Basalt fiber chenille woven fabric

A technology of basalt fiber and chenille machine, which is applied in fabrics, textiles, textiles, and papermaking, can solve the problems of high air resistance, high price, and limited popularization and application, and achieve low resistance, high strength, and high-efficiency blocking ultraviolet rays. transparent effect

Inactive Publication Date: 2014-11-05
ZHONGYUAN ENGINEERING COLLEGE
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the problems of the material itself, this kind of filter material has huge air resistance and high price, which limits its popularization and application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The present embodiment basalt fiber chenille woven cloth, it comprises the basalt fiber chenille woven cloth formed by rapier loom weaving by basalt fiber chenille yarn, and described basalt fiber chenille yarn comprises core There are two parts of thread and feather yarn. The surface of the core wire and feather yarn is coated with polyimide coating by spraying process. The material of the feather yarn is basalt fiber, and the fineness of the feather yarn is 25Nm; the core wire is two Strands, the fineness of each strand is 22Nm, the material of the core wire is basalt fiber, after the core wire is twisted, the feather yarn is sandwiched between the two core wires, the twisting twist of the core wire is 550 twists / m, and the feather yarn The axial density is 320 strands / cm, and the basalt fiber chenille yarn is used as the raw material, the polyimide fiber with a diameter of 0.2mm is used as the warp yarn, and the basalt fiber chenille yarn with a diameter of 10mm is us...

Embodiment 2

[0024] The present embodiment basalt fiber chenille woven cloth, it comprises the basalt fiber chenille woven cloth formed by rapier loom weaving by basalt fiber chenille yarn, and described basalt fiber chenille yarn comprises core There are two parts of thread and feather yarn. The surface of the core wire and feather yarn is coated with polyimide coating by spraying process. The material of the feather yarn is basalt fiber, and the fineness of the feather yarn is 50Nm; the core wire is two Strands, the fineness of each strand is 60Nm, the material of the core wire is quartz glass fiber, the feather yarn is sandwiched between the two core wires after the core wire is twisted, the twisting twist of the core wire is 10 twists / m, the feather yarn The axial density is 200 / cm, the basalt fiber chenille yarn is used as the raw material, the polyimide fiber is used as the warp of 0.2mm, and the basalt fiber chenille yarn is used as the weft yarn with a diameter of 10mm, on the rapie...

Embodiment 3

[0026]The present embodiment basalt fiber chenille woven cloth, it comprises the basalt fiber chenille woven cloth formed by rapier loom weaving by basalt fiber chenille yarn, and described basalt fiber chenille yarn comprises core There are two parts, the core wire and the feather yarn, and the surface of the core wire and the feather yarn is coated with a thermosetting epoxy resin coating by a dip coating process. The material of the feather yarn is a mixed yarn of basalt fiber and quartz glass fiber, and the fineness of the feather yarn is 100Nm; The core wire is two strands, the fineness of each strand is 0.01Nm, the material of the core wire is a mixed yarn of polytetrafluoroethylene fiber and polyimide fiber, and the feather yarn is twisted after the core wire is twisted. Sandwiched between two core wires, the twisting degree of the core wire is 10 twists / meter, and the axial density of the feather yarn is 10,000 pieces / cm. The basalt fiber chenille yarn is used as the ra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a basalt fiber chenille woven fabric woven by basalt fiber chenille yarns through weaving equipment. The basalt fiber chenille yarns comprise core wires and camlets. The camlets are made of basalt fiber or combination yarns made of the basalt fiber and one or more of silica glass fiber, high silica glass fiber, aluminum silicate fiber, polyamide-imide fiber, polyether-ether-ketone fiber, polyphenylene sulfide fiber, polysulfone base amide fiber, polyp-phenylene benzobisthiazole fiber, polybenzimidazole fiber, polytetrafluroethylene fiber, polyimide fiber and aramid fiber. The core wires are two piled yarns. After the core wires are twisted, the camlets are placed between the core wires. The processing method for the basalt fiber chenille woven fabric by the weaving equipment is the most traditional method and includes an included angle 90 degrees between latitudinal and longitudinal directions. Various equipment is suitable to produce the basalt fiber chenille woven fabric with huge quantity and lowest production cost.

Description

technical field [0001] The patent of the invention relates to a woven fabric for air purification, in particular to a basalt fiber chenille woven fabric. Background technique [0002] The core thread of the chenille yarn in the prior art is twisted with acrylic yarn as raw material, and the feather yarn is cut into short feathers with viscose yarn as raw material, which is widely used in the fields of home textiles and woven garments . The fabric that adopts common chenille yarn to weave generally gets its decorative effect more, and its comfortableness aspect is relatively poor. Rarely used for air filtration purposes. [0003] After China experienced the "soot-type pollution" brought about by the industrial revolution in the 18th century and the "photochemical smog pollution" brought about by the petroleum and automobile industries in the 19th century, modern people are experiencing "severe PM2.5-type smog" with Chinese characteristics. The third pollution period marked...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/02D02G3/04D03D15/242D03D15/283D03D15/47D03D15/587
Inventor 张迎晨吴红艳张琦周淑雯张青松王文娟杨艳玉占鏐祥王艳秋
Owner ZHONGYUAN ENGINEERING COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com