Preparation method of olivine type phosphate positive electrode material for lithium ion battery

A lithium-ion battery, olivine-type technology, applied in the direction of battery electrodes, secondary batteries, chemical instruments and methods, etc., can solve the problems of lack of commercial application, low electronic conductivity, dependence on modification effect, etc., to achieve good electrical Chemical performance, high reactivity, perfect crystallization effect

Active Publication Date: 2014-10-29
KUNMING UNIV OF SCI & TECH
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

LiFePO4 has a 3.4 V voltage platform, which has been commercialized many years ago; LiMnPO4 has a 4.1V voltage platform, and is currently undergoing commercial trials in various countries around the world; and LiCoPO4 sub>4 and LiNiPO4 have a higher voltage platform, about 4.8 V and 5.1 V, respectively, but due to the limitation of the electrochemical window of commercial electrolytes, there is still a lack of commercialization Conditions of application
However, whether it is commercially available LiFePO4 and LiMnPO4, or high-voltage LiCoPO4 and LiNiPO4 sub>, both have the problems of low electronic conductivity and slow diffusion of lithium ions. Only after modification by cation substitution, particle size reduction and carbon coating, the obtained LiMPO4-based materials can exhibit better performance, but the modification effect largely depends on the preparation method of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of olivine type phosphate positive electrode material for lithium ion battery
  • Preparation method of olivine type phosphate positive electrode material for lithium ion battery
  • Preparation method of olivine type phosphate positive electrode material for lithium ion battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The preparation method of the olivine type phosphate cathode material for lithium ion batteries, its specific steps are as follows:

[0025] (1) At room temperature, the LiCoPO obtained by preparing solid powders of metal salt, lithium source and phosphorus source as required 4 The stoichiometric ratio in (i.e. the molar ratio Li:Co:PO 4 =1:1:1) Mix well to obtain a mixture, then add alkali solid powder and carry out ball milling for 2 hours to make the metal salt and alkali undergo a solid-state reaction at room temperature, and finally obtain the precursor after drying at 100°C for 10 hours, in which the metal salt The molar ratio of metal ions to alkali solid powder is 1:2, the alkali solid powder is sodium hydroxide, the metal salt is cobalt chloride, lithium dihydrogen phosphate is both lithium source and phosphorus source, and cobalt chloride and sodium hydroxide are generated at room temperature Solid phase reaction to generate cobalt hydroxide and molten salt m...

Embodiment 2

[0031] The preparation method of the olivine type phosphate cathode material for lithium ion batteries, its specific steps are as follows:

[0032] (1) At room temperature, the metal salt, lithium source and phosphorus source solid powder were prepared according to the required phosphate LiCoPO 4 The stoichiometric ratio of / C (i.e. the molar ratio Li:Co:PO 4 =1:1:1) Mix well to obtain a mixture, then add alkali solid powder and carry out ball milling for 2 hours to make the metal salt and alkali undergo a solid-state reaction at room temperature, and finally obtain a precursor after drying at 120°C for 10 hours, in which the metal in the metal salt The molar ratio of ions to alkali solid powder is 1:2, the alkali solid powder is potassium hydroxide, the metal salt is cobalt sulfate and cobalt acetate with a molar ratio of 1:1, lithium dihydrogen phosphate is both lithium source and phosphorus source, cobalt sulfate Solid phase reaction at room temperature with cobalt acetate...

Embodiment 3

[0037] The preparation method of the olivine type phosphate cathode material for lithium ion batteries, its specific steps are as follows:

[0038] (1) At room temperature, the solid powder of metal salt, lithium source and phosphorus source was pressed by phosphate LiCoPO 4 The stoichiometric ratio of / C (i.e. the molar ratio Li:Co:PO 4 =1:1:1) Mix well to get the mixture, then add alkali solid powder and carry out ball milling for 4 hours to make the metal salt and alkali undergo a solid phase reaction at room temperature, and finally dry at 80°C for 10 hours to obtain the precursor, in which the metal in the metal salt The molar ratio of ions to alkali solid powder is 1:1, the alkali solid powder is calcium hydroxide, the metal salt is manganese chloride, lithium dihydrogen phosphate is both lithium source and phosphorus source, manganese chloride and calcium hydroxide are solidified at room temperature The opposite reaction generates manganese hydroxide and molten salt me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of an olivine type phosphate positive electrode material for a lithium ion battery, and belongs to the technical field of lithium ion battery electrodes. At room temperature, metal salt, lithium source and phosphorus source solid powder are evenly mixed in the stoichiometric ratio of phosphate molecular formula LiMPO4 to obtain a mixture, and then alkali solid powder is added for ball milling, so that solid state reaction of metal salt and alkali is performed at room temperature, finally a precursor is obtained by drying to; in the air or inert atmosphere, the precursor is sintered and then cooled to the room temperature to obtain a sintering product; sintered powder is obtained by washing and filtering and drying of the sintered product, the sintered powder and a carbon source are mixed evenly by ball milling, or the sintered powder is directly thermally treated and then cooled to the room temperature to obtain the olivine type phosphate positive electrode material. According to the method, the solid state reaction of the metal salt and the alkali is performed at the room temperature for online generation of a highly active metal hydroxide and a molten salt medium, and then the LiMPO4 based material is prepared by sintering, washing and heat treatment.

Description

technical field [0001] The invention relates to a preparation method of an olivine-type phosphate cathode material for a lithium-ion battery, and belongs to the technical field of lithium-ion battery electrodes. Background technique [0002] As a cathode material for lithium-ion batteries, olivine-type phosphate material LiMPO 4 (M = Fe, Mn, Co, Ni) have received great attention since they were first reported in 1997, and they have the advantages of wide source of raw materials, good stability and high safety, and have great application prospects. LiFePO 4 With a 3.4 V voltage platform, it has been commercialized many years ago; LiMnPO 4 It has a 4.1V voltage platform and is currently undergoing commercial trials in various countries around the world; while LiCoPO 4 and LiNiPO 4 It has a higher voltage platform, about 4.8 V and 5.1 V, respectively, but due to the limitation of the electrochemical window of the commercial electrolyte, there is still a lack of conditions f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M4/1397
CPCH01M4/1397H01M4/5825H01M10/0525C01B25/45Y02E60/10
Inventor 方海升陈维兵杨斌马文会姚耀春杨桂玲戴永年
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com