Metal-imitating ABS modified material and preparation method thereof

A modified material, imitating metal technology, applied in the field of plastic modification, can solve the problems of poor metal effect, weld marks, impact strength drop, etc., to overcome the impact strength drop, eliminate weld marks, and improve the effect of interaction force

Active Publication Date: 2014-12-17
广东波斯科技股份有限公司
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention can overcome the problems of serious welding lines, poor metal effects and decreased impact strength in the prior art, and has wide application prospects in the plastic product industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal-imitating ABS modified material and preparation method thereof
  • Metal-imitating ABS modified material and preparation method thereof
  • Metal-imitating ABS modified material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Weigh and batch according to the following formula: 85 parts of ABS, 5 parts of silver powder, 2 parts of YY-503 coupling lubrication composite modifier, 5 parts of petroleum resin, 2.8 parts of calcium carbonate, and 0.2 part of antioxidant.

[0035] The above components are pre-mixed evenly with a mixer, and then melted and granulated with a twin-screw extruder with a diameter of 40 mm and a length-to-diameter ratio of 36:1. rpm.

[0036] The prepared metal-like ABS modified material was dried at 80°C for 2 hours, and the mechanical sample strip and standard color plate were injected at 200°C by an injection molding machine, and the length of weld line and mechanical properties were measured.

Embodiment 2

[0038] Weighing and ingredients according to the following formula: 82 parts of ABS, 2 parts of gold powder, 0.2 parts of carbon black, 0.3 parts of phthalocyanine blue, 5 parts of YY-503 coupling lubrication composite modifier, 5 parts of petroleum resin, 3 parts of barium sulfate, 2.3 parts of talcum powder, 0.2 part of antioxidant.

[0039] The above components are pre-mixed evenly with a mixer, and then melted and granulated with a twin-screw extruder with a diameter of 40mm and a length-to-diameter ratio of 36:1. rpm.

[0040] The prepared metal-like ABS modified material was dried at 80°C for 2 hours, and the mechanical sample strip and standard color plate were injected at 200°C by an injection molding machine, and the length of weld line and mechanical properties were measured.

Embodiment 3

[0042] Weighing and batching according to the following formula: 76 parts of ABS, 3 parts of pearlescent pigment, 3 parts of silver powder, 0.8 parts of titanium dioxide, 5 parts of YY-503 coupling lubrication composite modifier, 8 parts of petroleum resin, 3.4 parts of talc powder, anti 0.8 parts of oxygen agent.

[0043] The above components are pre-mixed evenly with a mixer, and then melted and granulated with a twin-screw extruder with a diameter of 40mm and a length-to-diameter ratio of 36:1. rpm.

[0044] The prepared metal-like ABS modified material was dried at 80°C for 2 hours, and the mechanical sample strip and standard color plate were injected at 200°C by an injection molding machine, and the length of weld line and mechanical properties were measured.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a metal-imitating ABS modified material. The metal-imitating ABS modified material consists of the following components: 70-95 parts of ABS, 0.5-10 parts of pigments, 1-5 parts of a coupling-lubricating composite modifier, 5-10 parts of a tackifier, 0-10 parts of filler and 0.1-1 part of an antioxidant, wherein the trademark of the coupling-lubricating composite modifier is YY-503, and the number-average molecular weight of the coupling-lubricating composite modifier is 3000-5000; a low melting point of the coupling-lubricating composite modifier is 75 + / - 5 DEG C, and a high melting point of the coupling-lubricating composite modifier is 150 + / - 10 DEG C; the tackifier is C5 petroleum resin with average molecular weight of 1000-2500. The metal-imitating ABS modified material can be used for overcoming the problems that weld marks are severe, the metal effects are not good and the impact strength is declined in the prior art, and has a wide application prospect in the industry of plastic products.

Description

technical field [0001] The invention belongs to the technical field of plastic modification, and in particular relates to a metal imitation ABS modified material and a preparation method thereof. Background technique [0002] Plastic coloring can give plastic parts color and good appearance effect, and it is an indispensable and important link in the plastic processing industry. Compared with metal parts, plastic parts have the advantages of low density, high cost performance and corrosion resistance. [0003] In order to improve the decorative effect of plastic parts, the prior art usually uses electroplating or spraying metal colors on the plastic surface. The plastic surface electroplating process is long and requires multiple steps such as surface cleaning, roughening, electroless plating, electroplating, and water washing. During the production process, more wastewater and waste liquid will be generated, which will seriously pollute the environment. Surface spraying t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L55/02C08L57/02C08K13/02C08K3/08C08K3/26C08K3/04C08K3/34B29C47/92B29C48/92
Inventor 阳范文黎泽顺刘鹏卢俊文
Owner 广东波斯科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap