Plastic colored sand and processing technique thereof

A plastic and colored sand technology, which is applied in the field of plastic colored colored sand and processing technology, can solve the problems of high dispersion and high phase melting, limited range of colored sand, calcium carbonate is not acid-resistant, etc., to achieve good coloring power, good Heat resistance, the effect of improving the uniformity of dispersion

Inactive Publication Date: 2015-04-22
孙恩昌
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Plastic colored colored sand is used as a colorant in synthetic materials such as plastics, rubber, paints, and inks. It has high dispersibility and high phase solubility, and has functional characteristics such as small dosage, non-toxic, and dust-free. It is widely used in It is a new type of environmentally friendly functional material in the fields of household appliances, electronics, wire and cable, food packaging, etc. Calcium carbonate is added to the existing color sand formula, but calcium carbonate has the disadvantages of being not resistant to acid and aging, which makes The scope of use of colored sand with this formula is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Provided is a kind of plastic coloring sand, and the ratio of the parts of each component is: masterbatch pigment 30; low molecular weight polyethylene 20; nanometer BaSO410; titanium dioxide 30.

[0009] Due to the poor dispersibility of titanium dioxide, the surface of titanium dioxide is generally treated with an organic treatment agent. The organic treatment agent generally uses triethanolamine, sorbitol, mannitol, polyethylene glycol, polypropylene glycol, alkyl chlorosilane, Ester compounds, fatty acid compounds, etc.; the processing technology is: put the masterbatch pigment and titanium dioxide in the internal mixer for about 15 minutes, use titanium dioxide and the masterbatch pigment as the base material, add low molecular weight polyethylene to disperse function, add nano-BaSO4 to improve dispersion, pour out after the material is completely melted, cut into 10-20 cm blocks, cool under natural conditions, put them into a pulverizer for crushing, and then put t...

Embodiment 2

[0010] Embodiment 2: Provide a plastic colored colored sand, the ratio of the parts of each component is: 40 masterbatch pigments; 20 low molecular weight polyethylene; nanometer BaSO410; titanium dioxide 20.

[0011] Due to the poor dispersibility of titanium dioxide, the surface of titanium dioxide is generally treated with an organic treatment agent. The organic treatment agent generally uses triethanolamine, sorbitol, mannitol, polyethylene glycol, polypropylene glycol, alkyl chlorosilane, Ester compounds, fatty acid compounds, etc.; the processing technology is: put the masterbatch pigment and titanium dioxide in the internal mixer for about 15 minutes, use titanium dioxide and the masterbatch pigment as the base material, add low molecular weight polyethylene to disperse function, add nano-BaSO4 to improve dispersion, pour out after the material is completely melted, cut into 10-20 cm blocks, cool under natural conditions, put them into a pulverizer for crushing, and then...

Embodiment 3

[0012] Embodiment 3: Provide a plastic colored colored sand, the ratio of the parts of each component is: 20 masterbatch pigments; 10 low molecular weight polyethylene; nanometer BaSO420; titanium dioxide 50.

[0013] Due to the poor dispersibility of titanium dioxide, the surface of titanium dioxide is generally treated with an organic treatment agent. The organic treatment agent generally uses triethanolamine, sorbitol, mannitol, polyethylene glycol, polypropylene glycol, alkyl chlorosilane, Ester compounds, fatty acid compounds, etc.; the processing technology is: put the masterbatch pigment and titanium dioxide in the internal mixer for about 15 minutes, use titanium dioxide and the masterbatch pigment as the base material, add low molecular weight polyethylene to disperse function, then add nano BaSO4 to improve dispersion, pour out after the material is completely melted, cut into 10-20 cm blocks, cool under natural conditions, put them into a pulverizer for crushing, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a plastic colored sand and a processing technique thereof. The plastic colored sand is prepared from 20-30 parts of color master batch pigment, 20-30 parts of low-molecular weight polyethylene, 10-20 parts of nano BaSO4 and 30-50 parts of titanium dioxide. The processing technique comprises the following steps: by using the titanium dioxide and carbon black as base materials, adding the low-molecular weight polyethylene to perform dispersion function, adding the nano BaSO4 to improve the dispersity, banburying, cooling, pulverizing and milling to obtain the product. The plastic colored sand has the advantages of favorable coloring power, favorable dispersity, no pollution and the like, is convenient for measurement, does not change the physical properties of the plastic, and can be widely used in plastics, rubber, chemical fibers, wire cables and other industries.

Description

technical field [0001] The invention relates to a pigment dye, in particular to a plastic colored sand and a processing technology. Background technique [0002] Plastic colored colored sand is used as a colorant in synthetic materials such as plastics, rubber, paints, and inks. It has high dispersibility and high phase solubility, and has functional characteristics such as small dosage, non-toxic, and dust-free. It is widely used in It is a new type of environmentally friendly functional material in the fields of household appliances, electronics, wire and cable, food packaging, etc. Calcium carbonate is added to the existing color sand formula, but calcium carbonate has the disadvantages of being not resistant to acid and aging, which makes The range of use of colored sand with this formula is limited. Contents of the invention [0003] The object of the present invention is to provide a kind of plastic colored colored sand with high dispersibility and high phase meltin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08K9/04C08K3/22C08K3/30C08J3/20
CPCC08K9/04C08K3/22C08K3/30C08K2003/2237C08K2003/3045
Inventor 孙恩昌
Owner 孙恩昌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap