Colored special-shaped size-stabilized type polyester monofilament and preparation method thereof

A dimensionally stable polyester monofilament technology, applied in the fiber field, can solve the problems that have not been found in the reports of barium sulfate, monofilament special-shaping, and fiber preparation, etc., so that the creep and relaxation phenomenon is small, and the fabric is improved. Dimensional uniformity, effect of filament surface cleanliness

Inactive Publication Date: 2015-04-22
ZHEJIANG JINXIA NEW MATERIAL TECH CO LTD +1
View PDF14 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN102660018A and Chinese patent CN202968797U both announced the application of this material in fibers to improve the heat resistance or barrier properties of fibers, but did not involve its blending with PET to prepare colored special-shaped fibers
Chinese patent CN1211204C discloses a production method of PET / PEN blended or copolymerized film, but does not involve the preparation of fibers
Chinese patents, but none of them involve the effect of barium sulfate on the properties of PET / PEN fibers
Although there are a large number of reports on fiber specialization, there is no report on monofilament specialization.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The spun chip consists of 91.8 parts of polyethylene terephthalate (PET) spun chip, and Jinshan Petrochemical provides a molecular weight of 20,000. 5 parts of color masterbatch and 3 parts of polyethylene 2,6-diethyl naphthalate (PEN) chip (DuPont PEN Q3000) and 0.2 parts of barium sulfate powder (Yufeng Powder Material Co., Ltd. ultrafine barium sulfate YF-10000), cut and prepared after screw blending, and the slices prepared by blending were placed in a VC358 rotating pot, first Vacuum to within 30 Pa, then heat to 120°C for 8 hours for drying and dehydration, keep the water content below 35PPM for 8 hours; masterbatch (Lihe Chemical Fiber Plastic Factory T1714), gradually heat to 120°C at a constant speed for 8 hours ℃ for drying and dehydration, heat preservation for 8 hours, the water content is below 35PPM, the drying process is a well-known technology in the industry. Using VC406 spinning machine, polyester chips and color masterbatch are extruded, blended and m...

Embodiment 2

[0029] Spinning chip is made of 97.5 parts of polyethylene terephthalate (PET) spinning chip, Jinshan Petrochemical provides masterbatch with molecular weight of 20,000, Lihe Chemical Fiber Plastic Factory T1173, 2 parts, 0 parts of poly-2,6-naphthalene dicarboxylic acid Diethyl ester (PEN) slices and 0.5 parts of barium sulfate powder, Yufeng Powder Material Co., Ltd. ultrafine barium sulfate YF-10000), were prepared by cutting after screw blending, and polyethylene terephthalate (PET ) The spun chips are heated to 120°C for 8 hours for drying and dehydration, and the water content is kept below 35PPM for 8 hours; the color masterbatch is heated for 8 hours to 140°C for drying and dehydration, and the heat preservation is for 8 hours. The water content is below 35PPM; the polyester chip and the color masterbatch are extruded, blended and melted by a screw machine to form a melt, and then spun through the spinneret assembly, and the extrusion temperature of the screw machine is...

Embodiment 3

[0031] The spun chip is made of 88 parts of polyethylene terephthalate (PET) spun chip, Jinshan Petrochemical provides a molecular weight of 20,000. 3 parts of color masterbatch, Lihe Chemical Fiber Plastic Factory T1614. 8 parts of polyethylene 2,6-diethyl naphthalate (PEN) chips, DuPont PEN Q3000, and 1 part of barium sulfate powder, Yufeng Powder Material Co., Ltd. Ultra-fine barium sulfate YF-10000, prepared by cutting after screw blending, heating the blended slices to 120-160°C for 8-12 hours for drying and dehydration, keeping the water content below 35PPM for 8-10 hours; color The master batch is heated to 120-160°C for drying and dehydration in 8-12 hours, and kept for 8-10 hours. The water content is below 35PPM; the polyester chip and the color masterbatch are extruded, blended and melted by a screw machine to make a melt, and then spun through the spinneret assembly, and the extrusion temperature of the screw machine is: 280°C in the first zone, The second zone is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water contentaaaaaaaaaa
elongationaaaaaaaaaa
shrinkageaaaaaaaaaa
Login to View More

Abstract

The invention relates to a colored special-shaped size-stabilized type polyester monofilament and a preparation method thereof. The colored special-shaped size-stabilized type polyester monofilament is composed of, by weight, 84.5 parts to 99.75 parts of polyethylene terephthalate (PET), 0.2 part to 5 parts of color master batches, 0.1 part to 10 parts of poly(ethylene 2,6-naphthalate) (PEN) and 0.05 part to 1 part of barium sulfate powder. By adding the PEN, the thermal resistance of fiber is improved, and no roller sticking phenomenon can occur even when the heat setting temperature is above 245 DEG C; nanometer barium sulfate plays a role of plasticizer, the slippage among high polymers is improved, the drawing ratio is increased, the fiber contraction rate is decreased, and meanwhile the colored fiber can be more uniform and brighter in color and luster; the high drawing ratio is achieved in the fiber drawing process, induced crystallization produced in the fiber drawing process is improved, and the boiling water shrinkage is decreased; the fiber preparing process is simple, dry strands are uniform, fiber is uniform in thickness, woven fabric is smooth, grids are exquisite and uniform, and a colored special-shaped filament is softer and richer in color so that stylized reflection can be facilitated.

Description

【Technical field】 [0001] The invention relates to the field of fiber technology, in particular to a colored special-shaped dimensionally stable polyester monofilament and a preparation method thereof. 【Background technique】 [0002] Low-shrinkage polyester industrial yarn has been widely used in the field of narrow fabrics such as filter cloth, sunshade cloth, tarpaulin and so on. Fabrics woven from traditional low-shrinkage polyester industrial yarns have a large shrinkage rate and uneven shrinkage after coating heat treatment, which can easily cause uneven fabric surfaces, so they can only be used for weaving narrow-width fabrics. In recent years, due to the rapid development of materials such as membrane structures, higher requirements have been put forward for the dimensional stability of fabrics, while ordinary low-shrinkage polyester industrial yarns cannot meet the requirements of wide fabrics with a width of more than 5 meters; etc. have put forward higher requireme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/92D01F1/10D01D13/00D01D5/253
Inventor 张志明陈龙
Owner ZHEJIANG JINXIA NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com