A kind of mullite nano-whisker prepared from pyrite tailings as raw material and preparation method thereof

A technology of pyrite tailings and nano-whiskers, applied in chemical instruments and methods, single crystal growth, crystal growth, etc., can solve the problems of low added value, high energy consumption, high cost, etc., and achieve high added value and calcination temperature The effect of low cost and low raw material cost

Inactive Publication Date: 2017-06-06
CHENGDU UNIVERSITY OF TECHNOLOGY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although there have been a large number of reports on the reuse of pyrite tailings, the existing utilization methods generally produce products with low added value, high energy consumption and high cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of mullite nano-whisker prepared from pyrite tailings as raw material and preparation method thereof
  • A kind of mullite nano-whisker prepared from pyrite tailings as raw material and preparation method thereof
  • A kind of mullite nano-whisker prepared from pyrite tailings as raw material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The pyrite tailings used are taken from the flotation tank of a small-scale heavy flotation joint election of an enterprise in southern Sichuan, and its chemical composition weight percentage is: SiO 2 38.41%, A1 2 o 3 32.40%, CaO 3.02%, TiO 2 4.01%, MgO 0.76%, Fe 2 o 3 5.91%, Na 2 O 0.16%, K 2 O 0.35%, SO 3 0.92%, loss on ignition 14.30%, and the balance is other trace components. The process steps of using the pyrite tailings to prepare mullite whiskers are as follows:

[0039] (1) Ball mill the pyrite tailings at a speed of 400 rpm to a 50-mesh sieve, dehydrate, dry, and grind until passing through a 200-mesh sieve;

[0040] (2) Weigh 50g of pyrite tailings and 170ml of a mixed solution of 25% hydrochloric acid and 25% sulfuric acid with a volume ratio of 1:1, stir in a constant temperature water bath at 60°C for 1 hour, and dehydrate and dry by centrifugation , grinding;

[0041] (3) Calcining the acid-washed pyrite tailings at 400°C for 2 hours to obtai...

Embodiment 2

[0049] The pyrite tailings used are taken from the flotation tank of a small-scale heavy flotation joint election of an enterprise in southern Sichuan, and its chemical composition weight percentage is: SiO 2 38.41%, A1 2 o 3 32.40%, CaO 3.02%, TiO 2 4.01%, MgO 0.76%, Fe 2 o 3 5.91%, Na 2 O 0.16%, K 2 O 0.35%, SO 3 0.92%, loss on ignition 14.30%, and the balance is other trace components. The process steps of using the pyrite tailings to prepare mullite whiskers are as follows:

[0050] (1) Ball mill the pyrite tailings at a speed of 400 rpm to a 50-mesh sieve, dehydrate, dry, and grind until passing through a 200-mesh sieve;

[0051] (2) Weigh 50g of pyrite tailings and 170ml of a mixed solution of 30% hydrochloric acid and 30% sulfuric acid with a volume ratio of 1:1, stir in a constant temperature water bath at 60°C for 1 hour, and centrifuge, dry, and grind ;

[0052] (3) Calcining the acid-washed pyrite tailings at 400°C for 2 hours to obtain composition-adj...

Embodiment 3

[0060] The pyrite tailings used are taken from the flotation tank of a small-scale heavy flotation joint election of an enterprise in southern Sichuan, and its chemical composition weight percentage is: SiO 2 36.99%, A1 2 o 3 30.67%, CaO 3.33%, TiO 2 3.86%, MgO 0.75%, Fe 2 o 3 6.91%, Na 2 O 0.16%, K 2 O 0.36%, SO 3 2.89%, loss on ignition 13.56%, and the balance is other trace components. The process steps of using the pyrite tailings to prepare mullite whiskers are as follows:

[0061] (1) Ball mill the pyrite tailings at a speed of 400 rpm to a 50-mesh sieve, dehydrate, dry, and grind until passing through a 200-mesh sieve;

[0062] (2) Weigh 50g of pyrite tailings and 170ml of a mixed solution of 25% hydrochloric acid and 25% sulfuric acid with a volume ratio of 1:1, stir in a constant temperature water bath at 65°C for 1.5 hours, and centrifuge, dry, and grind ;

[0063] (3) Calcining the acid-washed pyrite tailings at 400°C for 2 hours to obtain composition-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
aspect ratioaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a mullite nano-whisker by using pyrite tailing as a raw material, and belongs to the field of nano-whisker preparation and mineral resource recycling. The method comprises the following steps: preparing the raw material, pickling for removing iron, calcinating for removing C, S and organic matters, preparing a precursor, and performing calcination and acid soaking for removing a glass phase. According to the invention, the prepared nanoscale mullite whisker has good quality, has excellent properties of both the mullite whisker and the nano-whisker, and has a high additional value and a remarkable economic benefit; in addition, the adopted raw material pyrite tailing is waste mineral materials after mineral dressing, so that the products are low in cost of raw materials, and the secondary recycling of pyrite resources is achieved; meanwhile, compared with other preparation methods, the preparation process of the invention requires lower calcination temperature and shorter calcination time, so that reduction of energy consumption is facilitated, thereby reducing production cost and resource consumption, and increasing economic benefits.

Description

technical field [0001] The invention relates to the fields of preparation of nano-whiskers and recycling of mineral resources, in particular to a mullite nano-whisker prepared from pyrite tailings as a raw material and a method thereof. Background technique [0002] Whisker is a single crystal fiber with excellent corrosion resistance, high strength, high hardness, good mechanical strength, high elastic modulus and other characteristics. Whiskers are usually added to plastics, metals, ceramics and other materials as modified reinforcing materials, which greatly enhance the physical and chemical properties and excellent mechanical properties of raw materials. As a kind of whisker, mullite whisker has the properties of anti-oxidation, high temperature resistance, wear resistance, small thermal expansion coefficient, high temperature strength, good thermal shock resistance and low high temperature creep. Therefore, mullite whiskers have extremely high utilization value as high...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C30B29/62C30B29/10C30B1/00
CPCC30B1/00C30B29/10C30B29/62
Inventor 叶巧明黄欢王明珠董悦罗如意马敏吴娇
Owner CHENGDU UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com