Cold-resistant and water-proof damping coating

A damping coating and polymer technology, applied in the coating field, can solve the problems that damping coating damping performance, cold resistance and water resistance cannot meet the requirements of society, and achieve good chemical compatibility and stability, wide damping temperature range, The effect of great adhesion

Inactive Publication Date: 2015-01-07
WUHU SHUANGBAO BUILDING MATERIAL
View PDF6 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the improvement of people's living standards and the emphasis on environmental factors, people have higher and higher requirements for sound insulation and noise reduction coatings. The damping performance, cold resistance and water resistance of existing damping coatings cannot meet the requirements of society.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cold-resistant and water-proof damping coating
  • Cold-resistant and water-proof damping coating
  • Cold-resistant and water-proof damping coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019]The cold-resistant and water-resistant polymer damping coating of the present invention, its raw material comprises the following components by weight: 40 parts of water-based polyurethane / polyacrylate emulsion, 16 parts of coupling agent modified sericite, 5 parts of talcum powder, hollow glass microspheres 10 parts, 3 parts of mica powder, 12 parts of perlite, 5 parts of diatomaceous earth, 10 parts of nanometer acrylate rubber powder, 0.3 parts of phosphate modified amine compound, 6 parts of magnesium hydroxide, 5 parts of aluminum hydroxide, glass 10 parts of fiber, 1 part of boron phenolic resin, 5 parts of organic solvent, 2 parts of film-forming aid, 5 parts of auxiliary agent, 20 parts of deionized water;

[0020] Wherein, the phosphate-modified amine complex is prepared according to the following process: 20 parts by weight of phosphoric acid and 20 parts of ethylenediamine are added to the flask, stirred for 20 minutes, heated to 55° C., reacted for 20 minutes,...

Embodiment 2

[0025] The cold-resistant and water-resistant polymer damping coating of the present invention, its raw material comprises the following components by weight: 60 parts of water-based polyurethane / polyacrylate emulsion, 5 parts of coupling agent modified sericite, 15 parts of talcum powder, hollow glass microspheres 3 parts, 8 parts of mica powder, 5 parts of perlite, 17 parts of diatomaceous earth, 4 parts of nanometer acrylate rubber powder, 0.9 parts of phosphate modified amine compound, 3 parts of magnesium hydroxide, 12 parts of aluminum hydroxide, glass 3 parts of fiber, 3 parts of boron phenolic resin, 2 parts of dipropylene glycol, 3 parts of propylene glycol phenyl ether, 4 parts of alcohol ester twelve, 2 parts of additives, 35 parts of deionized water;

[0026] Wherein, the auxiliary agent is a combination of defoamer, thickener, leveling agent, dispersant, and wetting agent in any ratio by weight;

[0027] The phosphate-modified amine complex is prepared according t...

Embodiment 3

[0032] The cold-resistant and water-resistant polymer damping coating of the present invention, its raw material comprises the following components by weight: 51.2 parts of water-based polyurethane / polyacrylate emulsion, 10 parts of coupling agent modified sericite, 13.5 parts of talcum powder, hollow glass microspheres 6.4 parts, 7.8 parts of mica powder, 11.2 parts of perlite, 11.5 parts of diatomaceous earth, 8.7 parts of nanometer acrylate rubber powder, 0.83 parts of phosphate modified amine compound, 5.8 parts of magnesium hydroxide, 10.8 parts of aluminum hydroxide, glass 7 parts of fiber, 2.6 parts of boron phenolic resin, 1.5 parts of 1,4-butanediol, 2.3 parts of pentylene glycol, 5.8 parts of film-forming aid, 3.8 parts of thickener, 30 parts of deionized water;

[0033] Wherein, the film-forming aid is a combination of polyethylene glycol, propylene glycol phenyl ether, alcohol ester dodecane, and ethylene glycol butyl ether in any ratio by weight; the thickener is c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a cold-resistant and water-proof damping coating which is characterized in that raw materials comprise the following components in parts by weight: 40-60 parts of waterborne polyurethane / polyacrylate latex, 5-16 parts of sericite modified by a coupling agent, 5-15 parts of talcum powder, 3-10 parts of hollow glass beads, 3-8 parts of mica powder, 5-12 parts of perlite, 5-17 parts of kieselguhr, 4-10 parts of nanometer acrylate rubber powder, 0.3-0.9 parts ofphosphate modified amine compound, 3-6 parts of magnesium hydroxide, 5-12 parts of aluminium hydroxide, 3-10 parts of glass fibre, 1-3 parts of boron-containing phenolic resin, 2-5 parts of organic solvent, 2-7 parts of a film coalescing aid, 2-5 parts of aids, and 20-30 parts of deionized water. The cold-resistant and water-proof damping coating provided by the invention has good damping performance, cold resistance and water-proof property.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a cold-resistant and water-resistant polymer damping coating. Background technique [0002] Polymer damping coating is a special coating with shock absorption, sound insulation and certain sealing performance made of high molecular polymer as the base material resin. Because of its convenient construction, it can better reflect its superiority especially for the surface with complex structure. At present, it has been widely used in the shock absorption and noise reduction of aircraft, ships, vehicles and various machinery. With the improvement of people's living standards and the emphasis on environmental factors, people have higher and higher requirements for sound insulation and noise reduction coatings. The damping performance, cold resistance and water resistance of existing damping coatings cannot meet the requirements of society. Therefore, how to develop a cold-resistant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/04C09D133/08C09D5/00C09D7/12
CPCC09D175/04C08L2205/025C08L2205/035C09D7/61C09D7/62C09D7/63C09D133/04C08L33/04C08L61/14C08K13/06C08K3/346C08K3/34C08K7/28C08K2003/2224C08K2003/2227C08K7/14C08K5/521C08L75/04
Inventor 胡昌悌
Owner WUHU SHUANGBAO BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com