Novel PVC (polyvinyl chloride) profile and preparation method thereof

A profile and a new type of technology, applied in the field of decorative materials, can solve the problems of poor apparent quality and poor gloss of PVC profiles, and achieve the effects of excellent thermal insulation performance, smooth surface and improved tensile impact strength

Inactive Publication Date: 2016-08-17
CHONGQING WANSENDA TECH DEV CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the apparent quality of existing PVC profiles is not good, such as poor gloss

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel PVC (polyvinyl chloride) profile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A new type of PVC profile, which consists of: 65kg of PVC waste, 12kg of sawdust, 13kg of 600-mesh light calcium carbonate, 0.72kg of rutile titanium dioxide, 2.5kg of EVA impact modifier, 1.8kg of MBS impact modifier, 0.84 kg of tin maleate, 0.48 kg of epoxy grease, 0.18 kg of ethyl bis stearamide, 0.45 kg of ethylene bis stearic acid and 2.4 kg of siloxane coupling agent.

[0027] The preparation method of described novel PVC profile is:

[0028] A. Grind PVC waste into powder and put it in a mixer, then add sawdust and light calcium carbonate to the mixer and stir for 8 minutes at a temperature of 136°C;

[0029] B. Mix maleic acid tin salt, epoxy grease, ethyl bis stearamide, ethylene bis stearic acyl, EVA impact modifier, MBS impact modifier, siloxane coupling agent and rutile Formed titanium dioxide was sequentially added to the mixture obtained in step A, stirred at 83°C for 9 minutes; then cooled to room temperature, extruded after discharge, and the new PVC pr...

Embodiment 2

[0031] A new type of PVC profile, which consists of: 55kg of PVC waste, 12kg of sawdust, 13kg of 600-mesh light calcium carbonate, 0.84kg of rutile titanium dioxide, 3.2kg of EVA impact modifier, 1.8kg of MBS impact modifier, Fatty acid tin salt 0.96kg, epoxidized soybean oil 0.51kg, ethyl bis stearamide 0.22 kg, ethylene bis stearic acid acyl 0.55 kg and siloxane coupling agent 1.5 kg.

[0032] The preparation method of described novel PVC profile is:

[0033] A. Put the PVC waste into powder and put it in the mixer, then add sawdust and light calcium carbonate into the mixer and stir at 129°C for 13 minutes;

[0034] B. Combine fatty acid tin salt, epoxidized soybean oil, ethyl bis stearamide, ethylene bis stearic acyl, EVA impact modifier, MBS impact modifier, siloxane coupling agent and rutile Titanium dioxide was sequentially added to the mixture obtained in step A, stirred at 78° C. for 6 minutes; then cooled to room temperature, discharged and then extruded to obtain t...

Embodiment 3

[0036] A new type of PVC profile, which consists of: 60kg of PVC waste, 13.6kg of sawdust, 14kg of 500-mesh light calcium carbonate, 0.75kg of rutile titanium dioxide, 2.8kg of EVA impact modifier, and 2.1kg of MBS impact modifier , fatty acid tin salt 0.88kg, epoxy grease 0.49kg, ethyl distearyl 0.2kg, ethylene distearyl 0.5kg and siloxane coupling agent 1.8kg.

[0037] The preparation method of described novel PVC profile is:

[0038] A. Grind PVC waste into powder and put it in a mixer, then add sawdust and light calcium carbonate into the mixer and stir for 11 minutes at a temperature of 134°C;

[0039] B. Combine fatty acid tin salt, epoxy resin, ethyl bis stearamide, ethylene bis stearic acid acyl, EVA impact modifier, MBS impact modifier, siloxane coupling agent and rutile titanium White powder was added to the mixture obtained in step A in turn, stirred at 81°C for 8 minutes; then cooled to room temperature, extruded after discharge, and the new PVC profile was obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Glossaaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel PVC (polyvinyl chloride) profile which comprises the following components in parts by weight: 55-65 parts of PVC waste, 12-15 parts of wood dust, 13-15 parts of light calcium carbonate, 0.72-0.84 part of titanium white, 2.5-3.2 parts of EVA (ethylene-vinyl acetate) impact modifier, 1.8-2.3 parts of MBS (methyl methacrylate-butadiene-styrene) impact modifier, 0.84-0.96 part of organic tin stabilizer, 0.48-0.51 part of epoxy compound stabilizer, 0.63-0.77 part of aliphatic acid amine and 1.5-2.4 parts of coupling agent. The PVC profile has the advantages of smooth surface, regular edge, no cracks, pores, adhesion, bubbles or scars, and high glossiness (up to 56.53Gu). The PVC profile has excellent heat-insulating property, ending deformation resistance, tensile impact resistance and solderability.

Description

technical field [0001] The invention relates to the field of decorative materials, in particular to a novel PVC profile and a preparation method thereof. Background technique [0002] The English abbreviation of polyvinyl chloride is PVC, which is a thermoplastic resin polymerized by vinyl chloride under the action of an initiator, and is a homopolymer of vinyl chloride. Vinyl chloride homopolymers and vinyl chloride copolymers are collectively referred to as vinyl chloride resins. PVC is a white powder with an amorphous structure and a small degree of branching. PVC is the most widely used general-purpose plastic in the world. It is widely used in building materials, industrial products, daily necessities, door and window leather, door and window bricks, artificial leather, pipes, wires and cables, packaging films, bottles, foaming materials, sealing materials, fibers, etc. are widely applied. [0003] PVC profiles are industrial and domestic PVC products that are extrud...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L97/02C08L23/08C08L51/04C08K13/02C08K3/26C08K3/22C08K5/20C08K5/5415
CPCC08L27/06C08K2201/003C08L2205/035C08L97/02C08L23/0853C08L51/04C08K13/02C08K2003/265C08K2003/2241C08K5/20C08K5/5415
Inventor 邓昌华
Owner CHONGQING WANSENDA TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap