts of dibutyl phthalate, 0.045 parts of anionic surfactant, 2 parts of polyvinyl alcohol, 18 parts of polysiloxane, 19 parts of sodium hydroxide, and 0.2 parts of auxiliary agent; wherein, the auxiliary agent is a thickening suspending agent.

Embodiment 2

[0057] Embodiment 2: a kind of preparation method of polymer emulsion, comprises the following steps: (1) batching; (2) prepares the first emulsion; (3) prepares waterproofing agent; (4) prepares the second emulsion; (5) Preparation of auxiliary agent solution; (6) preparation of finished product; wherein,

[0058] (1) Ingredients

[0059] Weigh each component according to the following parts by mass: 0.1 part of neoprene latex, 3 parts of butyl latex, 45 parts of ethyl acrylate latex, 15 parts of silicone emulsion, 4 parts of dibutyl phthalate, anionic surfactant 0.045 parts of agent, 2 parts of polyvinyl alcohol, 18 parts of polysiloxane, 19 parts of sodium hydroxide, 0.2 part of auxiliary agent; wherein, the auxiliary agent is a thickening suspending agent;

[0060] (2) Preparation of the first emulsion

[0061] In the reaction kettle, add 0.1 parts of neoprene latex, 3 parts of butyl latex, 45 parts of ethyl acrylate latex, 15 parts of siloxane emulsion, 4 parts of dibut...

Embodiment 3

[0071] Embodiment 3: a kind of polymer latex, it comprises each component of following mass fraction: 1 part of chloroprene latex, 3.6 parts of butyl latex, 47 parts of ethyl acrylate latex, 16 parts of siloxane emulsion, ortho 5 parts of dibutyl phthalate, 2.5 parts of anionic surfactant, 2.7 parts of polyvinyl alcohol, 20 parts of polysiloxane, 20 parts of sodium hydroxide, and 0.6 parts of auxiliary agent; wherein, the auxiliary agent is a thickening suspending agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a macromolecule polymer emulsion. The macromolecule polymer emulsion comprises the following components in parts by mass: 0.1-2 parts of neoprene latex, 3-4.3 parts of butyl latex and 45-49 parts of ethyl acrylate latex. A preparation method of the macromolecule polymer emulsion comprises the following steps: (1) preparing materials; (2) preparing a first emulsion; (3) preparing a waterproof agent; (4) preparing a second emulsion; (5) preparing an additive solution; and (6) preparing the finished product. A waterproof coating comprises the following components in parts by mass: 36-45 parts of the macromolecule polymer emulsion, 50-58 parts of composite powder and 5-6 parts of additives. The macromolecule polymer emulsion is high in elongation rate; the waterproof coating has waterproof and self-healing functions.

Description

[0001] Technical field: [0002] The invention relates to the technical field of coatings, in particular to a high molecular polymer emulsion, a preparation method thereof and a waterproof coating prepared therefrom. [0003] Background technique: [0004] Waterproof materials are generally divided into flexible waterproof materials and rigid waterproof materials. Among them, flexible waterproof materials have poor aging resistance, weather resistance, and water resistance, and are not suitable for waterproofing the backwater surface and wet base surface; rigid waterproof materials are not suitable for engineering deformation and displacement. waterproof treatment. Domestic polymer building waterproof materials mainly use butyl acrylate, methyl methacrylate, polyethylene and synthetic resin as raw materials. However, these raw materials need to be improved in terms of flexibility and elongation in cold environments. Traditional waterproof materials are toxic and not environme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L33/08C08L83/04C08K5/12C08J3/03C04B26/32
CPCC08L33/08C04B26/32C04B2111/00293C04B2201/50C08J3/03C08J2333/08C08J2483/04C08L2205/02C08L2205/035C08L83/04C08K5/12C04B14/28C04B14/20C04B14/042C04B14/06C04B14/04C04B2103/302C04B2103/601
Inventor 谢志杰谢效洧谢欣洧
Owner 呼伦贝尔辰研化工新科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com