Inorganic particle enhanced PTT/TPEE composite material

A technology of inorganic particles and composite materials, which is applied in the field of polymer materials, can solve problems such as low strength, poor thermal stability, and poor anti-aging performance, and achieve good anti-aging performance, easy promotion, and excellent mechanical properties. Effect

Inactive Publication Date:
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polytrimethylene terephthalate (PTT), as a new type of polyester polymer material with excellent comprehensive properties, has been widely used in the fields of fibers, films, engineering plastics, etc., but PTT alone has low strength and thermal stability. Not good, the problem of poor anti-aging performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] An inorganic particle-reinforced PTT / TPEE composite material, whose components are proportioned by mass percentage: PTT 60%, TPEE 20%, polyisobutylene adipate 3%, inorganic particles 15%, light stabilizer 1% , 0.1% aluminum-titanium composite coupling agent, 0.3% antioxidant, 0.6% pentaerythritol stearate, the PTT is polytrimethylene terephthalate, the TPEE is thermoplastic polyether fat, and the inorganic The particles are heavy calcium carbonate with a particle size between 10nm and 20μm, and the light stabilizer is a compound of hindered amine high molecular weight light stabilizer GW-944Z and GW-622 with a mass ratio of 1:1. The antioxidant is a compound of hindered phenol antioxidant 1076 and phosphite antioxidant 168 with a mass ratio of 1:1.

[0021] Preparation method: (1), put PTT in a forced air circulation oven and dry at 110°C-120°C for about 6-8 hours, dry the inorganic particles at 80°C-120°C for 30-45 minutes, and set aside; ( 2) Weigh the dry inorganic ...

Embodiment 2

[0023] An inorganic particle-reinforced PTT / TPEE composite material, whose components are proportioned by mass percentage: PTT 74%, TPEE 15%, polyisobutylene adipate 2%, inorganic particles 8%, light stabilizer 0.5% , titanate coupling agent 0.1%, antioxidant 0.1%, modified ethylene bis stearamide 0.3%, the PTT is polytrimethylene terephthalate, and the TPEE is thermoplastic polyether fat, The inorganic particles are magnesium hydroxide with a particle size between 10nm and 20μm, and the light stabilizer is a compound of hindered amine high molecular weight light stabilizer GW-944Z and GW-622 with a mass ratio of 1:1. The antioxidant is a compound of hindered phenol antioxidant 1076 and phosphite antioxidant 168 at a mass ratio of 1:1.

[0024] Preparation method: (1), put PTT in a forced air circulation oven and dry at 110°C-120°C for about 6-8 hours, dry the inorganic particles at 80°C-120°C for 30-45 minutes, and set aside; ( 2) Weigh the dry inorganic particles and titana...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an inorganic particle enhanced PTT/TPEE composite material. The composite material comprises the following ingredients, by weight, 50%-85% of PTT, 5%-25% of TPEE, 2%-5% of poly(diisobutyl adipate), 5%-25% of inorganic particles, 0.5%-2% of light stabilizing agents, 0.1%-0.5% of coupling agents, 0.1%-0.5% of anti-oxidants and 0.1%-1% of lubricants. The inorganic particles are one selected from heavy calcium carbonate, fumed silica, talcum powder, calcium oxide, aluminium hydroxide and magnesium hydroxide. The beneficial effects are that the composite material has excellent mechanical properties, heat resistance and corrosion resistance, the ageing resistance is good, the preparation technology is simple, the production cost is low, and popularization is easy.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an inorganic particle reinforced PTT / TPEE composite material. Background technique [0002] Polytrimethylene terephthalate (PTT), as a new type of polyester polymer material with excellent comprehensive properties, has been widely used in the fields of fibers, films, engineering plastics, etc., but PTT alone has low strength and thermal stability. Not good, the anti-aging performance is not strong. Polyether ester (TPEE) is polybutylene terephthalate-polyethylene oxide-polypropylene oxide thermoplastic elastomer, which is composed of dimethyl terephthalate, butylene glycol, polyethylene oxide two A block copolymer obtained by polycondensation of polyalcohols and / or polypropylene oxide diols, which has the elasticity of rubber and the strength of engineering plastics, and will have better processability and longer service life than rubber , Compared with engineering ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08K13/06C08K9/04C08K3/26C08K3/36C08K3/34C08K3/22
Inventor 不公告发明人
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap