Production process of basalt gridding cloth

A kind of basalt mesh cloth, the technology of production process, applied in the direction of textile, fabric, leno fabric, etc., can solve the problems of low strength, poor alkali resistance and flexibility, etc., achieve high modulus, improve hand feeling and flexibility, size good stability effect

Active Publication Date: 2015-02-11
HONGXIANG NEW GEO MATERIAL
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a production process of basalt mesh cloth to solve the problems of low strength, poor alkali resistance and poor flexibility existing in the existing mesh cloth

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] A kind of basalt grid cloth, which is made of basalt fiber woven fabric, soaked in acrylic acid polymer latex, coated with leno weaving, and then treated with alkali-resistant penetrating agent and high-temperature heat-setting treatment of reinforcing agent. into, the specific process steps are as follows:

[0013] (1) Soak the basalt fiber woven fabric into the acrylic acid polymer emulsion in the bubbling mixing tank, the soaking time is controlled at 20-60 minutes, the temperature is controlled above 30°C, and the gas is bubbling and mixed at the same time;

[0014] (2) After the basalt fiber is taken out and dried, the basalt fiber is twisted according to the leno structure to form a warp layer and a weft layer;

[0015] (3) hot pressing at high temperature, so that the warp yarn layer and the weft yarn layer are hot-pressed and welded to obtain the basalt mesh cloth;

[0016] (4) Soak the basalt mesh cloth in the alkali-resistant penetrating agent, then soak it i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
service temperatureaaaaaaaaaa
limiting oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production process of basalt gridding cloth. The basalt gridding cloth is prepared by adopting fiber woven fabrics of basalt as base materials, soaking in acrylic polymer emulsion for coating, carrying out twist-weaving of gauze weaves, and then carrying out alkali-resistant treatment with an alkali-resistant penetrating agent and high-temperature heat setting treatment with an enhancing agent. The production process is characterized in that the fiber woven fabrics of the basalt are adopted as base materials and are soaked by the acrylic polymer emulsion, so that the alkali resistance, the flexibility and the tensile strength of the warp-direction and weft-direction heights are good; and then the alkali-resistant treatment with the alkali-resistant penetrating agent and high-temperature heat setting treatment with the enhancing agent are carried out, and finally, by amino silicon oil, the handfeel and the flexibility of a product are greatly improved. The basalt gridding cloth is good in chemical stability, resists alkali, acid, water, cement erosion and other chemical corrosion, is strong in bonding property with resin, is easily dissolved in styrene and the like, is high in strength and modulus and light in weight, is good in size stability, is stiff and flat, is not easily shrunk and deformed, is excellent in positioning performance and better in impact resistance, is anti-mildew and insect-resistant, and is fireproof, heat-insulating, sound-insulating and insulated.

Description

technical field [0001] The invention relates to the technical field of production of thermal insulation and waterproof materials for buildings, in particular to a production process of basalt grid cloth. Background technique [0002] Basalt fiber has superior physical and chemical properties, and its characteristics are: (1) permanent flame retardancy: limiting oxygen index (LOI) > 70; (2) ultra-high softening temperature: > 1200 ° C; (3) extremely high Operating temperature: >880°C; (4) extremely low operating temperature: <-260°C; (5) high breaking strength: 4500MPa; (6) low elongation at break: 3.1%; (7) high elasticity Modulus: 1x104kg / mm2; (8) Material density: 2.7g / cm3; (9) Low thermal conductivity: 0.035W / m K; (10) High sound absorption coefficient: 0.95; (11) Low moisture absorption : 0.1%; (12) High specific volume resistance: 1x1012Ω·m; (13) Radiation-proof lead equivalent: 0.0073mmPb. . [0003] Mesh cloth has the characteristics of good chemical st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/263D06M15/423D06M15/643D03D19/00D06N7/06
Inventor 崔占明孟灵晋
Owner HONGXIANG NEW GEO MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com