A white corundum vitrified grinding wheel bond added with construction glass waste

A technology for architectural glass and ceramic grinding wheels, applied in abrasives, metal processing equipment, manufacturing tools, etc., can solve the problems of reducing the refractoriness of the binder, reducing the bonding strength of the binder, and increasing the production cost of the ceramic binder, so as to reduce the refractoriness. , the effect of increasing the infiltration capacity and saving the comprehensive production cost

Active Publication Date: 2017-08-25
白鸽磨料磨具有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Considering the needs of energy saving at low temperature, boron glass and other fusible substances are generally added to reduce the refractoriness of the binder without reducing the bonding strength of the binder, but this often increases the production cost of the vitrified binder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A white corundum vitrified grinding wheel bond added with construction glass waste

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The components of the white corundum ceramic grinding wheel bond with architectural glass waste added in the present invention are weighed and compounded according to the following mass percentages: 26% of potassium feldspar, 12% of clay, and 3% of talc, and the reclaimed architectural glass waste is finely ground Powder 59%.

[0026] Each of the raw materials is in the form of dry powder, with an average particle size d 50 It is 15.8~25.9μm.

[0027] The recycled construction glass waste composition is close to 0.5Na 2 O 0.5CaO SiO 2 , whose main chemical composition mass fraction is SiO 2 70~75%, CaO 8~10%, K 2 O 3~5%, Na 2 O 13~15%.

Embodiment 2

[0029] The various components of the white corundum ceramic grinding wheel bond added with architectural glass waste according to the present invention are weighed and compounded according to the following mass percentages: 28% potassium feldspar, 10% clay, and 4% talc, and the reclaimed architectural glass waste is finely ground Powder 58%.

[0030] Each of the raw materials is in the form of dry powder, with an average particle size d 50 It is 15.8~25.9μm.

[0031] The recycled construction glass waste composition is close to 0.5Na 2 O 0.5CaO SiO 2 , whose main chemical composition mass fraction is SiO 2 70~75%, CaO 8~10%, K 2 O 3~5%, Na 2 O 13~15%.

Embodiment 3

[0033] The components of the white corundum ceramic grinding wheel bond added with building glass waste in the present invention are weighed and compounded according to the following mass percentages: 30% potassium feldspar, 8% clay, 5% talc, and 57% recycled building glass.

[0034] Each of the raw materials is in the form of dry powder, with an average particle size d 50 It is 15.8~25.9μm.

[0035] The recycled construction glass waste composition is close to 0.5Na 2 O 0.5CaO SiO 2 , whose main chemical composition mass fraction is SiO 2 70~75%, CaO 8~10%, K 2 O 3~5%, Na 2 O 13~15%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
flexural strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a white corundum ceramic grinding wheel binder added with architectural glass wastes, and belongs to the technical field of bonded abrasive tool manufacturing. The white corundum ceramic grinding wheel binder is obtained through milling and mixing potassium feldspar, clay, talc and recycled architectural glass wastes according to a certain proportion, wherein all components are subjected to synergistic effect within a limited dosage range, so that the sintering temperature and use performance of the ceramic binder are ensured, the maximum sintering temperature does not exceed 1260 DEG C, and the white corundum ceramic grinding wheel binder is suitable for manufacturing ceramic grinding wheels by using milled white corundum. The white corundum ceramic grinding wheel binder is good in wettability to milled white corundum, strong in holding force, and good in abrasive tool self-sharpening property. The grinding wheel prepared by using the binder is high in rotating strength, has a use line viscosity of 63 m / s or more, and high in durability; a workpiece has no burn cracks; the recycled architectural glass wastes are milled and used for preparing the white corundum ceramic grinding wheel binder, so as to reduce the cost of raw materials of the binder and reduce non-renewable mineral resources.

Description

technical field [0001] The invention belongs to the technical field of bonded abrasive tool manufacturing, and in particular relates to a white corundum ceramic grinding wheel bond added with construction glass waste and a preparation method thereof. Background technique [0002] Grinding wheel is an important tool for mechanical processing. Vitrified grinding wheel is an abrasive tool made by combining loose and barren granular abrasives at high temperature with a vitrified bond. Vitrified grinding wheels have the advantages of high grinding efficiency, high processing precision, and low cost. Vitrified bond is the key raw material for preparing vitrified grinding wheels. Under the premise that the abrasive has been determined, the performance of the bond such as temperature and bonding strength determines the grinding wheel. The safe use performance and firing temperature. The safe use requirements of grinding wheel products in use stipulate that the insurance factor is a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B24D3/14
CPCB24D3/14
Inventor 王学涛杨雪峰李涛边华英尹青亚
Owner 白鸽磨料磨具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com