Recovery method for waste ferric trichloride etching liquid

A technology of ferric chloride and recovery method, applied in chemical instruments and methods, metallurgical wastewater treatment, water/sludge/sewage treatment, etc., to achieve the effects of less operating costs, no three waste discharges, good environmental benefits and economic benefits

Active Publication Date: 2014-11-05
宁波东顺电子科技有限公司
View PDF7 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some methods currently used have some problems in varying degrees in terms of process cost, safety and comprehensive utilization of resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Recovery method for waste ferric trichloride etching liquid
  • Recovery method for waste ferric trichloride etching liquid
  • Recovery method for waste ferric trichloride etching liquid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0123] 1L of waste etching solution 1 was added to the anode chamber and cathode chamber liquid storage tank of the electrolytic cell composed of heterogeneous positive membranes, and the membrane polarization curve was measured at room temperature. It can be seen that the voltage increases linearly with the current. In order to better understand the influence of the electrolysis voltage on the electrolysis effect, the electrolysis test was carried out at the electrolysis cell voltage of 2.5, 3.0, 3.5, and 4.0V. Analyze the ferrous ions and iron ions in the sample. The total electrolysis time is 3.0h. After 3 hours of electrolysis, analyze the concentration of free acid and chloride ion. 2+ The amount of material change is used to calculate the current efficiency. The experimental results are shown in Table 1-1, Table 1-2, and Table 1-3.

[0124] Table 1-1, Fe in cathode and anode storage tanks during electrolysis 2+ Concentration change table

[0125]

[0126] Table 1-2...

Embodiment 2

[0132] Add 1 L of waste etching solution 1 into the anode chamber and the cathode chamber. Different ion-exchange membranes were selected, electrolyzed at a constant voltage of 3.0V, and the total electrolysis time was 3.0h. In the experiment, 25 mL samples were taken in the anode storage tank and cathode storage tank every half hour, and the ferrous ions, iron ions, and free acid and chloride ion concentrations after electrolysis for 3 hours were analyzed, and the electrolysis current efficiency was calculated. As in Table 2-1 and 2-2. It can be seen from Table 2-1 and 2-2 that Fe ions migrate through the cathodic membrane to the cathode chamber in the electrolytic cell composed of heterogeneous cathodic membrane, and the electrolysis effect is better for heterogeneous cathodic membrane electrolyzer than homogeneous cathodic membrane electrolyzer. The heterogeneous negative film electrolyzer is the worst. From the perspective of free acid concentration (Table 2-3), using th...

Embodiment 3

[0140] There is no Na in the waste etching solution 2 + and H in acid + As a conductive ion, the negative membrane is selected to form an electrolytic cell for steady flow test. Add 3L of waste etching solution 2 to the anode storage tank, add 600ml of waste etching solution 2 to the cathode storage tank, and in a steady flow state, first perform electrolysis at a low current of 3.60A for 2 hours and then at a high current of 5.6A for 3 hours , the ferrous ions reacted to the anode are all oxidized to ferric ions. During this period, sample 25ml and 10ml in the anode chamber and the cathode chamber respectively every 1h or 2h (select specific questions), and analyze the ferrous ions and iron ions in the samples, as well as the free acid in the solution in each storage tank after electrolysis and chloride ion concentration and calculate the current efficiency. The results are shown in Table 3-1.

[0141] Table 3-1, 5.60A steady current electrolysis test results table

[01...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
current efficiencyaaaaaaaaaa
Login to View More

Abstract

The invention provides a recovery method for a waste ferric trichloride etching liquid. The method adopts integrated membrane electrolysis and extraction technology and comprises the following steps: providing an electrolytic tank, wherein an ion exchange membrane is arranged in the electrolytic tank to divide the electrolytic tank into an anode chamber and a cathode chamber, and a cathode and an anode are respectively positioned in the cathode chamber and the anode chamber located at two sides of the ion exchange membrane; adding the waste ferric trichloride etching liquid into the cathode chamber and carrying out membrane electrolysis so as to reduce Fe3+ ions into Fe2+ ions; carrying out extraction on a solution obtained after electrolysis in the cathode chamber to remove impurity metals so as to obtain an extract phase solution and a metal impurity-removed phase solution and delivering the metal impurity-removed phase solution to the anode chamber for membrane electrolysis so as to oxidize Fe2+ ions into Fe3+ ions; and recovering a solution obtained after electrolysis in the anode chamber. Compared with conventional processing technology for the waste ferric trichloride etching liquid, the recovery method provided by the invention has the advantages of short and simple process flow, no generation of secondary pollution, no discharge of waste gas, waste water and industrial residue, low production cost, applicability to large-scale treatment, treating capacity of more than ten thousands every year and good environmental and economic benefits.

Description

technical field [0001] The invention relates to a method for recovering ferric chloride etching waste liquid, in particular to a method for recovering ferric chloride etching waste liquid containing impurity metal ions. Background technique [0002] The etching method is suitable for large-volume, multi-variety, large-scale thin metal material processing and surface decoration of metal products (semi-etching). It is now used in various integrated circuit lead frames and fluorescent display displays, grids, precision filters, encoder gratings, microelectrodes, mask plates, integrated circuit cover plates, picture tube shadow masks, surface mount (SMT) solder paste For products such as screen printing plates, the etching method manufacturing process is often applied to high-tech fields. [0003] Ferric chloride solution has certain oxidation and acidity, and has a good corrosion effect on iron and nickel, so it is widely used in metal etching, such as etching of fine circuit ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23F1/46C02F1/461C02F1/26C02F1/62C02F101/20C02F103/16
Inventor 何公明梁泰频王满根
Owner 宁波东顺电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com