Magnesium oxide zinc oxide compound vulcanizing agent for chloroprene rubber vulcanization and preparation method thereof

A chloroprene rubber and magnesium oxide technology, which is applied in the field of vulcanizing agents for chloroprene rubber vulcanization, can solve the problems of reducing the influence of scorch properties of rubber compounds, increasing the risk of scorching, and being difficult to disperse, so as to improve dispersibility and reduce scorch. The effect of burning danger and high vulcanization efficiency

Active Publication Date: 2016-08-24
河北镁神科技股份有限公司 +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, active zinc oxide is not easy to disperse in chloroprene rubber, which increases the risk of glue burning; active magnesium oxide is easy to be affected by moisture and CO in the air. 2 Reaction reduces the activity and reduces the impact on the scorch performance of the compound

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnesium oxide zinc oxide compound vulcanizing agent for chloroprene rubber vulcanization and preparation method thereof
  • Magnesium oxide zinc oxide compound vulcanizing agent for chloroprene rubber vulcanization and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] This embodiment relates to a preparation method of a magnesium oxide zinc oxide compound vulcanizing agent for chloroprene rubber vulcanization, the method comprising the following steps:

[0033] a. Take active zinc oxide and active magnesium oxide and mix, and mark it as substance A; pour the dispersant into 30ml of absolute ethanol solution and stir, and mark it as substance B after completely dissolving;

[0034] b. Put substance A in a high-shear emulsifier, and disperse it evenly at a speed of 2000-3000r / min, so that zinc oxide adheres to the surface of magnesium oxide; evenly spray substance B on the magnesium oxide zinc oxide in a state of high-speed stirring and mixing In the solid powder, the dispersant can be evenly coated on the surface of the solid powder to form a coating film, and dispersed for 10-30 minutes to obtain a composite of magnesium oxide and zinc oxide;

[0035] c. Put the composite system obtained in step b in a constant temperature stirrer, a...

Embodiment 2

[0037] Each of the following examples relates to the composite vulcanizing agent of magnesium oxide and zinc oxide used for chloroprene rubber vulcanization, which all adopt the preparation method of Example 1, and the difference lies in the consumption of each raw material component, as shown in the following table:

[0038]

[0039] The compound vulcanizing agent obtained in the above examples was used to vulcanize neoprene rubber, and the performance evaluation of the vulcanized neoprene rubber was carried out. The Mooney scorch time was measured by a Mooney viscometer, and the tensile strength was tested according to the national standard GB / T528-1998. The results are shown in the table below.

[0040]

[0041] The chloroprene rubber is vulcanized with the superior product of the traditional powder vulcanizing agent, and the obtained chloroprene rubber has a Mooney scorch time of 30-60MSt 5 / min, the tensile strength is ≥24.0MPa. The results of each embodiment shown i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a magnesium oxide zinc oxide compound vulcanizing agent for chloroprene rubber vulcanization and a preparation method thereof. The vulcanizing agent is made of the following components: active magnesium oxide and active zinc oxide mixture 80.0%-90.0%; dispersion agent 10.0%-20.0%; the weight ratio of active magnesium oxide to active zinc oxide is 1:0.2-3.0. The preparation method is as follows: a, mixing active magnesium oxide and active zinc oxide to obtain substance A, dissolving the dispersant in absolute ethanol to obtain substance B; b, performing surface coating modification on substance A by substance B to obtain a compound; c 1. Heat and stir the compound to obtain a paste-like or viscous magnesium oxide zinc oxide compound vulcanizing agent. This vulcanizing agent solves the problems that the traditional vulcanizing agent is added into chloroprene rubber in powder form, which causes uneven dispersion of powder and easy failure of magnesium oxide activity, and improves the dispersion of zinc oxide and the activity retention of magnesium oxide. Reduced scorch hazard for high Mooney viscosity compounds.

Description

technical field [0001] The invention relates to a vulcanizing agent for chloroprene rubber vulcanization, in particular to a magnesium oxide zinc oxide compound vulcanizing agent, and at the same time, the invention also relates to a magnesium oxide zinc oxide compound vulcanization agent for neoprene vulcanization The preparation method of the agent. Background technique [0002] Neoprene is one of the main varieties of synthetic rubber. As a general-purpose special rubber, it has excellent properties such as heat resistance, flame resistance, oil resistance, and chemical corrosion resistance, and occupies an important position in synthetic rubber. According to the different molecular weight regulators used in the manufacturing process, chloroprene rubber can be divided into sulfur-regulated, non-sulfur-regulated and mixed-regulated types, of which non-sulfur-regulated types are the main varieties in the world. According to the crystallization speed or degree, chloroprene ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L11/00C08K9/10C08K3/22
Inventor 胡永琪李飞龙孙孟勇刘润静郑晓倩段晓宇崔继超刘亚青崔蕊张丽喆
Owner 河北镁神科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com