Flame-retardant and anti-rusting anti-adhesion epoxy paint and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of epoxy and paint, applied in the direction of epoxy resin coating, anti-corrosion coating, fire-proof coating, etc., can solve the problem of material waste, achieve the effect of reducing cost, improving flame retardancy and excellent temperature resistance
Inactive Publication Date: 2015-01-21
TIANCHANG YINHU PAINT
View PDF5 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Corrosion of metals not only causes huge material waste, but also causes huge economic losses
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0014] specific implementation plan
[0015] The present invention will be described in detail below through specific examples.
[0016] A flame-retardant and anti-rust anti-sticking epoxy paint, prepared from the following raw materials in parts by weight (kg): E-51 epoxy resin 35, fluorosilicone resin 14, polybutadiene epoxy resin 9, vinyl Triamine 4, Utotropine 2, bis(dioctyloxypyrophosphate) ethylene titanate 0.5, modified asphalt 12, asbestos 3, water glass 1, modified waste clay sand 4, hexachlorocyclocycline Pentadiene 3, p-nitrobenzoic acid 1, calcium monomethyl phosphinate 3, phenylethyl naphthol polyoxyethylene ether 0.6, nanometer calcium carbonate 2, diethylene glycol 6, xylene 8, acetic acid ethyl ester 11;
[0017] The modified asphalt is made from the following raw materials in parts by weight (kg): 40% chlorinated rubber 13, asphalt 93, stearamide 0.3, azobisisobutyronitrile 0.2, octabromodiphenyl ether 0.4, water 6. Polyoxyethylene castor oil 0.5, magnesiu...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
adhesivity
aaaaa
aaaaa
wear resistance
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses flame-retardant and anti-rusting anti-adhesion epoxy paint which is characterized by being prepared from the following raw materials in parts by weight: 30-40 parts of E-51 epoxy resin, 12-17 parts of fluorosilicone resin, 8-12 parts of polybutadiene epoxy resin, 3-5 parts of vinyl triamine, 2-3 parts of urotropine, 0.4-0.8 part of bis(P,P-bis-ethylhexyl diphosphato)ethanediolato titanate, 12-15 parts of modified asphalt, 2-4 parts of asbestos, 1-2 parts of sodium silicate, 3-6 parts of modified waste clay sand, 3-4 parts of hexachlorocyclopentadiene, 1-3 parts of p-nitrobenzoic acid, 3-4 parts of single methyl phosphinic acid calcium, 0.5-1.0 part of phenethyl naphthol polyoxyethylene ether, 2-4 parts of nano calcium carbonate, 5-7 parts of diethylene glycol, 7-9 parts of xylene and 9-13 parts of acetic ether. The fluorosilicone resin added into the paint disclosed by the invention is excellent in temperature resistance, adhesion prevention, chemical resistance, antifouling property and rain corrosion resistance; the mutual synergistic effects of pentaerythritol phosphate, single methyl phosphinic acid calcium and hexachlorocyclopentadiene added into the paint are brought into play, so that the flame retardancy of the paint is improved; as the waste clay sand is modified and added into the paint, both the cost of the paint is lowered, the weather resistance and corrosion resistance of the paint are improved, and the environment pollution is also alleviated.
Description
technical field [0001] The invention relates to a paint and a preparation method thereof, in particular to a flame-retardant and anti-rust anti-adhesive epoxy paint and a preparation method thereof. Background technique [0002] According to statistics, the direct economic loss caused by metal corrosion accounts for about 4% of the gross national product in my country every year. Corrosion of metals not only causes huge material waste, but also causes huge economic losses. Therefore, the corrosion protection of metals has attracted more and more attention. Paint is widely used in all kinds of construction projects and decoration of homes and public places. With the improvement of people's living standards and the use of various electrical appliances, the safety hazard of fire has increased. Therefore, fire-resistant and flame-retardant paints have emerged as the times require. pregnancy. [0003] Clay sand is a molding sand with clay as a binder. During the recycling proc...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.