Method for rolling nickel interlayer titanium steel composite board through large rolling reduction

A technology with a large reduction and an intermediate layer, applied in the direction of metal rolling, etc., can solve the problem that the quality of the titanium steel clad plate cannot be well guaranteed, cannot prevent the mutual diffusion of elements, and the coating metal does not have good ductility, etc. problem, to achieve the effect of improving the interface bonding effect, the bonding effect is good, and the plate shape is good.

Inactive Publication Date: 2015-08-12
PANGANG GROUP RESEARCH INSTITUTE CO LTD
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method can improve the bonding strength of the interface to a certain extent. However, due to the thin coating, elements such as titanium and iron can penetrate the coating under high temperature or long-term heating conditions and form brittle compounds at the interface, which cannot prevent the interdiffusion of elements. At the same time, due to the lack of good ductility of the coating metal, the problem of uneven interface state will be caused during the rolling process, resulting in the quality of the titanium-steel clad plate prepared by this method cannot be well guaranteed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Prepare the titanium-steel composite plate according to the following method:

[0043]a. Blank assembly: ①Two steel plates with a processing size of 200×160×18mm, one titanium plate with a size of 160×120×20mm, two side plates with a size of 120×20×20mm and 200×20×20mm, respectively. The surface is ground and polished to remove the surface dirt and oxide layer; the nickel foil with a thickness of 0.5mm is processed into the size of a titanium plate; seamless carbon steel pipe; ③Then carry out symmetrical blank assembly in the order of steel plate / titanium plate / nickel foil / steel plate, apply release agent on the adjacent surface of steel plate and titanium plate, set the side plates around the titanium plate, and Between the two steel plates, argon arc welding is used to weld the gap between the steel plate and the side plate and the gap between the side plate and the side plate, so that all materials become a combination; ④ After welding, pass through the seamless carb...

Embodiment 2

[0050] Prepare the titanium-steel composite plate according to the following method:

[0051] a. Blank assembly: processing steel plates and titanium plates with dimensions of 200×160×18mm and 160×120×20mm respectively, grinding and polishing the surface to remove surface dirt and oxide layer, and nickel with a thickness of 0.5mm The foil is processed to the size of the titanium plate, and then the adjacent surface of the steel plate and the titanium plate is coated with a release agent, and the billets are assembled symmetrically in the order of steel plate / titanium plate / nickel foil / steel plate, and then the four sides of the blank are welded together, and the inside of the blank is pumped Vacuum treatment, the vacuum degree reaches 1×10 -2 Pa, to obtain the combined blank;

[0052] b. Heating: Put the combined billet into the heating furnace for heating, the heating temperature is 1000°C, and the heat preservation is 120min;

[0053] c. Rolling: Take out the combined bill...

Embodiment 3

[0057] Prepare the titanium-steel composite plate according to the following method:

[0058] a. Blank assembly: processing steel plates and titanium plates with dimensions of 200×160×18mm and 160×120×20mm respectively, grinding and polishing the surface to remove surface dirt and oxide layer, and nickel with a thickness of 0.5mm The foil is processed to the size of the titanium plate, and then the adjacent surface of the steel plate and the titanium plate is coated with a release agent, and the billets are assembled symmetrically in the order of steel plate / titanium plate / nickel foil / steel plate, and then the four sides of the blank are welded together, and the inside of the blank is pumped Vacuum treatment, the vacuum degree reaches 1×10 -2 Pa, to obtain the combined blank;

[0059] b. Heating: Put the combined billet into the heating furnace for heating, the heating temperature is 940°C, and the heat preservation is 360min;

[0060] c. Rolling: Take out the combined bille...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of titanium steel composite board preparation and machining, in particular to a method for rolling a nickel interlayer titanium steel composite board through the large rolling reduction. According to the technical scheme, the method includes the following steps that symmetric assembling is conducted according to the steel plate / titanium plate / nickel foil / steel plate sequence, the periphery of a blank is welded, the interior of the blank is vacuumized, and then a combined blank is acquired; the combined blank is heated for 120 min to 360 min, wherein the heating temperature ranges from 940 DEG C to 1000 DEG C; the heated combined blank is rolled, and then the titanium steel composite board is obtained. The titanium steel composite board obtained through the method is good in plate cut, no significant defect is formed on the surface, no titanium / iron compound is generated on a bonding interface, the bonding effect is good, and the bonding strength is larger than 230 MPa and is far larger than that of similar titanium steel composite board in the national standard.

Description

technical field [0001] The invention relates to the field of preparation and processing of a titanium-steel composite plate, in particular to a method for rolling a nickel-interlayer titanium-steel composite plate with a large reduction. Background technique [0002] Titanium has good physical, chemical and mechanical properties, but its smelting technology is complicated and the production cost is high, so the price of titanium is very expensive, which greatly limits the promotion and application of titanium. Combining titanium with other metals (such as steel, copper, aluminum, etc.) -Steel composite materials are widely used in chemical, petroleum and other industrial sectors because of their high strength, excellent corrosion resistance and significant economic benefits. [0003] The existing manufacturing methods of clad steel plates include: filling metal ingot rolling method, explosive cladding method, rolling and crimping method, surfacing welding method and the lik...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21B1/38
CPCB21B1/38B21B2001/386
Inventor 杨柳李军彭琳栾佰峰于辉王莹
Owner PANGANG GROUP RESEARCH INSTITUTE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com