Solid-phase synthesis method for caesium tungsten bronze powder

A solid-phase synthesis method, cesium tungsten bronze technology, applied in tungsten compounds, chemical instruments and methods, inorganic chemistry, etc., can solve the problems of increasing gas source cost, increasing equipment investment, etc., achieve short reaction cycle, save gas source, The effect of simple synthesis process

Active Publication Date: 2015-11-04
烟台佳隆纳米产业有限公司
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the introduction of inert gas in the reaction will inevitably increase equipment investment, and the cost of gas source will also increase

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solid-phase synthesis method for caesium tungsten bronze powder
  • Solid-phase synthesis method for caesium tungsten bronze powder
  • Solid-phase synthesis method for caesium tungsten bronze powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A solid phase synthesis method of cesium tungsten bronze powder, comprising the following steps:

[0026] (1) Weigh 9.6g of ammonium tungstate and 3.1g of cesium carbonate, and grind them until they are evenly mixed;

[0027] (2) Put the ground material into a closed container and put it into a muffle furnace for reaction, the reaction temperature is 800°C, and the reaction time is 1h;

[0028] (3) After the reaction, blue-black cesium tungsten bronze powder with complete crystallinity is obtained.

[0029] The cesium tungsten bronze powder prepared in this embodiment has a metallic luster and is blue-black. from figure 1 It can be seen from the figure that the cesium tungsten bronze powder has high crystallinity and the crystal phase composition is Cs 0.3 WO 3 or Cs 0.32 WO 3 .

Embodiment 2

[0031] A solid phase synthesis method of cesium tungsten bronze powder, comprising the following steps:

[0032] (1) Weigh 11.3g of tungstic acid and 3.0g of cesium hydroxide, grind them until they are evenly mixed;

[0033] (2) Put the grinding material into a closed container and put it into a muffle furnace for reaction. The reaction temperature is 800°C and the reaction time is 2 hours;

[0034] (3) After the reaction, blue-black cesium tungsten bronze powder with complete crystallinity is obtained.

[0035] The cesium tungsten bronze powder prepared in this embodiment has a metallic luster and is blue-black. from figure 2 It can be seen from the figure that the cesium tungsten bronze powder has high crystallinity and the crystal phase composition is Cs 0.3 WO 3 or Cs 0.32 WO 3 .

Embodiment 3

[0037] A solid phase synthesis method of cesium tungsten bronze powder, comprising the following steps:

[0038] (1) Weigh 14.4g of ammonium tungstate and 3.7g of cesium nitrate, grind them until they are evenly mixed;

[0039] (2) Put the ground material into a high-temperature-resistant crucible, put the charged crucible into a closed stainless steel container, seal it and put it into a muffle furnace for reaction. The reaction temperature is 750°C and the reaction time is 2 hours;

[0040] (3) After the reaction, blue-black cesium tungsten bronze powder with complete crystallinity is obtained.

[0041] The cesium tungsten bronze powder prepared in this embodiment has a metallic luster and is blue-black. from image 3 It can be seen from the figure that the cesium tungsten bronze powder has high crystallinity and the crystal phase composition is Cs 0.3 WO 3 or Cs 0.32 WO 3 ;from Figure 4 It can be seen that its transmittance in the near-infrared region is low, indica...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of metal oxide powder preparation and particularly relates to a solid-phase synthesis method for caesium tungsten bronze powder. The solid-phase synthesis method comprises the following steps of weighing a tungsten compound and cesium salt according to the W / Cs molar ratio (2-3.5):1, and mixing and grinding; placing the ground substance into a sealed vessel to react at the temperature of 750-800 DEG C for 1-2 hours; and ending the reaction to obtain the black blue caesium tungsten bronze powder with complete crystallinity, wherein the crystal phase comprises the component, namely Cs0.3WO3 or Cs0.32WO3. According to the solid-phase synthesis method, a solid raw material is adopted to directly react in a sealed vessel, inert gases or reducing gases are not needed to be introduced, and a gas generated by self-reaction is used as a protecting gas, so that the obtained powder is black blue, the air source is saved, and the cost is reduced; in addition, the synthesis process disclosed by the invention is simple, short in reaction period and suitable for industrial production.

Description

technical field [0001] The invention belongs to the technical field of metal oxide powder preparation, in particular to a solid phase synthesis method of cesium tungsten bronze powder. Background technique [0002] WO 3 It has excellent performance in electrochromism, catalysis, gas sensitivity, etc. Its composite oxide - tungsten bronze, generally refers to a metal oxide with a darker metallic luster, and is usually a metal conductor or metal semiconductor, tungsten Bronze Formula A x WO 3 , However, with the different types and moles of cations—the values ​​of A and x, the structure and color of the compound will be different (J Analytical and Pyrolysis, 2000, 56:23-31). At present, there are many potassium cesium tungsten bronzes and cesium tungsten bronzes. Because of its low resistance, excellent visible light transmittance and near-infrared shielding performance, cesium tungsten bronze is widely used to prepare conductive films, and is used in transparent heat insul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01G41/00
Inventor 盛振宏施建军李宁陈鑫刘力娜王茂智冯志强刘静王晓梅王晓华徐斌
Owner 烟台佳隆纳米产业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com