Waterborne environment-friendly high-adhesion sealing adhesive

A high-adhesive, sealing adhesive technology, applied in the direction of polymer adhesive additives, adhesive types, ester copolymer adhesives, etc., can solve the problem of long surface drying time, low initial adhesion, poor permeability, etc. problem, to achieve the effect of fast drying time, strong initial adhesion and strong permeability

Inactive Publication Date: 2017-06-13
韩志龙
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing sealants have defects such as long surface...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Step 1: Emulsify 20kg of deionized water, 0.4kg of ethoxylated alkylphenol ammonium sulfate (co-436) into foam, add 14kg of styrene, 0.7kg of methyl methacrylate, 18kg of butyl acrylate, isoacrylate Add 0.8kg of octyl ester, 0.05kg of acrylic acid, 0.05kg of ethyl acrylate, 0.05kg of N-methylolacrylamide, 0.04kg of diacetone acryloyl, and 0.1kg of dodecanethiol into the pre-emulsification tank, and mix them Pre-emulsion A, weighing 5% of which is set as the bottom seed reaction solution B for subsequent use;

[0024] Step 2: Add 20kg of deionized water, 0.2kg of ethoxylated alkylphenol ammonium sulfate (co-436), and 0.1kg of sodium bicarbonate into the polymerization reactor, stir and raise the temperature to 80°C, and add 0.1kg of ammonium persulfate Raise to 80°C, put in the bottom seed reaction solution B, react for 35 minutes, then raise the temperature to 86°C, add the mixed pre-emulsion A into the polymerization reactor by dropwise addition, and drop 0.1kg of ammo...

Embodiment 2

[0029] Step 1: Emulsify 30kg of deionized water, 0.8kg of ethoxylated alkylphenol ammonium sulfate (co-436) into foam, add 18kg of styrene, 1kg of methyl methacrylate, 30kg of butyl acrylate, and isooctyl acrylate Add 1.2kg of ester, 0.1kg of acrylic acid, 0.1kg of ethyl acrylate, 0.1kg of N-methylolacrylamide, 0.06kg of diacetone acryloyl, and 0.05kg of dodecyl mercaptan into the pre-emulsification tank. Emulsion A, weighing 5% of which is set as the bottom seed reaction solution B for subsequent use;

[0030] Step 2: Add 30kg of deionized water, 0.4kg of ethoxylated alkylphenol ammonium sulfate (co-436), and 0.3kg of sodium bicarbonate into the polymerization reactor, stir and heat up to 80°C, and add 0.3kg of potassium persulfate Raise to 80°C, put in the bottom seed reaction solution B, react for 40 minutes, then raise the temperature to 86°C, add the mixed pre-emulsion A into the polymerization reactor by dropwise addition, and add 0.4kg of ammonia water dropwise at the s...

Embodiment 3

[0035] Step 1: Emulsify 25kg of deionized water, 0.6kg of ethoxylated alkylphenol ammonium sulfate (co-436) into foam, add 16kg of styrene, 0.8kg of methyl methacrylate, 26kg of butyl acrylate, isoacrylate Add 1.0kg of octyl ester, 0.07kg of acrylic acid, 0.08kg of ethyl acrylate, 0.06kg of N-methylolacrylamide, 0.05kg of diacetone acryloyl, and 0.03kg of dodecanethiol into the pre-emulsification tank, and mix them after stirring. Pre-emulsion A, weighing 5% of which is set as the bottom seed reaction solution B for subsequent use;

[0036] Step 2: Add 23kg of deionized water, 0.3kg of ethoxylated alkylphenol ammonium sulfate (co-436), and 0.2kg of sodium bicarbonate into the polymerization reactor, stir and heat up to 80°C, and add 0.3kg of potassium persulfate Raise to 80°C, put in the bottom seed reaction solution B, react for 40 minutes, then raise the temperature to 86°C, add the mixed pre-emulsion A into the polymerization reactor by dropping, and add 0.3kg of ammonia wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Surface dry timeaaaaaaaaaa
Peel strengthaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to waterborne environment-friendly high-adhesion sealing adhesive, prepared by combining sealing adhesive stock solution, Tacolyn 3509 emulsion tackifying resin, waterborne rosin, organic wax and deionized water according to a weight ratio of 5:3:1:0.5:0.5, wherein the sealing adhesive stock solution is made by polymerizing, at a weight ratio, deionized water, an emulsifier, styrene, methyl methacrylate, butyl acrylate, 2-ethylhexyl acrylate, acrylic acid, ethyl acrylate, N-methylolacrylamide, diacetoneacrylamide, a molecular control agent, a PH buffer agent, an initiator, a PH regulator and a functional aid. The invention also relates to a preparation method of the waterborne environment-friendly high-adhesion sealing adhesive. Compared with the prior art, the waterborne environment-friendly high-adhesion sealing adhesive has high initial adhesion and high permeability, can dry fast from surface in 20 s, and has peel strength of greater than 2 N/cm when it is dry.

Description

technical field [0001] The invention relates to the technical field of sealing glue, in particular to a water-based environment-friendly high-adhesion sealing glue and a preparation method thereof. Background technique [0002] Sealing glue is a one-component quick-drying water-based adhesive, non-toxic and non-polluting. Its products include hand glue and machine glue. Glue for lap molding. It is widely used in the bonding of cigarette boxes, wine boxes, shoe boxes, medicine boxes, health care boxes, food boxes, handbags, etc., as well as various paper, paper plastic, composite film paper, and glazing cartons in other related industries. Existing sealants have defects such as long surface-drying time, low initial adhesion, and poor permeability. Contents of the invention [0003] The invention proposes a water-based environment-friendly high-adhesion sealant and a preparation method thereof. [0004] Water-based environment-friendly high-adhesion sealing glue, the seal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/08C09J11/08C08F220/18C08F220/14C08F212/08C08F220/06C08F220/58C08F222/38
CPCC08F220/18C08F220/1804C08L2205/035C09J11/08C09J133/08C08L93/04C08L91/06C08L75/04C08F220/14C08F212/08C08F220/06C08F220/58C08F220/1808C08F222/385
Inventor 韩志龙
Owner 韩志龙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap