Fiber protection material with high fireproof coefficient

Abstract

The invention discloses a fiber protection material with high fireproof coefficient, which comprises the following raw materials by weight part: 50-55 parts of low density polyethylene, 13-15 parts of EVA resin, 69-12 parts of nylon, 14-16 parts of magnesium hydroxide, 0.6-0.8 parts of sodium methylene bis-naphthalene sulfonate, 1.3-2 parts of titanate coupling agent, 5-8 parts of organosilicon, 3-5 parts of organo montmorillonite, 2-4 parts of vinyl acetate, 4-5 parts of ceramic silicone rubber, 2-3 parts of perfluoropolyether, 4-5 parts of ammonium polyphosphate, 3-4 parts of tributyl 2-acetylcitrate, and a proper amount of deionized water. The synergism of the ceramic silicone rubber and ammonium polyphosphate can greatly enhance the refractiveness and flame resistance of a polyolefin material, combustion smog is little, and the fiber protection material has little hazardness on environment and human body, and is good for popularization.

Description

technical field [0001] The invention relates to the technical field of optical fiber sheathing materials, in particular to an optical fiber protection material with high fire resistance coefficient and a preparation method thereof. Background technique [0002] With the rapid development of the data communication industry, optical fiber is being widely used as the carrier of data transmission. The laying forms of optical fiber are buried and overhead, and with the transformation of urban network lines, most of them have been transferred underground. In order to prevent underground optical fibers and optical cables from being bitten or corroded by insects, sheath materials for optical fibers and optical cables have emerged as the times require. At present, polyolefin is mainly used as the sheath material of optical fiber and optical cable, which has the characteristics of light weight, high bending strength, small friction coefficient, good sealing performance, and corrosion...

AI Technical Summary

Problems solved by technology

[0003] Inorganic halogen-free flame retardants have strong polarity and hydrophilicity, while polyolefins are non-polar materials, the compatibility between the two is poor, and it is difficult to form a good bond and bond at the interface, especially magnesium hydroxide Magnesium hydroxide has excellent flame retardancy, smoke suppression, anti-dripping, anti-acid and other functions, and has been widely used. However, magnesium hydroxide has strong polarity, and its thermal expansion coefficient is different from that of resin. When it is processed and molded, it will expand with heat and contract with cold. The phase interface forms fine cracks, which will lead to the decline of the mechanical performance, waterproof performance and insulation performance of the material. Therefore, the surface modification of magnesium hydroxide must be carried out to make magnesium hydroxide have better comprehensive performance in polyolefin. It has good fluidity at high temperature and high strength and toughness at service temperature, and does not change the impact resistance of polyolefin profiles