A kind of porous mullite fiber product

A technology of porous mullite and mullite fiber, which is applied to the chemical characteristics of fibers, textiles and papermaking, artificial filaments made of inorganic raw materials, etc., can solve problems such as complex processes, high labor costs, and difficulty in continuous production, and achieve High thermal decomposition temperature, enhanced heat insulation effect, and reduced expansion rate

Active Publication Date: 2016-05-11
HUZHOU TEACHERS COLLEGE
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The process is relatively complicated, it is difficult to carry out continuous production, and the labor cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of porous mullite fiber product
  • A kind of porous mullite fiber product
  • A kind of porous mullite fiber product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The invention provides a porous mullite fiber product, which comprises the following three key process steps.

[0028] The first step is to modify the mullite fibers. Mullite can use Al 4+2x Si 2-2x o 10-x where x represents an oxygen vacancy (value range 0.2 to 0.9), and its structure terminates at the crystal surface, which will generate paired electrons, that is, dangling bonds. -OH structure can be formed in water. This structure is the reason why the mullite fiber can be chemically combined with the coupling agent. (1) Mix unmodified mullite fiber with aluminum-zirconium coupling agent, as a preference, the ratio of mass fraction is 100:10. Considering that any agitation has the possibility of fragmentation and shortening for brittle mullite inorganic fibers, once the fibers are shortened, on the one hand, it will affect the quality of the product, on the other hand, short and thin fibers will have an impact on industrial workers and the environment , so in t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of refractory material, and in particular relates to a porous mullite fiber product. The fiber product comprises the following components according to weight percentage: 85wt%-95wt% of modified mullite fiber, 1wt%-5wt% modified carbon fiber, 0.1wt%-1wt% of calcined alumina powder, 0.5wt%-2wt% silica sol, 0.2wt%-1.2wt% of sodium hypochlorite, 0.7wt%-1.3wt% of starch, and 0.5wt%-1.5wt% of an additive; the mullite fiber comprises the following chemical components: 50wt%<= Al2O3<= 70wt%, 25wt%<= SiO2<= 28wt%, and oily substances > 2wt%. The invention can prolong the service life of the mullite fiber porous product, and enhance the thermal insulation effect.

Description

technical field [0001] The invention belongs to the technical field of fire-resistant and heat-insulating materials, and in particular relates to a porous mullite fiber product. Background technique [0002] Mullite fiber is a kind of basic material in the field of high temperature technology. It has a series of excellent properties, including high melting point (1850 ° C), excellent high temperature creep resistance, excellent high temperature strength, electrical insulation and chemical stability. , low thermal conductivity and thermal expansion coefficient (~5.3×10 -6 K), as well as excellent corrosion resistance and high shear modulus, play a very prominent role in the development of the national economy, and are closely related to the development of steel, nonferrous metals, building materials, energy and new technology industries. Important Guarantee. Therefore, mullite fiber has been paid more and more attention as a light-weight and high-temperature resistant mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F9/08D01F1/10D01F11/00
Inventor 陈海锋
Owner HUZHOU TEACHERS COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com