Polyurethane waterproof flame-retardant paint and preparation method thereof

A polyurethane waterproof and flame-retardant coating technology, which is applied in polyurea/polyurethane coatings, fire-resistant coatings, reflection/signal coatings, etc., can solve the problems that are not very mature, and achieve the effect of improving gloss, increasing filler content, and bright color

Inactive Publication Date: 2015-07-01
GUANGXI JIKUAN SOLAR ENERGY EQUIP +1
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, there is no mature technology to prepare a coating that is flame-retardant, lightweight, waterproof, environmentally friendly, not easy to age, and long-lasting. Therefore, people are still constantly researching and testing water-based coatings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyurethane waterproof flame-retardant paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] First, 45 parts of polyurethane prepolymer; 2 parts of diacetone acrylamide; 4 parts of butyl stearate; 0.7 parts of titanate coupling agent TMC-3110.7 parts; 15 parts of rutile titanium dioxide; 0.2 parts of siloxane; 7 parts of white carbon black; 13 parts of mixed solvent (propylene glycol methyl ether and water, the weight ratio is 2:8); flame retardant materials (antimony trioxide, nano-zinc borate and xylyl phosphate by weight Ratio 1:1:1) 5 parts; leveling agent cellulose acetate butyrate is 3 parts by weight for material preparation.

[0042] The production method is to add 1.5 kg of ethanol with a volume concentration of 65 to 80% per kg of diacetone acrylamide to dissolve, and then mix it with polyurethane prepolymer in a reaction kettle. The reaction temperature is 75 ° C, and the reaction time is 1.2 hours. Ester coupling agent TMC-311; continue to react for 3 hours, then add butyl stearate, rutile titanium dioxide, polydimethylsiloxane, flame retardant mate...

Embodiment 2

[0044] First, 50 parts of polyurethane prepolymer; 2.5 parts of diacetone acrylamide; 5 parts of butyl stearate; 1.0 parts of titanate coupling agent TMC-3111; 20 parts of rutile titanium dioxide; 0.3 parts of siloxane; 10 parts of white carbon black; 15 parts of mixed solvent (propylene glycol methyl ether and water, the weight ratio is 2:8); flame retardant materials (antimony trioxide, nano-zinc borate, melamine by weight Ratio 1:1:1) 9 parts; antifreeze benzyl alcohol 5 parts, for material preparation.

[0045] The production method is to add 1.5 kg of ethanol with a volume concentration of 65 to 80% per kg of diacetone acrylamide to dissolve, and then mix it with polyurethane prepolymer in a reaction kettle. The reaction temperature is 95 ° C, and the reaction time is 1.3 hours. Ester coupling agent TMC-311; continue to react for 4 hours, then add butyl stearate, rutile titanium dioxide, polydimethylsiloxane, flame retardant materials, white carbon black, antifreeze and m...

Embodiment 3

[0047] First, 55 parts of polyurethane prepolymer; 3 parts of diacetone acrylamide; 6 parts of butyl stearate; 1.2 parts of titanate coupling agent TMC-3111.2 parts; 22 parts of rutile titanium dioxide; 0.4 parts of siloxane; 12 parts of white carbon black; 17 parts of mixed solvent (propylene glycol methyl ether and water, the weight ratio is 2:8); flame retardant materials (nanometer zinc borate, xylyl phosphate, melamine by weight Ratio 1:1:1) 10 parts; anti-settling agent polyolefin ester 6 parts, for material preparation.

[0048] The production method is to add 1.5 kg of ethanol with a volume concentration of 65-80% per kg of diacetone acrylamide to dissolve, and then mix it with polyurethane prepolymer in a reaction kettle. The reaction temperature is 119 ° C, and the reaction time is 1.5 hours. Ester coupling agent TMC-311; continue to react for 6 hours; then add butyl stearate, redstone titanium dioxide; polydimethylsiloxane, flame retardant material, white carbon bla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyurethane waterproof flame-retardant paint and a preparation method thereof. The paint comprises polyurethane prepolymers, diacetone acryloamide, buty stearate, titanate coupling agent TMC-311 and titanium pigment. The paint further comprises polydimethyl siloxane, white carbon black, mixed solvent and flame-retardant materials. The preparation method comprises the following steps: dissolving the diacetone acrylamide by ethanol of which the volume concentration is 65-80%, wherein the adding amount of the ethanol is 1.5 kilograms in per kilogram of diacetone acrylamide on the basis of weight; mixing the dissolved diacetone acrylamide with the polyurethane prepolymers in a reaction kettle, wherein the reaction temperature is 75-119 DEG C and the reaction time is 1.2-1.5 hours; adding the titanate coupling agent TMC-311 into the mixture and further reacting for 3-6 hours; then adding buty stearate, the rutile-type titanium pigment, polydimethyl siloxane, the flame-retardant materials, the white carbon black and the mixed solvent into the mixture and uniformly mixing, so that the polyurethane waterproof flame-retardant paint product is obtained. The paint prepared by the preparation method is good in waterproof and flame-retardant effects, friendly to the environment and not easy to age.

Description

technical field [0001] The invention relates to a flame-retardant coating, in particular to a polyurethane waterproof flame-retardant coating and a preparation method thereof. Background technique [0002] With the development of the construction industry, the demand for coatings is increasing day by day. Paint is a material that can be coated on the surface of an object by different construction techniques to form a solid film with firm adhesion, certain strength, and continuity. . Objects are exposed to the atmosphere and are corroded by oxygen, moisture, etc., which are likely to cause damage such as metal corrosion, wood decay, and cement weathering. Applying paint to the surface of the object forms a protective film, which can prevent or delay these damages. Occurrence and development can extend the service life of various materials. [0003] Polyurethane coating is an important architectural coating and can also be used as industrial coating. It is a new type of mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D5/18C09D5/33C09D7/12C09D7/00
CPCC09D175/14C08L2201/02C08L2205/03C09D5/18C09D7/20C09D7/61C09D7/63C08L83/04C08L1/12C08K13/02C08K3/36C08K2003/2241C08K3/2279C08K2003/387C08K5/523C08K5/06C08K5/34922C08K5/05
Inventor 谢刚杨明慧马昭键李珠肖
Owner GUANGXI JIKUAN SOLAR ENERGY EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com