Nanometer enhanced paper plastic material and preparation method thereof

A nano-reinforcement and manufacturing method technology, applied in the field of nano-cellulose reinforced paper-plastic materials and its manufacturing, can solve the problems of high equipment cost, poor mechanical properties of paper-plastic materials, and difficulties in continuous production of waste paper extrusion molding, etc. Achieve good dispersion, improve mechanical properties, and expand the effect of application fields

Inactive Publication Date: 2016-12-14
SOUTH CHINA AGRI UNIV
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the above problems, the purpose of the present invention is to provide a method that overcomes the difficulties in the continuous production of waste paper extrusion molding, poor mechanical properties of paper-plastic materials, and high equipment costs in the prior art, and provides a simple and energy-consuming A kind of nano-reinforced paper-plastic material with few, excellent mechanical properties and low cost and its manufacturing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Adopt this inventive method to manufacture a kind of nano-reinforced paper-plastic material and its manufacturing method, the specific steps are as follows:

[0033] (1), preparation is used to form the waste newspaper powder of composite material: Concrete steps are A: waste newspaper pretreatment: first waste newspaper is preliminarily pulverized, then the scrap after pulverizing is immersed in the sodium hydroxide solution of mass concentration 2% , treated at room temperature for 20 minutes, filtered and then dried, the drying temperature was 90°C, and the drying time was 18 hours; B: Crushing again: the dried pulp was pulverized in stages to obtain 40-200 mesh paper powder.

[0034] (2), raw material mixing: 42% waste newspaper powder, 39.7% high-density polyethylene, 5% calcium carbonate, 3‰ compound antioxidant 225: 5% maleic anhydride grafted polyethylene, HK101 / HK102=1 : 1, each 2.5%; 3% nanocellulose. Put them into a high-speed mixer for blending: the mixing ...

Embodiment 2

[0039] Adopt this inventive method to manufacture a kind of nano-reinforced paper-plastic material and its manufacturing method, the specific steps are as follows:

[0040] (1), preparation of waste roof-top packaging carton materials used to form composite materials: the specific steps are A: pretreatment of waste roof-top packaging cartons: first, the waste roof-top packaging cartons are initially crushed, and then the crushed pieces The material is immersed in a sodium hydroxide solution with a mass concentration of 2.5%, treated at room temperature for 40 minutes, and dried after filtration. The drying temperature is 100°C and the drying time is 24 hours; B: Crushing again: the dried pulp is crushed in stages Obtain 40-200 mesh paper powder.

[0041] (2) Mixing raw materials: 49.7% waste roof-top carton paper powder, 30% high-density polyethylene, 5% calcium carbonate, 3‰ compound antioxidant 225: 5% maleic anhydride grafted polyethylene, HK101 / HK102=1:1, 2.5% each; 5% n...

Embodiment 3

[0046] Adopt this inventive method to manufacture a kind of nano-reinforced paper-plastic material and its manufacturing method, the specific steps are as follows:

[0047] (1), preparation of waste and old wallpaper base materials used to form composite materials: the specific steps are A: pretreatment of waste and old wallpaper base materials: first, the waste and old wallpaper base materials are initially pulverized, and then the crushed scraps are immersed in 1.8% mass concentration Sodium hydroxide solution, treated at room temperature for 30 minutes, filtered and then dried, the drying temperature was 90°C, and the drying time was 20 hours; B: Crushing again: the dried pulp was crushed in stages to obtain 40-200 mesh paper powder .

[0048](2), raw material mixing: 46% waste and old wallpaper substrate paper powder, 31.7% high-density polyethylene, 8% calcium carbonate, 3‰ compound antioxidant 225, 5% maleic anhydride grafted polyethylene, HK101 / HK102=1:1, 2.5% each; 4...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a nanometer enhanced paper plastic material and a preparation method thereof. Well mixing, granulation, extrusion moulding and other steps are carried out for waste paper powder, high density polyethylene, a filling material, an anti-oxidant, a coupling agent, a lubricant and nanometer cellulose and other materials; and the nanometer enhanced paper plastic material which can be applied to the fields of outdoor floors, plank roads, corridors, packages and the like is obtained. Granular materials which have good dispersibility and are suitable for continuous industrial production are prepared by using reclaimed waste paper materials, nanometer cellulose is added, so that the material has higher mechanical properties, and application fields of paper plastic composite materials are enlarged; nanometer cellulose with modified functions is added for realization of electromagnetic shielding, antibiosis or luminescence and other additional effects; added values of paper plastic composite materials are increased, and at the same time, the material has important meanings for reducing environmental pollution.

Description

technical field [0001] The invention belongs to the field of wood-plastic composite materials, and in particular relates to nanocellulose-reinforced paper-plastic materials and a manufacturing method thereof. Background technique [0002] With the increasing amount of recycled paper in the world, how to use these waste paper with high added value has become an important issue. Chinese Patent No.: 201310081384.X discloses a production process of waste paper made of polyethylene composite material: combine the regenerated waste paper powder with alkaline solution and send it to the mixer under the condition of 30-40°C and 50r / min. After mixing, hot pressing molding. It proves the feasibility of using waste paper as raw material for composite materials. However, the dispersion of waste paper in the composite material prepared by this method is not good, and it is difficult to carry out continuous industrial production. [0003] Chinese Patent No.: 201310006671.4 discloses a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L1/02C08L23/06C08L51/06C08K13/02C08K3/26C08K5/134C08K5/526
CPCC08L1/02C08L2201/08C08L2205/025C08L2205/035C08L2207/062
Inventor 古今鲁群霞陈敏杰云虹胡传双涂登云宋杰
Owner SOUTH CHINA AGRI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap